Full-penetration micro-powder polishing tile and preparation method thereof

A micropowder and ceramic tile technology, applied in the field of building decoration materials, can solve the problems of not too good simulation effect, impermeability, poor gloss, unobvious surface layer, etc., and achieve good stone imitation effect, good gloss and high strength Effect

Inactive Publication Date: 2017-11-07
HEFEI XINYADA INTELLIGENT TECH CO LTD
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, at present, the polished tiles are mainly polished after being clothed by traditional cloth distribution equipment. The formula process is relatively simple. , poor gloss

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A fully transparent micropowder polished tile, made of the following raw materials in parts by weight: 50 parts of low-temperature feldspar, 35 parts of expanded perlite, 20 parts of calcined kaolin, 7 parts of soft soil, 5 parts of water-ground potassium feldspar powder, 11 parts of borax, 7 parts of porcelain sand, 4 parts of silica, 3 parts of washed albite, 10 parts of selected sand and 55 parts of water.

[0032] Wherein, the silicon dioxide content in the selected sand is not less than 95%.

[0033] A method for preparing fully transparent micropowder polished ceramic tiles, comprising the following steps:

[0034] (1) Ball mill: Weigh low-temperature feldspar, expanded perlite, calcined kaolin, soft soil, water-milled potassium feldspar powder, borax, porcelain sand, silica, washed albite, and selected sand, respectively, in parts by weight, and add them to the ball mill Add water and ball mill evenly to obtain mud;

[0035] (2) Iron removal and staleness: put ...

Embodiment 2

[0047] A fully transparent micropowder polished tile, made of the following raw materials in parts by weight: 45 parts of low-temperature feldspar, 30 parts of expanded perlite, 15 parts of calcined kaolin, 5 parts of soft soil, 2 parts of water-ground potassium feldspar powder, 8 parts of borax, 5 parts of porcelain sand, 2 parts of silica, 1 part of washed albite, 5 parts of selected sand and 50 parts of water.

[0048] Wherein, the silicon dioxide content in the selected sand is not less than 95%.

[0049] A method for preparing fully transparent micropowder polished ceramic tiles, comprising the following steps:

[0050] (1) Ball mill: Weigh low-temperature feldspar, expanded perlite, calcined kaolin, soft soil, water-milled potassium feldspar powder, borax, porcelain sand, silica, washed albite, and selected sand, respectively, in parts by weight, and add them to the ball mill Add water and ball mill evenly to obtain mud;

[0051] (2) Iron removal and staleness: put the...

Embodiment 3

[0063] A fully transparent micropowder polished ceramic tile, made of the following raw materials in parts by weight: 55 parts of low-temperature feldspar, 40 parts of expanded perlite, 25 parts of calcined kaolin, 10 parts of soft soil, 8 parts of water-ground potassium feldspar powder, 15 parts of borax, 10 parts of porcelain sand, 6 parts of silica, 5 parts of washed albite, 15 parts of selected sand and 60 parts of water.

[0064] Wherein, the silicon dioxide content in the selected sand is not less than 95%.

[0065] A method for preparing fully transparent micropowder polished ceramic tiles, comprising the following steps:

[0066] (1) Ball mill: Weigh low-temperature feldspar, expanded perlite, calcined kaolin, soft soil, water-milled potassium feldspar powder, borax, porcelain sand, silica, washed albite, and selected sand, respectively, in parts by weight, and add them to the ball mill Add water and ball mill evenly to obtain mud;

[0067] (2) Iron removal and stale...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fully transparent micropowder polished ceramic tile and a preparation method thereof, which is made of the following raw materials in parts by weight: 45-55 parts of low-temperature feldspar, 30-40 parts of expanded perlite, 15-25 parts of calcined kaolin, soft soil 5‑10 parts, water ground potassium feldspar powder 2‑8 parts, borax 8‑15 parts, porcelain sand 5‑10 parts, silica 2‑6 parts, washed albite 1‑5 parts, selected sand 5‑15 parts and 50‑60 parts of water. Its preparation method: (1) ball milling; (2) removing stale iron; (3) milling; (4) pressing; (5) firing; (6) polishing. The invention solves the poor surface level, three-dimensionality and blurred stone-like effect of traditional polished tiles, and develops the application of super-transparent materials, so that the stone-like effect is more realistic, and at the same time, it has better permeability resistance and gloss.

Description

technical field [0001] The invention relates to the technical field of building decoration materials, in particular to a fully transparent micropowder polished ceramic tile and a preparation method thereof. Background technique [0002] Polished brick is a kind of whole body brick. It is a kind of bright brick made by grinding the surface of the whole body brick body. It is a new decorative ceramic material that is very popular at home and abroad in recent years. The whole body brick is much smoother. [0003] Compared with natural stone, polished tiles have no radioactive elements. Natural stone is mineral and has not been sintered at high temperature, so it contains individual trace radioactive elements. Long-term exposure will be harmful to human body; polished tiles are harmless to human body; The color difference between different shades is large, the polished tiles are carefully prepared, the design and color of the same batch of products are consistent, and there is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/18C04B35/622
CPCC04B35/18C04B35/622C04B2235/3201C04B2235/3409C04B2235/3418C04B2235/3463C04B2235/3472C04B2235/349C04B2235/6562C04B2235/6567C04B2235/96
Inventor 张玉
Owner HEFEI XINYADA INTELLIGENT TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap