Printing method of polyester blended fabrics

A technology of blended fabrics and printing methods, applied in dyeing, textiles and papermaking, etc., can solve the problems of poor color fastness, easy fading of fabrics, etc., and achieve good printing effect.

Inactive Publication Date: 2018-07-06
海宁市美元达经编有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the printing method disclosed in this patent has strong practicability, the steps of the printing method are relatively simple, and the fabric is prone to fading after washing, and the color fastness is poor. Therefore, it is necessary to design a printing method for polyester blended fabrics. of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Printing method of polyester blended fabrics
  • Printing method of polyester blended fabrics
  • Printing method of polyester blended fabrics

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] The following are specific embodiments of the present invention and in conjunction with the accompanying drawings, further describe the technical solution of the present invention, but the present invention is not limited to these embodiments.

[0037] The printing method of this polyester blended fabric comprises the steps:

[0038] a, pretreatment: remove the impurities on the surface of the polyester blended fabric by a hot air blower, and preheat it. The temperature of the hot air blower is 28-36 ° C; Impurities are removed and preheated, the temperature of the hot air blower is 30°C;

[0039] b. Printing treatment: the polyester blended fabric is printed by a liquid jet printing machine, and the printing temperature is 45-55°C; in this embodiment, the polyester blended fabric is printed by a liquid jet printing machine, and the printing temperature is 48°C ;

[0040]c. Color fixation treatment: put the printed polyester blended fabric into a steamer for steam fix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a printing method of polyester blended fabrics. By adoption of the printing method, the technical problems of simpler steps, easy fading and poor color fastness of fabrics afterwashing and the like in the existing printing method are solved. The printing method of the polyester blended fabric comprises the following steps of: (a) pretreatment: removing impurities on the surfaces of the polyester blended fabrics by a hot-air blower, carrying out preheating treatment on the polyester blended fabrics, wherein the temperature of the hot-air blower is 28-36 DEG C; (b) printing treatment: carrying out printing treatment on the polyester blended fabrics by a liquid-spraying printing machine, wherein the printing temperature is 45-55 DEG C; (c) fixation treatment: placing printed polyester blended fabrics into a steaming box to carry out steam fixation treatment, wherein the temperature of the steaming box is 100-110 DEG C; (d) washing treatment: firstly using cold water with the temperature of 20-26 DEG C to wash for 4-8 minutes, then using hot water with the temperature of 40-50 DEG C to wash for 3-4 minutes; (e) drying treatment: placing the washed polyester blended fabrics into a drying oven to carry out drying treatment and then obtaining the printed polyester blended fabrics. The printing method provided by the invention has the advantage of good printingeffect.

Description

technical field [0001] The invention relates to a printing method for polyester blended fabrics. Background technique [0002] Blended or blended chemical fiber fabrics are textile products made of chemical fibers mixed with other cotton wool, silk, hemp and other natural fibers. It has both the style of polyester and the advantages of cotton fabrics, such as polyester cotton cloth and polyester wool gabardine. Blending is divided into wool-viscose blending, sheep and rabbit wool spinning, TR fabrics, high-density NC fabrics, 3M waterproof mousse fabrics, Tencel fabrics, Rousai silk, TNC fabrics, composite fabrics, etc. [0003] After searching, for example, Chinese patent literature discloses a printing method for hemp blended fabrics [application number: 201710821918.6; publication number: CN 107653713A]. The printing method of this hemp blended fabric is characterized in that it comprises the following steps: a. Take 3-6 parts of printing paste, 4-5 parts of thickener, 0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06P3/82D06P5/02D06P7/00
CPCD06P3/8204D06P5/02D06P7/00
Inventor 张左元
Owner 海宁市美元达经编有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com