Composite carbon fiber spectacle frame and preparation process thereof

A technology of composite carbon fiber and preparation process, applied in the field of glasses, can solve the problems of high production cost of carbon fiber glasses frames, lower radial strength than axial strength, and great influence of carbon fiber strength, etc., and achieves good curing effect, improved wear resistance, Good mixing effect

Inactive Publication Date: 2017-12-26
东莞市鼎耀实业有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The carbon fiber spectacle frames of the prior art have the following defects. On the one hand, due to the high price of carbon fiber, the production cost of the carbon fiber spectacle frame is high; For reasons such as objects, the spectacle frame is prone to self-bacteria, which is not conducive to human health. In the third aspect, carbon fiber is easy to oxidize. Due to friction with the human body and heat generation, the material is heated and aged, and the spectacle frame will harden, which greatly reduces the service life of the spectacle frame. Fourth, the strength of carbon fiber is greatly affected by the environment, and the radial strength is not as good as the axial strength, so it is easy to scratch. Fifth, it does not have a luminous effect, and there are potential safety hazards for users when walking at night

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite carbon fiber spectacle frame and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0029]The composite carbon fiber spectacle frame is made of the following raw materials in parts by weight: 10 parts of carbon fiber, 23 parts of acetate fiber, 60 parts of epoxy resin, 3 parts of wear-resistant agent, 1 part of antibacterial agent, 0.5 part of luminous material, and 0.5 part of antioxidant , 1 part of coupling agent, 0.5 part of lubricant, 0.5 part of compatibilizer.

[0030] Among them, the wear-resistant agent is a mixture of graphite and polytetrafluoroethylene; the antibacterial agent is nano-silver; the luminous material is Zn 3 Ga 2 Ge 2 o 10 :Cr 3+ , the particle size of the material is 200nm; the antioxidant is antioxidant 1010 [3-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid] pentaerythritol and antioxidant 168 (three (2,4-di tert-butylphenyl) phosphite) mixture; coupling agent is aminosilane coupling agent; lubricant is stearylamide lubricant; described compatibilizer is the copolymer of styrene and maleic anhydride, The length of the carb...

specific Embodiment 2

[0031] The composite carbon fiber spectacle frame is made of the following raw materials in parts by weight: 20 parts of carbon fiber, 21 parts of acetate fiber, 52 parts of epoxy resin, 1 part of wear-resistant agent, 1 part of antibacterial agent, 0.5 part of luminous material, and 0.5 part of antioxidant , 3 parts of coupling agent, 0.5 part of lubricant, 0.5 part of compatibilizer.

[0032] Among them, the wear-resistant agent is a mixture of graphite and polytetrafluoroethylene; the antibacterial agent is nano-silver; the luminous material is Zn 3 Ga 2 Ge 2 o 10 :Cr 3+ , the particle size of the material is 200nm; the antioxidant is antioxidant 1010 [3-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid] pentaerythritol and antioxidant 168 (three (2,4-di tert-butylphenyl) phosphite) mixture; coupling agent is aminosilane coupling agent; lubricant is stearylamide lubricant; described compatibilizer is the copolymer of styrene and maleic anhydride, The length of the car...

specific Embodiment 3

[0033] The composite carbon fiber spectacle frame is made of the following raw materials in parts by weight: 20 parts of carbon fiber, 21 parts of acetate fiber, 52 parts of epoxy resin, 1 part of wear-resistant agent, 1 part of antibacterial agent, 0.5 part of luminous material, and 0.5 part of antioxidant , 3 parts of coupling agent, 0.5 part of lubricant, 0.5 part of compatibilizer.

[0034] Among them, the wear-resistant agent is a mixture of graphite and polytetrafluoroethylene; the antibacterial agent is nano-silver; the luminous material is Zn 3 Ga 2 Ge 2 o 10 :Cr 3+ , the particle size of the material is 200nm; the antioxidant is antioxidant 1010 [3-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid] pentaerythritol and antioxidant 168 (three (2,4-di tert-butylphenyl) phosphite) mixture; coupling agent is aminosilane coupling agent; lubricant is stearylamide lubricant; described compatibilizer is the copolymer of styrene and maleic anhydride, The length of the car...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of spectacles, and especially relates to a composite carbon fiber spectacle frame and a production process thereof. The composite carbon fiber spectacle frame is prepared from the following raw materials, in parts by weight: 10-30 parts of carbon fibers, 20-40 parts of cellulose acetate fibers, 30-60 parts of epoxy resin, 1-3 parts of a wear resistant agent, 0.5-1.5 parts of an antibacterial agent, 0.5-1 part of a luminous material, 0.5-1 part of an antioxidant, 1-3 parts of a coupling agent, 0.5-1.5 parts of a lubricant, and 0.5-1.5 parts of a compatilizer. The composite carbon fiber spectacle frame has low production costs, high strength, long service life, antibacterial properties and a luminous effect, and is not easy to scratch and beneficial for human health and security.

Description

technical field [0001] The invention relates to the field of spectacles, in particular to a composite carbon fiber spectacle frame and a production process thereof. Background technique [0002] The spectacle frame is an important part of the glasses, mainly to support the spectacle lens, and the spectacle frame with a beautiful appearance can also play an aesthetic role. [0003] The spectacle frame is composed of the main parts such as the frame, the bridge, the nose pads, the studs and the temples. The frame is where the lenses are fitted. The middle beam is used to connect the left and right frames to fix the lens position. The nose pad is used for direct contact with the nose and plays a role in supporting and stabilizing the spectacle frame. The pile head is used for the connection of the mirror frame and mirror feet. The mirror feet are used to hang on the ears and play a role in fixing the mirror frame. [0004] According to the material, there are mainly metal ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08L1/12C08L27/18C08L35/06C08K13/04C08K7/06C08K3/04C08K3/08C08K5/134C08K5/526C08K5/20
CPCC08L63/00C08K2003/0806C08K2201/011C08L2201/08C08L2205/035C08L1/12C08L27/18C08L35/06C08K13/04C08K7/06C08K3/04C08K3/08C08K5/1345C08K5/526C08K5/20
Inventor 李锦兰
Owner 东莞市鼎耀实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com