UV (ultraviolet) single-side adhesive tape with adhesive failure after ultraviolet irradiation and preparation method of adhesive tape

A post-irradiation, ultraviolet technology, applied in the direction of adhesives, film/sheet adhesives, etc., can solve the problems of insufficient adhesive force of the tape, poor adhesion loss effect, etc., and achieve good adhesion effect, high adhesion, no The effect of residual glue

Inactive Publication Date: 2017-12-01
东莞市古川胶带有限公司
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of this, the present invention aims at the deficiencies in the prior art, and its main purpose is to provide a UV single-sided adhesive tape that loses its adhesion after ultraviolet irradiation and its preparation method, which can effectively solve the problems of insufficient adhesion and loss of adhesive force of the existing adhesive tape. The problem of poor stickiness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • UV (ultraviolet) single-side adhesive tape with adhesive failure after ultraviolet irradiation and preparation method of adhesive tape
  • UV (ultraviolet) single-side adhesive tape with adhesive failure after ultraviolet irradiation and preparation method of adhesive tape

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0020] The present invention also discloses a preparation method of UV single-sided adhesive tape that loses tack after being irradiated by ultraviolet rays, comprising the following steps:

[0021] (1) Take UV adhesive, curing additive, ethyl ester solution and toluene solution, prepare and stir the ethyl ester solution, toluene solution, UV adhesive and curing additive to form glue, and strictly prohibit sunlight exposure during glue mixing and production process;

[0022] (2) Coat the above-mentioned prepared glue on the transparent base film by direct coating, bake at 85°C-95°C for 2-4 minutes for curing treatment, and then cover the single-sided release film and send it to 45°C- 55 ℃ warm room for 23H-25H curing treatment.

Embodiment 1

[0025] One includes a transparent base film 10 , a UV adhesive layer 20 and a single-side release film 30 . The UV adhesive layer 20 is coated on the surface of the transparent base film 10, and the single-sided release film 30 is coated on the surface of the UV adhesive layer 20; and, the UV adhesive layer 20 includes the following weight percentage components : UV adhesive 38%, curing additive 2%, ethyl ester 20% and toluene 40%. The transparent base film 10 is made of PET, and the thickness of the UV adhesive layer 20 is 8 μm.

[0026] A kind of preparation method of the UV one-sided adhesive tape that loses tack after ultraviolet irradiation comprises the following steps:

[0027] (1) Take UV adhesive, curing additive, ethyl ester solution and toluene solution, prepare and stir the ethyl ester solution, toluene solution, UV adhesive and curing additive to form glue, and strictly prohibit sunlight exposure during the glue mixing and production process.

[0028] (2) Apply ...

Embodiment 2

[0030] One includes a transparent base film 10 , a UV adhesive layer 20 and a single-side release film 30 . The UV adhesive layer 20 is coated on the surface of the transparent base film 10, and the single-sided release film 30 is coated on the surface of the UV adhesive layer 20; and, the UV adhesive layer 20 includes the following weight percentage components : UV adhesive 40%, curing additive 2.5%, ethyl ester 19.5% and toluene 38%. The transparent base film 10 is made of PET, and the thickness of the UV adhesive layer 20 is 5 μm.

[0031] A kind of preparation method of the UV one-sided adhesive tape that loses tack after ultraviolet irradiation comprises the following steps:

[0032] (1) Take UV adhesive, curing additive, ethyl ester solution and toluene solution, prepare and stir the ethyl ester solution, toluene solution, UV adhesive and curing additive to form glue, and strictly prohibit sunlight exposure during the glue mixing and production process.

[0033] (2) Ap...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a UV (ultraviolet) single-side adhesive tape with adhesive failure after ultraviolet irradiation and a preparation method of the adhesive tape. The UV single-side adhesive tape comprises a transparent base film, a UV adhesive layer and a single-side release film, wherein the UV adhesive layer coats the surface of the transparent base film, the single-side release film covers the surface of the UV adhesive layer, and the UV adhesive layer comprises, in weight percentage, 38%-80% of UV adhesives, 0.5%-2.5% of curing additives, 9%-20% of ethyl ester and 10%-40% of methylbenzene. The UV adhesive layer is prepared by a specific formula, so that the UV single-side adhesive tape has high adhesive force, wafers cannot fly apart in cutting, grinding and the like, workpieces can be effectively protected, after UV irradiation, adhesive failure is rapid, adhesive failure effects are good, adhesive residues are omitted, and machining production operation is facilitated.

Description

technical field [0001] The invention relates to the technology in the field of adhesive tapes, in particular to a UV single-sided adhesive tape that loses adhesion after being irradiated by ultraviolet rays and a preparation method thereof. Background technique [0002] In the process of wafer grinding, dicing, various silicon wafers, packaging substrates, ceramics, glass, crystal fine electronic parts, and processing and cutting of small parts of various materials, tapes are often used for protection. In the prior art, the adhesive tape used for processing protection generally has the problems of insufficient adhesion and poor adhesion loss effect, so that it cannot protect the workpiece well, and after the workpiece is processed, the tape is difficult to peel off from the workpiece. It is easy to leave residual glue after peeling off, which brings inconvenience to processing and production operations. Contents of the invention [0003] In view of this, the present inven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/02
CPCC09J2301/122C09J2301/312C09J2467/006
Inventor 王建义徐宏飞王博文黄世锋付江勇杨春吉周雄安吴荣斌罗通化罗焕
Owner 东莞市古川胶带有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com