Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of Taishan jade surface treatment process

A surface treatment and process technology, applied in the field of Taishan jade surface treatment technology, can solve the problems of multiple cracks and multiple ribs, unsightly display, no aesthetics, etc., to achieve the effect of bright color contrast, increased product aesthetics, and guaranteed product quality.

Active Publication Date: 2020-06-30
师秀娜
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Based on the excellent quality and rich cultural connotation of Taishan jade, it is processed into various craft ornaments, which are favored by collectors. However, Taishan jade products and rough stones are cracked and ribbed, and the display is very ugly, and the yield rate is low. No aesthetics, which has brought a relatively negative impact on the promotion of Taishan jade products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of surface treatment process of Mount Tai jade rough stone is processed according to the following steps successively,

[0026] Fissure filling: First, wash with strong acid to remove impurities, and then use filling glue to fill the gaps on the surface of Taishan jade or product surface;

[0027] Surface polishing and cleaning: use 120-mesh and 800-mesh sandpaper to smooth and polish the surface of the original Taishan jade after glue filling, and clean it;

[0028] Spray paint: Spray black blending paint on the surface of the original Taishan jade stone, then put the painted Taishan jade original stone into the oven, and dry it at 70°C;

[0029] Applique: Make low-temperature real gold decal paper into a patch with a specific pattern shape, paste the patch on the surface of the original Taishan jade through the applique process, and place the original Taishan jade after the patch is placed in an oven to dry;

[0030] Remove the film and clean: remove the outer...

Embodiment 2

[0035] A kind of surface treatment process of Mount Tai jade rough stone is processed according to the following steps successively,

[0036] Fissure filling: First, wash with strong acid to remove impurities, and then use filling glue to fill the gaps on the surface of Taishan jade or product surface;

[0037] Surface polishing and cleaning: use 120-mesh and 800-mesh sandpaper to smooth and polish the surface of the original Taishan jade after glue filling, and clean it;

[0038] Spray paint: Spray black blending paint on the surface of the original Taishan jade stone, then put the painted Taishan jade original stone into the oven, and dry it at 70°C;

[0039] Applique: Make low-temperature real gold decal paper into a patch with a specific pattern shape, paste the patch on the surface of the original Taishan jade through the applique process, and place the original Taishan jade after the patch is placed in an oven to dry;

[0040] Remove the film and clean: remove the outer...

Embodiment 3

[0045] A kind of surface treatment process of Mount Tai jade product, according to the following steps successively,

[0046] Fissure filling: First, wash with strong acid to remove impurities, and then fill the Taishan jade product or the gap on the surface of the product with filling glue;

[0047] Surface polishing and cleaning: use 120-mesh and 800-mesh sandpaper to smooth and polish the surface of the Taishan jade product after glue filling, and clean it;

[0048]Spray paint: spray black blending paint on the surface of Taishan jade products, then put the painted Taishan jade products into the oven, and dry them at 70°C;

[0049] Applique: Make low-temperature real gold decal paper into a patch with a specific pattern shape, paste the patch on the surface of the original Taishan jade through the applique process, and place the original Taishan jade after the patch is placed in an oven to dry;

[0050] Remove the film and clean: remove the outer film of the patch, and wip...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of jade artware processing and particularly relates to a surface treatment process for Taishan jade. The surface treatment process comprises the following steps: crack filling, surface polishing and cleaning, paint spraying, carrying out applique, film uncovering and cleaning and glazing, wherein a treated raw material is raw Taishan jade or a product. By using the process disclosed by the invention, flaws on the jade can be covered, so that the aesthetic degree of the product is improved; gold is matched with jade, and gold is matched with black, so that the color contrast is sharp; the yield of the Taishan jade is greatly increased; and the surface treatment process has important significance for the inheritance and popularization of the Taishan jade culture.

Description

technical field [0001] The invention belongs to the field of processing jade handicrafts, and in particular relates to a surface treatment process for Mount Tai jade. Background technique [0002] Taishan jade (English name taishan jade) is produced at the foot of Mount Tai in Tai'an City, Shandong Province, and is mainly distributed in Shila Village and Jieshou Village. Taishan jade was formed in the Xidian sub-unit of the Nanluopo superunit in the Fuping period of the Archean Neoarchean. The lithology is variable pyroxene peridotite, and the formation time is 2.536 billion years ago. The formation process is that deep-source magma intrudes along the structure, and magnesium-rich ultrabasic rocks are metamorphosed by high-temperature gas-liquid, which belongs to metamorphic ultrabasic magma deposits. [0003] Before the Qin and Han Dynasties, Taishan jade was already famous in China. According to the "Shan Hai Jing": "There are many jades on Mount Tai, surrounded by water,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B44C5/06
CPCB44C5/06
Inventor 师秀娜
Owner 师秀娜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com