A kind of hydrogel seaweed fiber and preparation method thereof

A technology of hydrogel seaweed and seaweed fiber, which is applied in the fields of fiber chemical characteristics, wet spinning method, pharmaceutical formula, etc. It can solve the problems of poor application of wound cleaning and care, low fiber strength, and long gelation time, etc. problem, achieve the effect of inhibiting Staphylococcus aureus, improving three-dimensional porous structure, improving wet strength and flexibility

Active Publication Date: 2019-11-12
青岛海赛尔酌澳生物科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing seaweed fiber still has the following problems: the gelation time is long, it cannot be well applied to wound cleaning and nursing of acute massive bleeding or exudate, the fiber strength is not high, and the spinnability is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A preparation method of hydrogel seaweed fiber, comprising the following steps:

[0033](1) Clean the kelp salvaged in seawater with clear water, dry it in an oven at a constant temperature of 60°C until the weight percentage of water is 18%, take it out and pulverize it and pass through a 50-mesh sieve to obtain kelp powder; weigh 30g of kelp powder, put the weighed kelp into a beaker, add 1L of 3% sodium hydroxide solution to the beaker, soak for 6h, filter, remove the filtrate, and add 200mL of purified water to the beaker containing the soaked kelp , put the beaker in a water-bath shaking pot at 70°C for 60 minutes, take it out and cool it to room temperature, and then store the beaker in a refrigerator at 4°C for 10 hours; take the beaker out of the refrigerator, and adjust the pH with 5% hydrochloric acid to 4.2, then transfer the beaker to an ultrasonic oscillator, use 180W power, sonicate for 50 minutes, centrifuge, and collect the supernatant; add a mass fracti...

Embodiment 2

[0041] A preparation method of hydrogel seaweed fiber, comprising the following steps:

[0042] (1) Clean the kelp salvaged in seawater with clear water, dry it in an oven at a constant temperature of 60°C until the weight percentage of water is 15%, take it out and pulverize it and pass through a 50-mesh sieve to obtain kelp powder; weigh 35g of kelp powder, put the weighed kelp into a beaker, add 1L of 5% sodium hydroxide solution to the beaker, soak for 8 hours, filter, remove the filtrate, and add 250mL of purified water to the beaker containing the soaked kelp , put the beaker in a water-bath shaking pot at 80°C for 50 minutes, take it out and cool it to room temperature, then store the beaker in a refrigerator at 4°C for 8 hours; take the beaker out of the refrigerator, and adjust the pH with 4% hydrochloric acid to 4.4, then transfer the beaker to an ultrasonic oscillator, use 220W power, sonicate for 50 minutes, centrifuge, and collect the supernatant; add a mass fract...

Embodiment 3

[0050] A preparation method of hydrogel seaweed fiber, comprising the following steps:

[0051] (1) Clean the kelp salvaged in seawater with clear water, dry it in an oven at a constant temperature of 60°C until the weight percentage of water is 20%, take it out and pulverize it and pass through a 50-mesh sieve to get kelp powder; weigh 40g of kelp powder, put the weighed kelp into a beaker, add 1L of 4% sodium hydroxide solution to the beaker, soak for 8 hours, filter, remove the filtrate, and add 300mL of purified water to the beaker containing the soaked kelp , put the beaker in a water-bath shaking pot at 70°C for 60 minutes, take it out and cool it to room temperature, then store the beaker in a refrigerator at 4°C for 12 hours; take the beaker out of the refrigerator, and adjust the pH with 3% hydrochloric acid to 4.4, then transfer the beaker to an ultrasonic oscillator, use 200W power, sonicate for 60 minutes, centrifuge, and collect the supernatant; add a mass fractio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of functional renovation of alginate fibers, in particular to an aquagel alginate fiber and a preparation method for the same. The preparation method for the aquagel alginate fiber comprises the following steps: (1) extracting a sodium alginate raw material from algae; (2) preparing an 8 to 10 mass percent aqueous solution of the alginate, and performing defoaming to obtain an alginate spinning solution; (3) preparing a mixed solution of an aqueous solution of soluble starch and the alginate spinning solution; (4) enabling the mixed solution obtained in step (3) to pass through a metering pump, and extruding the mixed solution into a first coagulating bath from a spinneret plate; (5) introducing as-spun fibers into a second coagulating bath; (6) introducing the fibers into a third coagulating bath, performing drawing forming, squeezing water out, and performing washing and drying to a constant weight, so as to obtain the aquagel alginate fibers. According to the aquagel alginate fiber and the preparation method, a preparation process is improved to improve the strength and the spinnability of the alginate fibers and shorten the gelation time, and the prepared aquagel alginate fiber can be used for preparing medical sanitary dressings and skin-care facial masks.

Description

technical field [0001] The invention relates to the technical field of functional transformation of seaweed fibers, in particular to a hydrogel seaweed fiber, and also to a preparation method of the hydrogel seaweed fiber. Background technique [0002] There are many kinds of seaweed. Alginic acid is the main component of alginate, which exists in the stems and leaves of seaweed (about 10-20% of which is crude protein, crude fat, crude cellulose, water and impurities, etc.). Seaweed fiber is a new type of high-performance fiber obtained by wet spinning production process using polysaccharide extracted from natural seaweed as raw material, water-soluble metal salt solution as coagulation bath, and can be used as green fiber. [0003] Seaweed fiber products have good health care and medical functions. Through the exchange of calcium ions and human sodium ions, it can promote the wound to produce sodium alginate and calcium alginate gel. This gel is hydrophilic and can inhibit ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/18D01F11/00A61L26/00A61K8/73A61Q19/00D01D5/06
CPCA61K8/733A61L26/0023A61L26/0061A61L26/008A61L26/0085A61Q19/00D01D5/06D01F8/18D01F11/00C08L5/04
Inventor 郝继海
Owner 青岛海赛尔酌澳生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products