A preparation process of Jun porcelain with natural cracks

A preparation process and a technology for natural cracks, which are applied in the field of the preparation process of Jun porcelain with natural cracks, can solve the problems of difficult firing, low rate of Jun porcelain treasures, complicated production process, etc., and achieve the effect of preventing falling off.

Inactive Publication Date: 2020-10-16
YUZHOU ZHENGYUJUN KILN CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the production process of Jun porcelain has always been complicated, and it is not easy to fire. From the selection of materials to the firing of finished products, there are many processes to go through. The reason for the extremely low treasure rate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Step 1. Put the dried biscuit into the kiln for firing, close the kiln door when the firing temperature rises to 550°C, and stop the fire when the temperature continues to rise to 980°C. The heating rate at this stage is 20°C / min. Take it out after cooling to get plain tires;

[0033] Step 2: Attach a layer of 0.1cm-thick green body slurry on the surface of the plain tire, and then put it into the kiln again for secondary firing. When the temperature is 550°C, the heating rate is 12°C / min, and the temperature rises When the heating rate is as high as 980 °C, the heating rate is 5 °C. At this time, the heating rate should not be too fast to avoid the outer layer of the green body from falling off;

[0034] Step 3. When the plain embryo after the secondary firing is cooled to 190°C, it is taken out and placed in a constant temperature and pressure container with a pressure of 200MPa and a temperature of 80°C. After being kept warm for 1 hour, it is taken out and naturally...

Embodiment 2

[0045] Step 1. Put the dried green body into the kiln for firing. When the firing temperature rises to 575°C, close the kiln door, and stop the fire when the temperature continues to rise to 990°C. The heating rate at this stage is 21°C / min. Take it out after cooling to get plain tires;

[0046] Step 2: Attach a layer of 0.15cm-thick green body slurry on the surface of the plain body, and then put it into the kiln again for secondary firing. When the temperature is 575°C, the heating rate is 13°C / min, and the temperature rises When the heating rate is as high as 990 °C, the heating rate is 6 °C. At this time, the heating rate should not be too fast, so as to avoid the outer layer of the green body from falling off;

[0047] Step 3. When the plain embryo after the secondary firing is cooled to 195°C, it is taken out and placed in a constant temperature and pressure container with a pressure of 200MPa and a temperature of 90°C. After being kept warm for 1.5 hours, it is taken ou...

Embodiment 3

[0058] Step 1. Put the dried biscuit into the kiln for firing, close the kiln door when the firing temperature rises to 600°C, and stop the fire when the temperature continues to rise to 1000°C. The heating rate at this stage is 22°C / min. Take it out after cooling to get plain tires;

[0059] Step 2: Attach a layer of 0.2cm-thick green body slurry on the surface of the plain tire, and then put it into the kiln again for secondary firing. When the temperature is 600°C, the heating rate is 14°C / min, and the temperature rises When the heating rate reaches 1000°C, the heating rate is 7°C. At this time, the heating rate should not be too fast to prevent the outer layer of the green body from falling off;

[0060] Step 3. When the plain embryo after the secondary firing is cooled to 200° C., it is taken out and placed in a container with a pressure of 200 MPa and a temperature of 100° C., taken out after 2 hours of heat preservation, and naturally cooled to room temperature;

[006...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

A preparation method of Jun porcelain with natural cracks comprises specific steps as follows: step 1, a dried biscuit is placed in a kiln for primary firing and a base is obtained; step 2, a layer ofbiscuit material which is 0.1-0.2 cm thick is attached to the surface of the base, and the base is placed in the kiln again for secondary firing; step 3, the base subjected to secondary firing is taken out and placed in a constant-temperature and constant-pressure container after being cooled to 200 DEG C, kept at the constant temperature for 1-2 h, taken out and naturally cooled to the room temperature; step 4, the base subjected to secondary firing is glazed and the glazed base is dried again; step 5, the glazed base is placed in the kiln to be fired, and three stages of glaze firing are performed during firing. The biscuit is subjected to a series of biscuit firing and glaze firing, the strength of the biscuit of Jun porcelain is improved, glazing of the biscuit is facilitated, unevenconcave-convex surfaces occur due to existence of natural cracks on surfaces, and the Jun porcelain is brighter in color gradation due to difference between heating degrees during heating.

Description

technical field [0001] The invention belongs to the field of Jun porcelain, in particular to a preparation process of Jun porcelain with natural cracks. Background technique [0002] Jun kiln is one of the five famous kilns in the Song Dynasty in China. It is on par with Ru, Guan, Ge and Ding kilns. The traditional works of Jun porcelain, such as statues, tripods, bowls, washers, and bottles, are placed in the court room, which is magnificent and full of brilliance; Chen's few cases are pleasing to the eye and elegant. However, the production process of Jun porcelain has always been complicated, and it is not easy to fire. From the selection of materials to the firing of finished products, there are many processes to go through. The reason for the extremely low treasure rate. [0003] The traditional firing method of Jun kiln is to use copper oxide as the colorant and fire at 1280-1300°C. The bisque is firstly fired before being glazed, and then fired after being glazed. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/34C04B41/86
Inventor 王现锋
Owner YUZHOU ZHENGYUJUN KILN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com