Allergy prevention toothpaste and production method thereof

An anti-allergy, toothpaste technology, applied in allergic diseases, dentistry, pharmaceutical formulations, etc., can solve the problems of shortening the service life of toothpaste, unstable peroxides, etc., to inhibit the growth of bacteria, freshen breath, and prevent gum inflammation. Effect

Inactive Publication Date: 2018-06-05
房世俊
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the main method is to add peroxide into toothpaste to remove dental plaque, the cleaning effect is better, but due to the instability of peroxide, the service life of toothpaste is shortened

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The hypoallergenic toothpaste comprises the following components by mass:

[0020] 3 parts of nano silicon dioxide, 0.2 parts of microcrystalline cellulose, 0.01 parts of sodium lauryl sulfate, 0.03 parts of polyethylene glycol, 0.5 parts of xylitol, 0.02 parts of snow lotus flower extract, 0.02 parts of sodium fluoride, carboxymethyl 0.5 parts of sodium cellulose, 0.01 parts of tea polyphenols, 0.05 parts of ginkgo extract, 1 part of sodium alginate, and 6 parts of water.

[0021] Nano-silica, microcrystalline cellulose, sodium lauryl sulfate, polyethylene glycol, xylitol, snow lotus extract, sodium fluoride, sodium carboxymethyl cellulose, tea polyphenols, ginkgo extract, seaweed sodium bicarbonate, water. Add it into the reaction container according to the proportion, and stir at 50-80° C. for 1.5 hours to obtain the hypoallergenic toothpaste.

Embodiment 2

[0023] The hypoallergenic toothpaste comprises the following components by mass:

[0024] 3 parts of nano silicon dioxide, 0.25 parts of microcrystalline cellulose, 0.03 parts of sodium lauryl sulfate, 0.04 parts of polyethylene glycol, 0.55 parts of xylitol, 0.02 parts of snow lotus flower extract, 0.025 parts of sodium fluoride, carboxymethyl 0.6 parts of sodium cellulose, 0.02 parts of tea polyphenols, 0.06 parts of ginkgo extract, 1.2 parts of sodium alginate, and 7 parts of water.

[0025] Nano-silica, microcrystalline cellulose, sodium lauryl sulfate, polyethylene glycol, xylitol, snow lotus extract, sodium fluoride, sodium carboxymethyl cellulose, tea polyphenols, ginkgo extract, seaweed sodium bicarbonate, water. Add it into the reaction container according to the proportion, and stir at 50-80° C. for 1.5 hours to obtain the hypoallergenic toothpaste.

Embodiment 3

[0027] 6 parts of nano-silica, 0.25 parts of microcrystalline cellulose, 0.04 parts of sodium lauryl sulfate, 0.04 parts of polyethylene glycol, 0.5 parts of xylitol, 0.03 parts of snow lotus flower extract, 0.02 parts of sodium fluoride, carboxymethyl 0.8 parts of sodium cellulose, 0.03 parts of tea polyphenols, 0.08 parts of ginkgo extract, 1.5 parts of sodium alginate, and 8 parts of water.

[0028] The preparation method of above-mentioned hypoallergenic toothpaste is characterized in that, comprises the steps:

[0029] Nano-silica, microcrystalline cellulose, sodium lauryl sulfate, polyethylene glycol, xylitol, snow lotus extract, sodium fluoride, sodium carboxymethyl cellulose, tea polyphenols, ginkgo extract, seaweed sodium bicarbonate, water. Add it into the reaction container according to the proportion, and stir at 50-80° C. for 1.5 hours to obtain the hypoallergenic toothpaste.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention provides an allergy prevention toothpaste, which comprises, by mass, 3-6 parts of nanometer silica, 0.2-0.3 part of microcrystalline cellulose, 0.01-0.05 part of sodium lauryl sulfate, 0.03-0.05 part of polyethylene glycol, 0.5-0.6 part of xylitol, 0.02-0.03 part of a saussurea involucrata extract, 0.02-0.03 part of sodium fluoride, 0.5-0.8 part of sodium carboxymethyl cellulose, 0.01-0.03 part of tea polyphenol, 0.05-0.08 part of a ginkgo extract, 1-1.5 part of sodium alginate, and 6-8 part of water. The invention further discloses a preparation method of the whitening toothpaste. According to the present invention, the toothpaste has effects of gingiva inflammation prevention and breath refreshing, can protect the health of gingiva in an assisted manner, and can relieve oral ulcer, gingiva swelling and pain and other symptoms.

Description

technical field [0001] The invention belongs to the technical field of daily necessities, and in particular relates to an antiallergic toothpaste and a preparation method thereof. Background technique [0002] In today's society, people pay more and more attention to their oral hygiene and health. A white tooth has become the goal pursued by many people. How to effectively remove dental plaque on the surface of teeth has become a topic of concern in the field of scientific research. At present, it is mainly used to add peroxide into toothpaste to remove dental plaque, and its cleaning effect is better, but due to the instability of peroxide, the service life of toothpaste is shortened. Therefore, it is necessary to search for a novel material that is stable and effective in cleaning dental plaque. Contents of the invention [0003] Purpose of the invention: to provide a hypoallergenic toothpaste and its preparation method. [0004] Technical solutions: [0005] A kind o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/9789A61K8/9771A61K8/86A61K8/73A61K8/46A61K8/34A61K8/25A61K8/21A61Q11/00A61Q17/00A61P37/08A61P31/04A61P1/02
CPCA61K8/25A61K8/21A61K8/345A61K8/463A61K8/731A61K8/733A61K8/86A61K8/97A61Q11/00A61Q17/005
Inventor 不公告发明人
Owner 房世俊
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com