Preparation method of graphene quantum dot supported Ag-TiO2 nano array

A technology of graphene quantum dots and nano-arrays, applied in the direction of light water/sewage treatment, etc., can solve problems such as toxicity, unsatisfactory visible light response performance, and complicated preparation process

Inactive Publication Date: 2018-01-16
HEFEI NORMAL UNIV
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to overcome the preparation of TiO in the prior art 2 The visible light response performance of the film is not ideal, the preparation process is complicated, the required chemical reagents are expensive or toxic, etc., providing a graphene quantum dot loaded Ag-TiO 2 A method for preparing nano-arrays, which has low-value raw materials, non-toxicity, and simple preparation process. In TiO 2 Ag nanoparticles and graphene quantum dots are loaded on the nanoarrays, and through the joint action of the two, the TiO 2 Visible light response properties of nanoarrays

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of graphene quantum dot supported Ag-TiO2 nano array
  • Preparation method of graphene quantum dot supported Ag-TiO2 nano array
  • Preparation method of graphene quantum dot supported Ag-TiO2 nano array

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A graphene quantum dot supported Ag-TiO 2 The preparation method of nanometer array specifically comprises the following steps:

[0031] The present invention uses FTO conductive glass (1 * 1.5 * 0.21cm) as substrate, and FTO conductive glass is ultrasonically cleaned in acetone and deionized water respectively for 20 minutes, to remove organic pollutants and impurities on the surface of the FTO film, and the cleaned FTO Conductive glass is dried in an atmosphere at 60°C.

[0032] Mix 20 ml of hydrochloric acid, 20 ml of deionized and 0.68 ml of butyl titanate, and after stirring magnetically at room temperature for 30 minutes, transfer the solution to a 50 ml autoclave lined with polytetrafluoroethylene, and place the cleaned FTO conductive glass Tilt in the autoclave, put the autoclave into an oven at 150°C, react for 10 hours, cool to room temperature naturally, take out the sample, wash the sample with deionized water several times, and dry the sample in an oven at...

Embodiment 2

[0039] The steps in this embodiment two are basically the same as those in embodiment one, the difference is:

[0040] Drop 0.5 ml of graphene quantum dot dispersion liquid on the sample surface each time, let it stand for 5 minutes, wait for the dispersion liquid to infiltrate the sample, and then use the spin coating technology to evenly coat the dispersion liquid on the sample surface, and the spin coating rotation speed is 1000 revolutions / min, the coating time was 5 seconds, and then the sample was dried in the atmosphere at 100°C, and the above process was repeated 12 times to obtain graphene quantum dot-loaded Ag-TiO 2 Nanoarrays; samples also formed graphene quantum dots supported on Ag-TiO 2 Nanoarray composite nanomaterials, Ag-TiO modified by 12 graphene quantum dots 2 The number of graphene quantum dots on the nano-array is significantly increased, and the UV-visible absorption spectrum test results of the sample show that, compared with the sample obtained in Ex...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a graphene quantum dot supported Ag-TiO2 nano array. The preparation method comprises the following steps: (a) preparing a TiO2 nano array; (b) preparing an Ag-TiO2 nano array: reducing Ag nano particles (Ag<+>) loaded on the TiO2 nano array prepared in the step (a) by UV rays to obtain the Ag-TiO2 nano array; and (c) preparing a graphene quantum dotsupported Ag-TiO2 nano array: evenly painting a graphene quantum dot dispersion liquid onto the surface of the Ag-TiO2 nano array prepared in the step (b) by a spinning coating technology, and dryingto obtain the graphene quantum dot supported Ag-TiO2 nano array. The raw materials are cheap and nontoxic, the preparation process is simple, Ag nano particles and graphene quantum dots are loaded onTiO2 nano arrays, and through the cooperation of Ag nano particles and graphene quantum dots, the visible light responsive performance of TiO2 nano array is enhanced.

Description

technical field [0001] The invention relates to a graphene quantum dot loaded Ag-TiO 2 The invention relates to a method for preparing a nano array, which belongs to the technical field of nano composite materials. Background technique [0002] At present, the energy crisis and environmental issues have become two key issues restricting the world's economic and social development. Photocatalytic degradation technology is expected to become an effective way to solve energy and environmental problems. Using solar photolysis technology to convert solar energy into clean hydrogen is expected to solve the energy crisis caused by the depletion of fossil energy; in addition, through photocatalytic degradation technology It can degrade toxic organic pollutants and will become an effective way to solve environmental problems. Energy and environmental issues are two major issues facing the world today. Therefore, the development and utilization of clean renewable energy (such as: so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/50C02F1/30
Inventor 吕建国赵敏祝钱钱曾争汪文豪
Owner HEFEI NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com