Fireproof door core and preparation method thereof

A fire-resistant door core and closed-cell technology, applied in the field of doors and windows, can solve the problems of poor fire resistance, endangering life and health and property safety, poor toughness, etc., and achieve the effect of improving toughness, good stability and good fire resistance.

Inactive Publication Date: 2018-08-17
HEFEI YIZHI DOORS & WINDOWS CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the fireproof door cores in the prior art have disadvantages such as poor fire resistance and poor toughness, which seriously endanger people's lives, health and property safety.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] This embodiment relates to a fire door core, including the following raw materials by weight: 10 parts of closed-cell expanded perlite, 15 parts of gypsum, 20 parts of cement, 7 parts of coated nano-fly ash, 5 parts of silica fume, and 5 parts of magnesium sulfate. parts, 4 parts of bleaching beads, 5 parts of calcined kaolin, 2 parts of sodium methyl silicate, 3 parts of calcium stearate, 1 part of foaming agent, 2 parts of glass fiber, and 1 part of polypropylene fiber.

[0027] Wherein, the preparation method of described coated nano fly ash is as follows:

[0028] (1) Ball milling and dispersing the fly ash with alcohol for 3 hours, then adding 3% by weight of alkyl glycosides, 2% tricresyl phosphate and 8% deionized water to it, and keeping the temperature at 60°C. Stir and heat in a water bath for 45 minutes to obtain a dispersion;

[0029] (2) Add aluminum sulfate solution with a concentration of 25% equivalent to 15% of its weight into the dispersion, and at th...

Embodiment 2

[0039] This embodiment relates to a fire door core, which includes the following raw materials by weight: 20 parts of closed-cell expanded perlite, 28 parts of gypsum, 30 parts of cement, 14 parts of coated nano-fly ash, 12 parts of silica fume, and 10 parts of magnesium sulfate. parts, 9 parts of bleaching beads, 12 parts of calcined kaolin, 6 parts of sodium methyl silicate, 5 parts of calcium stearate, 2 parts of foaming agent, 4 parts of glass fiber, and 3 parts of polypropylene fiber.

[0040] Wherein, the preparation method of described coated nano fly ash is as follows:

[0041] (1) Ball milling and dispersing the fly ash with alcohol for 3 hours, then adding 3% by weight of alkyl glycosides, 2% tricresyl phosphate and 8% deionized water to it, and keeping the temperature at 70°C. Stir and heat in a water bath for 45 minutes to obtain a dispersion;

[0042] (2) Add aluminum sulfate solution with a concentration of 25% equivalent to 15% of its weight into the dispersion...

Embodiment 3

[0052]This embodiment relates to a fire door core, including the following raw materials by weight: 13 parts of closed-cell expanded perlite, 17 parts of gypsum, 22 parts of cement, 8 parts of coated nano-fly ash, 7 parts of silica fume, and 6 parts of magnesium sulfate. parts, 5 parts of bleaching beads, 6 parts of calcined kaolin, 3 parts of sodium methyl silicate, 3.5 parts of calcium stearate, 1.2 parts of foaming agent, 2.5 parts of glass fiber, and 1.7 parts of polypropylene fiber.

[0053] Wherein, the preparation method of described coated nano fly ash is as follows:

[0054] (1) Ball milling and dispersing the fly ash with alcohol for 3 hours, then adding 3% by weight of alkyl glycosides, 2% tricresyl phosphate and 8% deionized water to it, and keeping it at a constant temperature of 63°C. Stir and heat in a water bath for 45 minutes to obtain a dispersion;

[0055] (2) Add aluminum sulfate solution with a concentration of 25% equivalent to 15% of its weight into the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fireproof door core, comprising, by weight, 10 parts of closed-cell expanded perlite, 15 parts of gypsum, 20 parts of cement, 7 parts of coated nano flyash, 5 parts of silicafume, 5 parts of magnesium sulfate, 4 parts of floating beads, 5 parts of calcined kaolin, 2 parts of sodium methyl silicate, 3 parts of calcium stearate, 1 part of a foaming agent, 2 parts of glassfiber, and 1 part of polypropylene fiber. The fireproof door core has good fireproof performance, is harmless to human bodies and environment, and has good toughness and stability.

Description

technical field [0001] The invention belongs to the technical field of doors and windows, and in particular relates to a fireproof door core and a preparation method thereof. Background technique [0002] The fire door is composed of skeleton, door core filling material and fireproof hardware. The filling material of the door core board is the core material of the fire door, and its quality and performance are particularly important. [0003] However, the fireproof door core in the prior art has shortcomings such as poor fireproof performance and poor toughness, which seriously endanger people's life, health and property safety. SUMMARY OF THE INVENTION [0004] The present invention provides a fireproof door core and a preparation method thereof, which solve the problems in the above-mentioned background technology. [0005] In order to solve the problems existing in the prior art, the following technical solutions are adopted: [0006] A fire door core, comprising the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B38/10C04B20/10C04B20/02C04B20/04E06B3/70C04B111/28C04B18/08
CPCC04B20/1066C04B28/14C04B2111/28E06B3/7015E06B2003/7023E06B2003/7028C04B14/185C04B7/00C04B18/08C04B18/146C04B22/142C04B18/082C04B14/106C04B24/42C04B24/085C04B14/42C04B16/0633C04B24/16C04B38/10C04B20/023C04B20/026C04B20/04Y02W30/91
Inventor 汪中奇
Owner HEFEI YIZHI DOORS & WINDOWS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap