Rubber track

A technology of rubber crawler and raw rubber, applied in the field of high-strength rubber crawler and its preparation, can solve the problems of crawler aging, lowering the use level of crawler, lowering the strength of rubber crawler, etc., so as to enhance the strength, prolong the service life and improve the anti-aging performance. Effect

Active Publication Date: 2018-11-02
JIANGSU XCMG CONSTR MASCH RES INST LTD
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the commonly used rubber track has a low load-bearing capacity and is prone to early aging, which cannot meet the requirements for load-bearing capacity and service life of construction machinery.
[0003] At present, domestic research on the anti-aging performance of rubber tracks has improved the aging properties of rubber tracks by adding accelerators, anti-aging agents, plasticizers, diatomaceous earth powder, etc., but this also leads to a decrease in the strength of rubber tracks, to a certain extent The use level of the crawler is reduced; the domestic research on the bearing capacity of the rubber crawler mainly improves the strength of the crawler by adding carbon black, white carbon black, homogenized anti-tearing agent, etc. This method improves the strength of the crawler, but There is no improvement in the anti-aging performance of the track, and even the early aging phenomenon of the track

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber track

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] The preparation method of described high-strength rubber track is as follows:

[0037] step one:

[0038] Raw material preparation: prepare raw rubber, cut it into wedge-shaped pieces of 8kg, and then dry; crush and dry the compounding agent, sieve it, and weigh it according to the proportion.

[0039] Step two:

[0040] Mastication: Set the speed ratio of the front and rear rollers of the mill to 1:1.2, adjust the roller distance of the mill to 0.8mm, add raw rubber for plastication, and make triangular bags, 5 times.

[0041] Step three:

[0042] Mixing: Adjust the roller distance of the open mill to 0.8mm, and add raw rubber into the mixing.

[0043] Step four:

[0044] Final refining: Add mixed rubber into the open mill, and then add various compounding agents for final refining. After the powder is finished, pack it several times to evenly disperse the raw rubber and compounding agents. Then the rubber material was unloaded and parked for 4 hours.

Embodiment 1

[0046] A kind of high-strength rubber track provided in this embodiment, the high-strength rubber track includes the following raw materials in parts by weight: 70 parts of natural rubber, 30 parts of styrene-butadiene rubber, 1.5 parts of sulfur, 1 part of accelerator DTDM, 2.5 parts of magnesium oxide 2 parts of zinc oxide, 2 parts of anti-aging agent DFC-345 parts, 2 parts of titanate coupling agent HY311W, 0.8 parts of antiscorch agent NA, 50 parts of carbon black N220, 2 parts of antimony trioxide, 4 parts of microcrystalline wax, Light stabilizer PDS1.5 parts.

[0047] step one:

[0048] Raw material preparation: prepare raw rubber, cut it into wedge-shaped pieces of 8kg, and then dry; crush and dry the compounding agent, sieve it, and weigh it according to the above ratio.

[0049] Step two:

[0050] Masticating: Set the speed ratio of the front and rear rollers of the mill to 1:1.2, adjust the roller distance of the mill to 0.8mm, masticate the styrene-butadiene rubb...

Embodiment 2

[0056]A kind of high-strength rubber track provided by the present embodiment, the high-strength rubber track comprises the following raw materials in parts by weight: 60 parts of natural rubber, 40 parts of EPDM rubber, 2 parts of sulfur, 1.5 parts of accelerator BZ, 2 parts of magnesium oxide, 2 parts of zinc oxide, 5 parts of antioxidant MB, 3 parts of titanate coupling agent HY311W, 1 part of anti-scorch agent NA, 60 parts of carbon black N234, 1.5 parts of chlorinated paraffin, 3 parts of microcrystalline wax 1 part of light stabilizer PDS.

[0057] step one:

[0058] Raw material preparation: prepare raw rubber, cut it into wedge-shaped pieces of 8kg, and then dry; crush and dry the compounding agent, sieve it, and weigh it according to the above ratio.

[0059] Step two:

[0060] Masticating: Set the speed ratio of the front and rear rollers of the mill to 1:1.2, adjust the roller distance of the mill to 0.8mm, and masticate the EPDM rubber and natural rubber separate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rubber track. The rubber track is prepared from raw materials including raw rubber, sulfur, an accelerant, magnesia, zinc oxide, an anti-aging agent, a titanate coupling agent, an anti-coking agent, carbon black, a flame retardant, micro-crystal wax and a light stabilizer through plastication, mixing and final refining. The strength and wear resistance of rubber are enhanced by adding different raw rubber components, carbon black, the titanate coupling agent and the like. The aging resistance of rubber is improved and the service life of rubber is prolonged by addingthe anti-aging agent, the anti-coking agent and the light stabilizer. Thus, the rubber track has the characteristics of high strength and high reliability.

Description

technical field [0001] The invention relates to a rubber material and a preparation method thereof, in particular to a high-strength rubber track and a preparation method thereof. Background technique [0002] The rubber track is a new type of walking part developed to simulate the metal track. It has good longitudinal flexibility and lateral rigidity. The advantages of road surface, fast speed, and light weight have been widely used in agricultural machinery, and the proportion of application in construction machinery has continued to increase. However, the currently widely used rubber crawlers have low load-bearing capacity and are prone to early aging phenomena, which cannot meet the requirements of load-bearing capacity and service life on construction machinery. [0003] At present, domestic research on the anti-aging performance of rubber tracks has improved the aging properties of rubber tracks by adding accelerators, anti-aging agents, plasticizers, diatomaceous ear...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/06C08L23/16C08L91/06C08K13/02C08K3/06C08K3/22C08K3/04
CPCC08K2003/222C08K2003/2296C08K2201/014C08L7/00C08L2201/02C08L2205/025C08L2205/03C08L2205/035C08L9/06C08L91/06C08K13/02C08K3/06C08K3/22C08K3/04C08K3/2279C08L23/16
Inventor 李毅朱鹏霄陈波
Owner JIANGSU XCMG CONSTR MASCH RES INST LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com