Glass-fiber-reinforced modified resin ASA composite material with low smell and preparation method thereof

A modified resin and glass fiber technology, applied in the field of polymer materials, can solve the problems of high price, need to be studied, low VOC, etc., achieve the effect of low price, control odor, and reduce odor level

Active Publication Date: 2018-09-28
中广核俊尔(上海)新材料有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional solution, as described in CN201310308220.6, uses nano-zinc oxide and nano-titanium dioxide to achieve low odor and low VOC by changing the mass ratio of the added amount and vacuuming it out. Although it can achieve its ideal effect, However, nano-zinc oxide and nano-titanium dioxide are expensive, and it is not feasible to achieve low-odor and low-VOC effects by adding these two additives in actual factory production. Not only that, but this method can only reduce some The small molecular substances are extracted, and the other substances with higher boiling points still remain in the material, which cannot be really eradicated; CN201010543461.5 also uses a similar solution, using a compound deodorant to achieve the purpose of deodorization and low VOC , but the use of zinc ricinoleate as the leading deodorant has a significant effect on the removal of small sulfur molecules. The effectiveness of other small molecules such as benzene, aldehydes and ketones still needs to be studied, so it cannot really achieve low Glass fiber reinforced modified resin ASA with odor and low VOC requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass-fiber-reinforced modified resin ASA composite material with low smell and preparation method thereof
  • Glass-fiber-reinforced modified resin ASA composite material with low smell and preparation method thereof
  • Glass-fiber-reinforced modified resin ASA composite material with low smell and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Weigh each component according to the data of Example 1 shown in Table 1, mix the components other than the chopped glass fiber reinforced system uniformly in a high-speed mixer, and put them into the main feeding bin of the twin-screw extruder , the chopped glass fiber reinforced system is put into the side feeding bin, the screw diameter of the extruder is 35mm, the length-to-diameter ratio L / D is 35, and the temperature of each zone of the main barrel from the feed port to the exit of the machine head is set as: 180°C , 210°C, 230°C, 240°C, 240°C, 240°C, 240°C, the speed of the host machine is 150 rpm, after melt extrusion, cooling, granulation, and drying, the low-odor glass fiber reinforced modified Resin ASA composite material.

Embodiment 2

[0044] Weigh each component according to the data of Example 2 shown in Table 1, mix the components other than the chopped glass fiber reinforced system uniformly in a high-speed mixer, and put them into the main feeding bin of the twin-screw extruder , the chopped glass fiber reinforced system is put into the side feeding bin, the screw diameter of the extruder is 35mm, the length-to-diameter ratio L / D is 35, and the temperature of each zone of the main barrel from the feed port to the exit of the machine head is set as: 180°C , 210°C, 230°C, 240°C, 240°C, 240°C, 240°C, the speed of the host machine is 150 rpm, after melt extrusion, cooling, granulation, and drying, the low-odor glass fiber reinforced modified Resin ASA composite material.

Embodiment 3

[0046] Weigh each component according to the data of Example 3 shown in Table 1, mix the components other than the chopped glass fiber reinforced system uniformly in a high-speed mixer, and put them into the main feeding bin of the twin-screw extruder , the chopped glass fiber reinforced system is put into the side feeding bin, the screw diameter of the extruder is 35mm, the length-to-diameter ratio L / D is 35, and the temperature of each zone of the main barrel from the feed port to the exit of the machine head is set as: 180°C , 210°C, 230°C, 240°C, 240°C, 240°C, 240°C, the speed of the host machine is 150 rpm, after melt extrusion, cooling, granulation, and drying, the low-odor glass fiber reinforced modified Resin ASA composite material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a glass-fiber-reinforced modified resin ASA composite material with a low smell. The glass-fiber-reinforced modified resin ASA composite material comprises, by weight, 60-90 parts of modified resin ASA, 5-40 parts of short glass fiber reinforcements, 3-10 parts of interface compatilizer, 1-5 parts of first deodorant, 1-5 parts of second deodorant and 0.1-1 part of antioxygen. The invention further provides a preparation method of the glass-fiber-reinforced modified resin ASA composite material. The glass-fiber-reinforced modified resin ASA composite material has the advantages that glass fibers are used for modification, and with the joint aid of the interface compatilizer and the antioxygen, the smell of the composite material can be controlled effectively while themechanical property of the material is improved further; the composite material has outstanding performance in a high-content glass fiber system, and the smell is not quite different from the smell of a low-glass-fiber-content glass fiber system.

Description

technical field [0001] The invention belongs to the field of polymer materials, and relates to a glass fiber reinforced modified resin ASA composite material, in particular to a glass fiber reinforced modified resin ASA composite material with low odor and a preparation method thereof. Background technique [0002] Modified resin ASA is a widely used general-purpose plastic. It has excellent comprehensive performance, molding processability, and relatively low price. It occupies a leading position in plastics and is widely used in daily life. Adding the glass fiber system can effectively make up for the performance defects of the modified resin ASA, thereby further reducing the cost. [0003] With the current trend of automobile lightweight, the use of glass fiber reinforced modified resin ASA system has been more and more used in various parts of automobiles, such as rearview mirrors, bumpers and so on. More and more glass fiber reinforced modified resin ASA systems have e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L51/00C08L23/06C08K13/04C08K7/24C08K5/134C08K5/526C08J5/04
CPCC08J5/043C08J2351/00C08J2451/00C08K5/1345C08K5/526C08K7/24C08K13/04
Inventor 张逸冰屈国梁黄志杰王海华杨仓先
Owner 中广核俊尔(上海)新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap