Environment-friendly composite type electric wire and cable material

A wire and cable material and composite technology, applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve the problems of non-wear resistance, poor elasticity of wire and cable, and non-corrosion resistance, etc., to achieve perfect flame retardancy and good weather resistance Effect of performance, performance improvement

Inactive Publication Date: 2017-12-26
KUNSHAN XINZHICHENG ELECTRONICS TECH
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Purpose of the invention: The purpose of the invention is to solve the defects of poor elasticity, non-corrosion resistance, and non-wear resistance in the current wire and cable, and to provide an environmentally friendly composite wire and cable material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] An environmentally friendly composite wire and cable material, the wire and cable material includes the following weight components:

[0036] PP: 100 copies;

[0037] PET: 23-26 parts;

[0038] Impact modifier: 8 parts;

[0039] Polypropylene fiber: 11 parts;

[0040] EPDM rubber and ethylene-butylene elastomer mixture: 30 parts;

[0041] Plasticizer: 281 parts;

[0042] Stabilizer: 1.4 parts;

[0043] Lubricant: 8 parts;

[0044] Calcium carbonate: 7 parts;

[0045] Flame retardant: 8 parts;

[0046] Polyisobutenyl succinimide: 1.5 parts;

[0047] Titanium dioxide: 0.8 parts.

[0048] Preferably, the impact modifier is ACR resin.

[0049] Preferably, the plasticizer is epoxidized soybean oil, which has a better plasticizing effect and is more environmentally friendly and pollution-free.

[0050] Preferably, the stabilizer is isooctyl antimony trimercaptoacetate. As a stabilizer, isooctyl antimony trimercaptoacetate has excellent initial hue and hue retention...

Embodiment 2

[0055] PP: 100 copies;

[0056] PET: 24 parts;

[0057] Impact modifier: 10 parts;

[0058] Polypropylene fiber: 13 parts;

[0059] EPDM rubber and ethylene-butylene elastomer mixture: 33 parts;

[0060] Plasticizer: 20 parts;

[0061] Stabilizer: 1.8 parts;

[0062] Lubricant: 10 parts;

[0063] Calcium carbonate: 8 parts;

[0064] Flame retardant: 8 parts;

[0065] Polyisobutenyl succinimide: 2.1 parts;

[0066] Titanium dioxide: 0.8 parts.

[0067] Preferably, the impact modifier is ACR resin.

[0068] Preferably, the plasticizer is epoxidized soybean oil, which has a better plasticizing effect and is more environmentally friendly and pollution-free.

[0069] Preferably, the stabilizer is isooctyl antimony trimercaptoacetate. As a stabilizer, isooctyl antimony trimercaptoacetate has excellent initial hue and hue retention, excellent thermal stability, and is non-toxic, adapting to environmental protection in modern society. requirements.

[0070] Preferably, the l...

Embodiment 3

[0074] PP: 100 copies;

[0075] PET: 26 parts;

[0076] Impact modifier: 12 parts;

[0077] Polypropylene fiber: 15 parts;

[0078] EPDM rubber and ethylene-butylene elastomer mixture: 335 parts;

[0079] Plasticizer: 31 parts;

[0080] Stabilizer: 2 parts;

[0081] Lubricant: 12 parts;

[0082] Calcium carbonate: 9 parts;

[0083] Flame retardant: 8 parts;

[0084] Polyisobutenyl succinimide: 3 parts;

[0085] Titanium dioxide: 0.8 parts.

[0086] Preferably, the impact modifier is ACR resin.

[0087] Preferably, the plasticizer is epoxidized soybean oil, which has a better plasticizing effect and is more environmentally friendly and pollution-free.

[0088] Preferably, the stabilizer is isooctyl antimony trimercaptoacetate. As a stabilizer, isooctyl antimony trimercaptoacetate has excellent initial hue and hue retention, excellent thermal stability, and is non-toxic, adapting to environmental protection in modern society. requirements.

[0089] Preferably, the lu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly composite type electric wire and cable material comprising the following components by weight: 100 parts of PP, 23-26 parts of PET, 8-12 parts of an impact-resistant modifier, 11-15 parts of a polypropylene fiber, 30-35 parts of an ethylene-propylene-diene monomer and ethylene-butylene elastomer mixture, 28-31 parts of a plasticizer, 1.4-2 parts of a stabilizer, 8-12 parts of a lubricant, 7-9 parts of calcium carbonate, 8 parts of a flame retardant, 1.5-3 parts of polyisobutylene succinimide and 0.8 part of titanium dioxide. In the product, the materials from the used main ingredients of PP and PET to other auxiliary reagents are environment-friendly materials, so the final electric wire and cable material is superior in environment-friendly property.

Description

technical field [0001] The invention relates to an environment-friendly composite wire and cable material, which belongs to the wire and cable industry. Background technique [0002] Wire and cable is a wire product used to transmit electric (magnetic) energy, information and realize electromagnetic energy conversion. As the main carrier of power transmission, wire and cable are widely used in electrical equipment, lighting circuits, household appliances, etc. The quality of wire and cable directly affects the quality of the project and the safety of consumers' lives and property. Although the wire and cable industry is only a supporting industry, it accounts for 1 / 4 of the output value of China's electrical industry. It has a wide variety of products and a wide range of applications, involving industries such as electric power, construction, communications, and manufacturing, and is closely related to various sectors of the national economy. Wires and cables are also know...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L67/02C08L23/16C08L23/08C08L33/04C08L91/00C08L91/06C08K13/02C08K5/58C08K3/26C08K3/22H01B3/44
CPCC08L23/12C08K2003/2241C08K2003/265C08L2201/02C08L2201/08C08L2203/202C08L2205/025C08L2205/035C08L2205/16H01B3/441C08L67/02C08L23/16C08L23/0815C08L33/04C08L91/00C08L91/06C08K13/02C08K5/58C08K3/26C08K3/22
Inventor 林珑
Owner KUNSHAN XINZHICHENG ELECTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com