Mesoporous gamma-Fe-Ti-Al2O3 catalyst, and preparation method and application thereof

A -fe-ti-al2o3, catalyst technology, applied in the field of catalyst preparation, to achieve significant effects

Inactive Publication Date: 2018-10-19
HUAIHAI INST OF TECH +1
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for the aqueous phase reaction, the research on the heterogeneous catalytic ozonation reaction is still in the preliminary stage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mesoporous gamma-Fe-Ti-Al2O3 catalyst, and preparation method and application thereof
  • Mesoporous gamma-Fe-Ti-Al2O3 catalyst, and preparation method and application thereof
  • Mesoporous gamma-Fe-Ti-Al2O3 catalyst, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1, a kind of mesoporous γ-Fe-Ti-Al 2 o 3 Catalyst, this catalyst is made of the raw material of following weight ratio:

[0031] Aluminum isopropoxide C 6 h 21 AlO 3 15

[0032] Glucose C 6 h 12 o 6 .H 2 O 18

[0033] Fe(NO 3 ) 3 .9H 2 O 1.50;

[0034] Tetrabutyl titanate TBOT aqueous solution, the volume concentration is 0.1%;

[0035] The aluminum isopropoxide C 6 h 21 AlO 3 The mass volume ratio of tetrabutyl titanate TBOT aqueous solution to TBOT is 15:200, the unit is g / mL.

Embodiment 2

[0036] Example 2, a mesoporous γ-Fe-Ti-Al 2 o 3 Catalyst, this catalyst is made of the raw material of following weight ratio:

[0037] Aluminum isopropoxide C 6 h 21 AlO 3 18

[0038] Glucose C 6 h 12 o 6 .H 2 O 15

[0039] Fe(NO 3 ) 3 .9H 2 O 0.30;

[0040] Tetrabutyl titanate TBOT aqueous solution, the volume concentration is 0.3%;

[0041] The aluminum isopropoxide C 6 h 21 AlO 3 The mass volume ratio of tetrabutyl titanate TBOT aqueous solution to TBOT is 18:250, the unit is g / mL.

Embodiment 3

[0042] Embodiment 3, a kind of mesoporous γ-Fe-Ti-Al 2 o 3 Catalyst, this catalyst is made of the raw material of following weight ratio:

[0043] Aluminum isopropoxide C 6 h 21 AlO 3 16.8

[0044] Glucose C 6 h 12 o 6 .H 2 O 16.8

[0045] Fe(NO 3 ) 3 .9H 2 O 1.33;

[0046] Tetrabutyl titanate TBOT aqueous solution, the volume concentration is 0.19%;

[0047] The aluminum isopropoxide C 6 h 21 AlO 3 The mass volume ratio of tetrabutyl titanate TBOT aqueous solution to TBOT is 16.8:216, unit g / mL.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a mesoporous gamma-Fe-Ti-Al2O3 catalyst. The catalyst is prepared from the following raw materials of aluminum isopropoxide C6H21AlO3, glucose C6H12O6.H2O, Fe(NO3)3.9H2O, and tetrabutyl titanate (TBOT) aqueous solution. The invention further discloses a preparation method and application of the mesoporous gamma-Fe-Ti-Al2O3 catalyst. The novel mesoporous gamma-Fe-Ti-Al2O3 catalyst can be applied to catalytic ozonation of ibuprofen and blocking of bromate generation, and has remarkable effect.

Description

technical field [0001] The invention relates to a method for preparing a catalyst, especially a mesoporous γ-Fe-Ti-Al 2 o 3 Catalyst and its preparation method and use. Background technique [0002] The heterogeneous catalytic ozonation technology has the advantages of complete oxidation of organic pollutants, good stability, and the catalyst can be regenerated and reused. It has become a research hotspot in the field of environment in recent years. However, the research on heterogeneous catalyzed ozonation reaction is still in the preliminary stage for water phase reaction. Therefore, it is of great significance to study catalysts for heterogeneously catalyzed ozonation reactions. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a new mesoporous γ-Fe-Ti-Al 2 o 3 The catalyst can be used to catalyze the ozone oxidation reaction, and can effectively promote the removal of ibuprofen and TOC. [0004] The prese...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/745B01J35/10C02F1/72C02F1/78C02F101/30C02F101/12
CPCC02F1/725C02F1/78B01J23/002B01J23/745C02F2101/12C02F2101/30B01J35/64
Inventor 邴吉帅陈丽胡春
Owner HUAIHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com