A kind of high water-locking anti-dripping bamboo charcoal biological fiber mask base cloth and high water-locking moisturizing mask

A bio-fiber facial mask, bamboo charcoal technology, applied in fiber treatment, fiber type, non-woven fabrics and other directions, can solve the problems of loss and waste of active ingredients, unsustainable liquid holding capacity, troublesome cleaning, etc., and achieve excellent processing performance and Mechanical properties, balanced liquid retention and moisture release capabilities, moderate effect of action intensity

Active Publication Date: 2019-11-26
广东柏俐臣生物科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing mask technology pursues "thin and non-sense", requiring the mask to be light and soft, that is, to minimize the weight of the mask base fabric on the basis of ensuring the basic mechanical properties of the mask base fabric
This results in insufficient liquid-holding capacity of the mask base fabric and short liquid-holding time. Although most masks are hung with essence more than ten times their own mass in the liquid-hanging step of the preparation process, the instant liquid-holding Fluid power doesn't last long
When the user takes the mask out of the packaging bag or box and unfolds it, part of the essence often flows down from the base fabric of the mask and drips due to gravity, resulting in the loss and waste of active ingredients; when the mask is applied to the face, There are also some essences that flow downwards under the action of gravity, causing the essence to be applied on the face to be less and more, and the distribution is uneven, which affects the use effect of the mask; The neck, hair or scalp (when applying the mask in a supine position) continues to flow downward. The essence of the mask is sticky and sticky and cold, which can easily cause sensory discomfort to the user. The lost essence cannot play the role of facial skin care. Pollution of clothes, hair, etc., troublesome cleaning

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high water-locking anti-dripping bamboo charcoal biological fiber mask base cloth and high water-locking moisturizing mask
  • A kind of high water-locking anti-dripping bamboo charcoal biological fiber mask base cloth and high water-locking moisturizing mask
  • A kind of high water-locking anti-dripping bamboo charcoal biological fiber mask base cloth and high water-locking moisturizing mask

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The high water-locking anti-dripping bamboo charcoal biological fiber facial mask base cloth of the present embodiment is prepared by the following method:

[0037] 1) Dissolve the silane coupling agent 3-aminopropyltriethoxysilane in ethanol aqueous solution (the volume ratio of ethanol to water is 80:20), adjust the pH value of the system to 5 with acetic acid, heat up to 55°C and keep stirring Hydrolyzed for 25 minutes to obtain a silane coupling agent solution;

[0038] According to the mass ratio of nanometer bamboo charcoal powder and silane coupling agent 3-aminopropyltriethoxysilane being 10:1.0, take nanometer bamboo charcoal powder and add in silane coupling agent solution, keep stirring for 3h to make it disperse evenly, then After filtering, washing to neutrality, and drying at 75°C, modified bamboo charcoal powder is obtained;

[0039] 2) Get gelatin and add it to water, heat and dissolve to prepare gelatin solution; according to the mass ratio of modified...

Embodiment 2

[0046] The high water-locking anti-dripping bamboo charcoal biological fiber facial mask base cloth of the present embodiment is prepared by the following method:

[0047] 1) Dissolve the silane coupling agent 3-aminopropyltriethoxysilane in ethanol aqueous solution (the volume ratio of ethanol to water is 80:20), adjust the pH value of the system to 4.5 with acetic acid, heat up to 50°C and keep stirring Hydrolyzed for 30 minutes to obtain a silane coupling agent solution;

[0048] According to the mass ratio of nano-bamboo charcoal powder and silane coupling agent 3-aminopropyltriethoxysilane being 10:1.1, take nano-bamboo charcoal powder and add it to the silane coupling agent solution, keep stirring for 4h to make it disperse evenly, and then After filtering, washing to neutrality, and drying at 75°C, modified bamboo charcoal powder is obtained;

[0049] 2) Take gelatin and add it to water, heat and dissolve to prepare gelatin solution; according to the ratio of 9:2 in ma...

Embodiment 3

[0056] The high water-locking anti-dripping bamboo charcoal biological fiber facial mask base cloth of the present embodiment is prepared by the following method:

[0057] 1) Dissolve the silane coupling agent 3-aminopropyltriethoxysilane in an aqueous ethanol solution (the volume ratio of ethanol to water is 80:20), adjust the pH value of the system to 4 with acetic acid, and raise the temperature to 50°C and keep it warm Stir and hydrolyze for 25 minutes to obtain a silane coupling agent solution;

[0058] According to the mass ratio of nano-bamboo charcoal powder and silane coupling agent 3-aminopropyltriethoxysilane being 10:1.2, take nano-bamboo charcoal powder and add it to the silane coupling agent solution, keep stirring for 5h to make it disperse evenly, and then After filtering, washing to neutrality, and drying at 75°C, modified bamboo charcoal powder is obtained;

[0059] 2) Add gelatin to water, heat and dissolve to prepare gelatin solution; according to the mass...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
pore sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to a biological bamboo fiber mask base cloth with high water preservation performance and an anti-dropping function and a moisture mask with high water preservation performance.A preparation method of the mask base cloth includes the following steps that 1, nanometer bamboo carbon powder is modified by a silane coupling agent to obtain modified bamboo carbon powder; 2, the modified bamboo carbon powder and a dispensing agent are added into a gelatin solution and dispersed uniformly to obtain bamboo slurry; 3, polylactic acid is dissolved in trichloromethane to prepare aspinning solution, the spinning solution is subjected to electrostatic spinning to obtain a polylactic acid fibrofelt, and the polylactic acid fibrofelt is soaked in the bamboo slurry for dipping andmodification to obtain a modified fibrofelt; 4, sodium alginate is added into chitosan liquid for dissolution to obtain a finishing liquid, and the modified fibrofelt is soaked in the finishing liquidfor after-finishing to obtain a compound fibrofelt; 5, hydroentangling and reinforcement are conducted on the compound fibrofelt to obtain a finished product. The obtained biological bamboo fiber mask base cloth has an excellent constraint capability on essence liquid and great liquid preservation and moisture releasing performance. After the essence liquid is loaded on the cloth by liquid suspension, the moisture mask with high water preservation performance is obtained, the situation that loss of the essence liquid is caused since the essence liquid flows down and drops is avoided, and waste is prevented.

Description

technical field [0001] The invention belongs to the technical field of cosmetics, and in particular relates to a high water-locking and anti-dripping bamboo charcoal biological fiber facial mask base cloth, and also relates to a high water-locking and anti-dripping bamboo charcoal biological fiber facial mask base cloth with high water-locking and moisturizing Facial mask. Background technique [0002] With the development of society, people pay more and more attention to skin care and beauty, which makes facial mask, a skin care product, from the original special care product to today's daily fast-moving consumer product, occupying an important share of the beauty cosmetics market. Masks can be divided into four types according to their product forms: mask stickers (peelable masks), gel masks, cream (milk) masks, and powder masks. Among them, mask stickers are divided into base cloth masks made of natural or synthetic fibers and A gel mask processed into a sheet with a gel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04H1/728D01D5/00D06M11/74D04H1/492D06M15/03D06M15/13A61K8/02A61K8/9794A61Q19/00D06M101/32
CPCA61K8/0212A61K8/97A61Q19/00D01D5/003D04H1/492D04H1/728D06M11/74D06M15/03D06M15/13D06M2101/32
Inventor 魏科峰
Owner 广东柏俐臣生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com