High-antistatic dope and preparation method thereof

An electrostatic and high-performance technology, which is applied in the field of high antistatic performance coatings and its preparation, can solve problems such as partial discharge and poor conductivity, and achieve the effects of increasing durability, improving adhesion performance, and improving uniform stability

Active Publication Date: 2017-09-22
GUANGDONG MIDEA KITCHEN APPLIANCES MFG CO LTD +1
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In view of the problems existing in the prior art, the present invention provides a coating with high antistatic performance and its preparation method, which solves the partial discharge and dust viscosity caused by the poor conductivity of the base material, improves the user experience, reduces the difficulty of cleaning, etc. advantage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-antistatic dope and preparation method thereof
  • High-antistatic dope and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0062] The preparation method of the above-mentioned high antistatic performance coating includes the following steps: mixing the components together according to the above-mentioned proportion.

[0063] When the auxiliary agent includes an adhesion promoter, a wetting and dispersing agent and a defoamer, the preparation method of the high antistatic performance coating can specifically adopt the following steps to prepare:

[0064] (1) Preparation of wet dispersion system:

[0065] Mix the wetting and dispersing agent with the solvent in proportion to obtain a wetting and dispersing system;

[0066] (2) Preparation of conductive system:

[0067] Add conductive filler in proportion to the wetting dispersion system obtained in step (1), and mix to obtain a conductive system;

[0068] (3) Preparation of high antistatic performance coatings:

[0069] Add defoamer and nano-sol in proportion to the conductive system obtained in step (2), mix, then add conductive additive and adh...

Embodiment 1

[0082] The high antistatic performance paint consists of the following components by weight: multilayer graphene conductive filler is 1.8 kg, Hostastat HS1 conductive additive is 1.5 kg, SiO 2 / TiO 2 Nano-sol is 45 kg, solvent (i.e. isopropanol) is 50.7 kg, DOW CORNING 2-6040 adhesion promoter is 0.3 kg, Efka-701 wetting and dispersing agent is 0.4 kg, 082 defoamer is 0.3 kg.

[0083] The preparation method of this high antistatic performance coating is as follows:

[0084] (1) Preparation of wet dispersion system:

[0085] At room temperature, add 0.4 kg of Efka-701 wetting and dispersing agent and 50.7 kg of isopropanol solvent into the reactor, stir at a low speed of 100 r / min to dissolve the two, and obtain a wetting and dispersing system;

[0086] (2) Preparation of conductive system:

[0087] At room temperature, add 1.8 kilograms of multilayer graphene conductive fillers to the wet dispersion system obtained in step (1), and stir at 1200r / min for 10min to obtain a co...

Embodiment 2

[0091] The high antistatic performance coating includes the following components by weight: 0.3 kg for monolayer graphene conductive filler, 1.5 kg for Hostastat HS1 conductive additive, SiO 2 / TiO 2 Nano sol is 45 kg, solvent (isopropanol) is 52.2 kg, DOW CORNING 2-6040 adhesion promoter is 0.3 kg, Efka-701 wetting and dispersing agent is 0.4 kg, 082 defoamer is 0.3 kg.

[0092] The preparation method of this high antistatic performance coating is as follows:

[0093] (1) Preparation of wet dispersion system:

[0094] At room temperature, add 0.4 kg of Efka-701 wetting and dispersing agent and 52.2 kg of isopropanol solvent into the reactor, stir at a low speed of 100 r / min to dissolve the two, and obtain a wetting and dispersing system;

[0095] (2) Preparation of conductive system:

[0096] At room temperature, add 0.3 kg of single-layer graphene conductive filler to the wet dispersion system obtained in step (1), and stir at 1000r / min for 10min to obtain a conductive sys...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
electrical resistivityaaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-antistatic dope and a preparation method thereof. The high-antistatic dope is prepared from the following components in parts by weight: 0.3 to 1.8 parts of conductive filler, 0.5 to 1.5 parts of conductive improver, 25.7 to 80 parts of nanometer sol, 16.6 to 70 pats of solvent and 0.5 to 1 part of auxiliary agent. During preparation, the components are mixed together according to proportions to prepare the high-antistatic dope. The high-antistatic dope and the preparation method thereof provided by the invention solve the problems of local discharging and dust viscosity caused by poor conductivity of base materials and have the advantages that using experiences of users are improved and cleaning difficulty is reduced and the like.

Description

technical field [0001] The invention belongs to the technical field of coatings, in particular to a coating with high antistatic performance and a preparation method thereof. Background technique [0002] In 2000, Professor Shirakawa of Japan and Professor MacDiarmid of the United States discovered that polyacetylene has high conductivity, which broke people's traditional thinking, that is, the concept that high molecular polymers are insulating, and made conductive polymers become the focus of many scientific research work. The focus of the researchers' research has aroused extensive attention. Conductive polymers are formed by chemical or electrochemical doping of polymers with conjugated π bonds, and a class of polymer materials whose conductivity extends from insulators to conductors. [0003] Traditional plastic parts are insulating materials, and home appliances are mostly made of plastic materials. Plastic materials have always been the main raw materials used in ho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/24C09D7/12
CPCC09D1/00C09D5/24
Inventor 赵莉
Owner GUANGDONG MIDEA KITCHEN APPLIANCES MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com