A kind of transparent breathable fish tank and preparation method thereof

A transparent, fish tank technology, applied in the field of breeding vessels, can solve the problems of fish tank ornamental and ventilation effects not reaching the technical effect, messy, not continuous, etc., to achieve the effect of improving mechanical strength, good ventilation effect, and improving heat resistance

Inactive Publication Date: 2020-12-22
嘉兴市诚峰金属制品股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Tracing it to its cause, this invention ignores that the fish tank body has a certain thickness, and the aggregates are covered by epoxy resin. Although gaps can be formed between the aggregates, they are not continuous through channels. It is difficult to enter the inside of the fish tank from the outside of the tank through the pores, and the material of the copied fish tank is opaque, so the actual ornamental and air-permeable effects of the fish tank of the invention have not reached the technical effect described in the invention

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of transparent breathable fish tank and preparation method thereof
  • A kind of transparent breathable fish tank and preparation method thereof
  • A kind of transparent breathable fish tank and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] (1) Weighing by weight percentage: 77% of thermoplastic resin particles, 20% of hydrophobic materials, and 3% of metal nanowires.

[0048] (2) After drying, the thermoplastic resin particles are evenly mixed with hydrophobic materials and metal nanowires, and then poured into the barrel of an injection molding machine for injection molding at a set temperature and pressure.

[0049] (3) Carry out laser cutting of the block finished product formed in step (2) vertically to the thickness direction of the block product in space to obtain a plate of the required size with uniform thickness, and soak the plate in 4mol / L dilute nitric acid for 10 hours, After taking it out, rinse it repeatedly with clean water 2-3 times to remove residual dilute nitric acid.

[0050] (4) Splice and assemble the plates in step (3) to obtain the required fish tank, and carry out the air permeability test on the fish tank: take three commercially available common fish tanks with the same size an...

Embodiment 2

[0054] (1) Weighing by weight percentage: 81% of thermoplastic resin particles, 15% of hydrophobic materials, and 4% of metal nanowires.

[0055] (2) After drying, the thermoplastic resin particles are evenly mixed with hydrophobic materials and metal nanowires, and then poured into the barrel of an injection molding machine for injection molding at a set temperature and pressure.

[0056] (3) Carry out laser cutting of the block finished product formed in step (2) along the space perpendicular to the thickness direction of the block product to obtain a plate of the required size with uniform thickness, and soak the plate in 5mol / L dilute nitric acid for 8 hours, After taking it out, rinse it repeatedly with clean water 2-3 times to remove residual dilute nitric acid.

[0057] (4) Splice and assemble the plates in step (3) to obtain the required fish tank, and carry out the air permeability test on the fish tank: take three commercially available common fish tanks with the sam...

Embodiment 3

[0061] (1) Weighing by weight percentage: 85% of thermoplastic resin particles, 10% of hydrophobic materials, and 5% of metal nanowires.

[0062] (2) After drying, the thermoplastic resin particles are evenly mixed with hydrophobic materials and metal nanowires, and then poured into the barrel of an injection molding machine for injection molding at a set temperature and pressure.

[0063] (3) Carry out laser cutting of the block-shaped finished product formed in step (2) along the space perpendicular to the thickness direction of the block-shaped finished product to obtain a plate of the required size with uniform thickness, and soak the plate in 6mol / L dilute nitric acid for 6 hours, After taking it out, rinse it repeatedly with clean water 2-3 times to remove residual dilute nitric acid.

[0064] (4) Splice and assemble the plates in step (3) to obtain the required fish tank, and carry out the air permeability test on the fish tank: take three commercially available common ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a transparent and breathable fish tank. The fish tank is assembled by splicing transparent and breathable macromolecular panels. The top of the fish tank is opened, other parts, at least the ornamental side, of the tank body is made from the transparent and breathable macromolecular panels, the transparent and breathable macromolecular panels are provided with continuous cut-through pore ways in the thickness direction, and the continuous cut-through pore ways extend linearly and have the diameters of 0.6 micrometers or below. According to the comparison of the transparent and breathable fish tank and a common fish tank, an oxygenation pump is reduced, the production and operation cost of the fish tank is lowered, and the wholeness and the ornamental value of the fish tank are improved.

Description

technical field [0001] The invention belongs to the field of culture vessels, and in particular relates to a transparent and air-permeable fish tank and a preparation method thereof. Background technique [0002] With the increase of people's income, the pursuit of a comfortable life has become a new trend. As a kind of container for ornamental use and special breeding of aquatic animals and plants, fish tank is also increasingly popular and enters the homes of ordinary people. At present, there are various types of fish tanks such as plastic, glass, and ceramics for consumers to choose from on the market, but most of these traditional fish tanks need oxygen pumps to inflate and increase oxygen in the fish tanks, which increases the complexity of fish tank installation and production and operating costs. In the event of a power outage or forgetting to charge, the fish in the fish tank will struggle to survive due to lack of oxygen. For example, patent CN205455391U disclose...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A01K63/00C08L33/12C08L25/06C08L69/00C08L55/02C08L67/02C08L27/06C08L83/16C08L27/18C08L83/04C08L91/00C08K5/5419C08L51/00C08K3/34C08J9/26B29C45/00
CPCA01K63/003B29C45/0013B29C71/0009C08J9/26C08J2201/0442C08J2325/06C08J2333/12C08J2369/00C08K3/34C08L25/06C08L27/06C08L33/12C08L51/003C08L55/02C08L67/02C08L69/00C08L2201/08C08L2201/10C08L2203/14C08L83/16C08L27/18C08L83/04C08L91/00C08K5/5419
Inventor 高云
Owner 嘉兴市诚峰金属制品股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com