Environment-friendly flame-retardant foaming material for pickup fuel tank and preparation method of environment-friendly flame-retardant foaming material

A technology for foaming materials and fuel tanks, which is applied in the field of environmentally friendly flame-retardant foaming materials and their preparation, can solve problems such as unreachable and potential safety hazards, and achieve the effects of prolonging service life, ensuring vehicle and personal safety, and having high strength.

Inactive Publication Date: 2018-11-02
YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The characteristics of traditional pickup fuel tanks usually cannot achieve ideal results, and there are great potential safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] An environmentally friendly flame-retardant foaming material for pickup fuel tanks, its raw materials include isocyanate and synthetic material, the mass ratio of the isocyanate to the synthetic material is 1:1.4, and the synthetic material contains The mass parts of points and each component are as follows:

[0026] JTM polyether 4110: 55 parts;

[0027] Polyether 4110: 22 parts;

[0028] Stabilizer: 2.5 parts;

[0029] Diethanolamine: 9 parts;

[0030] Catalyst: 3 parts;

[0031] Water: 3 parts;

[0032] Glass fiber: 80 parts;

[0033] Flame retardant: 30 parts.

[0034] The stabilizer is silicone oil.

[0035] The catalyst is catalyst APM9.

[0036] The flame retardant is flame retardant TCPP.

[0037] A method for preparing an environmentally friendly flame-retardant foaming material for a pickup fuel tank, the method steps comprising:

[0038] (1) Raw material processing: drying JTM polyether 4110, polyether 4110 and isocyanate;

[0039] (2) Weighing pro...

Embodiment 2

[0045] An environmentally friendly flame-retardant foaming material for pickup fuel tanks, its raw materials include isocyanate and synthetic material, the mass ratio of the isocyanate to the synthetic material is 1:1.4, and the synthetic material contains The mass parts of points and each component are as follows:

[0046] JTM polyether 4110: 60 parts;

[0047] Polyether 4110: 25 parts;

[0048] Stabilizer: 2.6 parts;

[0049] Diethanolamine: 11 parts;

[0050] Catalyst: 3.5 parts;

[0051] Water: 3.4 parts;

[0052] Glass fiber: 80 parts;

[0053] Flame retardant: 33 parts.

[0054] The stabilizer is silicone oil.

[0055] The catalyst is catalyst APM9.

[0056] The flame retardant is flame retardant TCPP.

[0057] A method for preparing an environmentally friendly flame-retardant foaming material for a pickup fuel tank, the method steps comprising:

[0058] (1) Raw material processing: drying JTM polyether 4110, polyether 4110 and isocyanate;

[0059] (2) Weighin...

Embodiment 3

[0065] An environmentally friendly flame-retardant foaming material for pickup fuel tanks, its raw materials include isocyanate and synthetic material, the mass ratio of the isocyanate to the synthetic material is 1:1.4, and the synthetic material contains The mass parts of points and each component are as follows:

[0066] JTM polyether 4110: 65 parts;

[0067] Polyether 4110: 28 parts;

[0068] Stabilizer: 2.8 parts;

[0069] Diethanolamine: 13 parts;

[0070] Catalyst: 4 parts;

[0071] Water: 3.8 parts;

[0072] Glass fiber: 80 parts;

[0073] Flame retardant: 35 parts.

[0074] The stabilizer is silicone oil.

[0075] The catalyst is catalyst APM9.

[0076] The flame retardant is flame retardant TCPP.

[0077] A method for preparing an environmentally friendly flame-retardant foaming material for a pickup fuel tank, characterized in that the steps of the method include:

[0078] (1) Raw material processing: drying JTM polyether 4110, polyether 4110 and isocyanat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly flame-retardant foaming material for a pickup fuel tank and a preparation method of the environment-friendly flame-retardant foaming material. The environment-friendly flame-retardant foaming material for the pickup fuel tank comprises the following raw materials: isocyanate and a composite material, where the mass ratio of isocyanate to the composite material is 1:1.4, and the composite material comprises the following components by mass: 55 to 65 parts of JTM polyether 4110, 22 to 28 parts of polyether 4110, 2.5 to 2.8 parts of a stabilizer, 9to 13 parts of diethanolamine, 3 to 4 parts of a catalyst, 3 to 3.8 parts of water, 80 parts of glass fiber, and 30 to 35 parts of a flame retardant. The environment-friendly flame-retardant foaming material for the pickup fuel tank in the invention is proper in components and component proportions, so that the environment-friendly flame-retardant foaming material has the characteristics of high-temperature resistance, high flame-retardant performance, high strength, and environmental friendliness.

Description

technical field [0001] The invention relates to an environment-friendly flame-retardant foaming material used for a pickup fuel tank and a preparation method thereof. Background technique [0002] At present, with the development of the pickup truck industry and the enhancement of people's awareness of safety and environmental protection, people's requirements for pickup truck components have also increased significantly. Strength and highly environmentally friendly properties. The characteristics of traditional pickup fuel tanks usually cannot achieve ideal results, and there are great potential safety hazards. Contents of the invention [0003] The purpose of the present invention is to overcome the defects in the prior art and provide an environmentally friendly flame-retardant foaming material for pickup truck fuel tanks. High performance, high strength, and environmental protection characteristics. [0004] In order to solve the above technical problems, the techni...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/66C08G18/48C08G18/32C08K7/14C08K5/521C08G101/00
CPCC08G18/3275C08G18/4804C08G18/6688C08K5/521C08K7/14C08G2110/0083
Inventor 朱章娣朱凌宇
Owner YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More