Preparation of array-structure transition metal selenide electrode and application of array-structure transition metal selenide electrode to electrolyzed water

A transition metal, array structure technology, applied in water/sewage treatment, chemical instruments and methods, water/sludge/sewage treatment, etc., can solve the problem of insufficient exposure of active sites, unfavorable mass transfer and electron transfer, inhibition of development and application issues, to achieve the effects of excellent electrocatalytic water splitting performance, controllable synthesis process, and easy implementation.

Active Publication Date: 2018-08-24
BEIJING UNIV OF TECH
View PDF8 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nevertheless, there are still some problems in the synthesis of MOFs, such as the powder is easy to agglomerate, the active sites cannot be fully exposed, etc., which is not conducive to mass transfer and electron transfer, and inhibits its development and application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation of array-structure transition metal selenide electrode and application of array-structure transition metal selenide electrode to electrolyzed water
  • Preparation of array-structure transition metal selenide electrode and application of array-structure transition metal selenide electrode to electrolyzed water
  • Preparation of array-structure transition metal selenide electrode and application of array-structure transition metal selenide electrode to electrolyzed water

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The first step is to treat the nickel sheet (NF) with hydrochloric acid, acetone, ethanol and water for 10 minutes. -15 minutes, use the same method to sequentially use acetone, ethanol and water for ultrasonic cleaning. Then dry the cleaned NF for the next step.

[0023] In the second step, NF is immersed in mother liquor B for hydrothermal reaction. Mother liquor B is 0.15g of 2,5-dihydroxyterephthalic acid and 0.7g of cobalt nitrate hexahydrate dissolved in 20ml of N,N-dimethylformamide and water mixed solution with ethanol. The volume ratio of N,N-dimethylformamide to water and ethanol is 1:1:1, and transferred into a 100ml reactor for hydrothermal reaction at 100°C for 15 hours. After the reaction, the NF-Co-MOF composite was obtained by washing with ethanol and N,N-dimethylformamide several times.

[0024] In the third step, 0.1-0.3g of selenium powder and the NF-Co-MOF composite material synthesized in the previous step are placed in a magnetic boat at the sam...

Embodiment 2

[0026] The first step is to pretreat the nickel sheet (NF) with hydrochloric acid, acetone, ethanol and water for 10 minutes. For 10-15 minutes, use the same method to sequentially use acetone, ethanol and water for ultrasonic cleaning. Then dry the cleaned NF for the next step.

[0027] In the second step, NF is immersed in mother liquor B for hydrothermal reaction. Mother liquor B is 0.15g of 2,5-dihydroxyterephthalic acid and 0.7g of nickel nitrate hexahydrate dissolved in 20ml of N,N-dimethylformamide and water mixed solution with ethanol. The volume ratio of N,N-dimethylformamide to water and ethanol is 1:1:1, and transferred into a 100ml reactor for hydrothermal reaction at 100°C for 15 hours. After the reaction, the NF-Ni-MOF composite was obtained by washing with ethanol and N,N-dimethylformamide several times.

[0028] In the third step, 0.1-0.3g of selenium powder and the NF-Ni-MOF composite material synthesized in the previous step are placed in a magnetic boat a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides preparation of an array-structure transition metal selenide electrode and application of the array-structure transition metal selenide electrode to electrolyzed water and belongs to the technical field of electrodes. The preparation comprises the following steps: step 1, optimizing a nickel sheet (NF) substrate through simple pre-treatment; step 2, uniformly forming a metalorganic framework material (Mn / Fe / Co / Ni / Cu-MOF) nano-array on the surface of the nickel sheet substrate in situ, so as to obtain an NF-MOFs material; step 3, carrying out selenation on the surface ofan MOFs nano-array in situ to finally prepare an NF-MxSey nano-array electrode material. The NF-MxSey is used as an electrolyzed water electrode, has a relatively low starting site, relatively large current density, excellent electro-catalytic water decomposition performance and relatively high stability, and can be applied to new energy source storage and conversion devices for the electrolyzed water and the like.

Description

technical field [0001] The invention belongs to the technical field of electrocatalysis development in the conversion field of new energy storage. The technology involves the construction of metal-organic framework materials (MOFs) and the preparation of array-structured transition metal selenides (NF-M x Se y )electrode. Background technique [0002] With the rapid development of industrial production and the continuous increase of population, fossil fuels mainly represented by coal, oil and natural gas have been consumed in large quantities in recent decades, causing inevitable environmental pollution and energy shortage. Therefore, finding a clean and renewable energy source has increasingly become the development demand of the present era. Among many materials, hydrogen, as a green, efficient, and energy-rich clean energy, is a potential substitute for fossil energy in the future. Renewable characteristics can well solve the two major problems of energy crisis and en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/461
CPCC02F1/46109C02F2001/46138Y02E60/36
Inventor 李建荣刘名乘豆义波谢亚勃魏欣
Owner BEIJING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com