Inoculating agent used for thin-walled ferrite nodular cast iron and preparing method of inoculating agent

A technology of nodular cast iron and ferrite, which is applied in the field of inoculants for thin-walled ferritic nodular cast iron and its preparation, can solve the problems of unstable inoculation effect and scrapped castings, and achieve the elimination of poor spheroidization, carbides, The effect of promoting graphite nucleation

Inactive Publication Date: 2018-01-23
ANHUI POLYTECHNIC UNIV MECHANICAL & ELECTRICAL COLLEGE
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the amount of ferrosilicon inoculants still accounts for more than 80% of the total amount of cast iron inoculants, resulting in unstable inoculation effects and often scrapped castings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0016] The present invention also provides a method for preparing the inoculant for thin-walled ferritic nodular cast iron described above, the preparation method comprising: (1) according to the chemical composition and mass percentage of the inoculant for thin-walled ferritic nodular cast iron Weighing raw materials for blending; (2) smelting the blended raw materials; (3) pouring, cooling, crushing and granulating the smelted product. For example, the chemical composition and mass percentage here can be obtained by formulating and calculating according to the content of each element in the raw materials used, as long as those skilled in the art can understand the method can be used here.

[0017] Through the above technical scheme, the inoculant for thin-walled ferritic nodular cast iron of the present invention has the following advantages: (1) suppress pearlite and promote the formation of ferrite: use aluminum to increase the ferrite content, add an appropriate amount of ...

Embodiment 1

[0024] A method for preparing an inoculant for thin-walled ferritic ductile iron, characterized in that the preparation method comprises:

[0025] (1) According to the chemical composition and mass percentage of the inoculant for thin-walled ferritic nodular cast iron, the raw materials are weighed for deployment: the total weight of the inoculant for thin-walled ferritic nodular cast iron is 100%, and the thin-walled ferritic nodular cast iron The chemical composition of the inoculant for cast iron includes: 68.6% Si, 2.6% RE, 1.2% Sr, 0.4% Bi, 1.6% Ca, 2.6% Ba, 0.32% Al, and the balance is Fe;

[0026] (2) Smelting the prepared raw materials at 1490°C;

[0027] (3) Cast the smelt at 1510° C., cool, crush and granulate.

Embodiment 2

[0029] A method for preparing an inoculant for thin-walled ferritic ductile iron, characterized in that the preparation method comprises:

[0030] (1) According to the chemical composition and mass percentage of the inoculant for thin-walled ferritic nodular cast iron, the raw materials are weighed for deployment: the total weight of the inoculant for thin-walled ferritic nodular cast iron is 100%, and the thin-walled ferritic nodular cast iron The chemical composition of the inoculant for cast iron includes: 69.6% Si, 3.4% RE, 1.8% Sr, 0.6% Bi, 2.6% Ca, 3.6% Ba, 0.46% Al, and the balance is Fe;

[0031] (2) Smelting the prepared raw materials at 1520°C;

[0032] (3) Cast the smelt at 1530° C., cool, crush and granulate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an inoculating agent for thin-walled ferrite nodular cast iron. With the total weight of the inoculating agent for the thin-walled ferrite nodular cast iron being 100%, the inoculating agent for the thin-walled ferrite nodular cast iron comprises, by weight, 68-70% of Si, 2-4% of RE, 1-2% of Sr, 0.3-0.8% of Bi, 1.0-3.0% of Ca, 2.0-4.0% of Ba, 0.3-0.5% of Al and the balanceFe. The obtained thin-walled ferrite nodular cast iron has the functions of promoting graphite nucleation, reducing chilling tendency, increasing the number of the nodular cast iron and improving theintegrity of the nodular cast iron, the ferrite content can be remarkably improved in a casting state, and the elongation and strength of the nodular cast iron are improved.

Description

technical field [0001] The invention relates to the field of ductile iron casting, in particular to an inoculant for thin-walled ferrite ductile iron and a preparation method thereof. Background technique [0002] The inoculant is a kind of inoculant that can promote graphitization, reduce the tendency of whitening, improve the morphology and distribution of graphite, increase the number of eutectic groups, and refine the matrix structure. It has a good effect in a short time after inoculation treatment. In the production of ductile iron, inoculation is an essential process due to the relatively large tendency of supercooling. The main function of using inoculants for inoculation treatment is to increase the number of graphite nodules in ductile iron, improve their roundness, refine graphite nodules, prevent spheroidization recession, reduce the tendency of white mouth, and prevent the formation of free particles between eutectic clusters. Cementite and segregation. The mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C33/08C22C37/04C21C1/10
Inventor 柴知章席世亨许本琪张月茹
Owner ANHUI POLYTECHNIC UNIV MECHANICAL & ELECTRICAL COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com