Orthoformic acid organic amine salt compound and application thereof as foaming agent

An organic amine salt and compound technology, which is applied in the field of orthoformic acid organic amine salt compound and its use as a foaming agent, can solve the problem of uneven cell size, uneven cell distribution, affecting the strength performance and thermal insulation of foamed materials nature, etc.

Active Publication Date: 2017-08-25
新泰补天新材料技术有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In short, the foaming agent in the prior art cannot be dispersed into the foaming composition at the molecular level, resulting in uneven distribution of cells and uneven cell size, which ultimately affects the strength performance and thermal insulation of the foamed material nature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Orthoformic acid organic amine salt compound and application thereof as foaming agent
  • Orthoformic acid organic amine salt compound and application thereof as foaming agent
  • Orthoformic acid organic amine salt compound and application thereof as foaming agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment A-1

[0175] The water of 1.4 tons of ammonium carbamate (molecular weight 78.07), 0.7 tons of ethylene glycol, and 0.9 tons is joined in the stainless steel autoclave with cooling water jacket (abbreviated as reactor in other embodiments below), Start the stirrer to slowly dissolve the ammonium carbamate (not necessarily completely dissolved), purge the reactor with nitrogen, then close the reactor and start stirring, and feed a total of 1.7 tons of propylene oxide (molecular weight 58.08, boiling point 34 ° C) , control the feeding speed of propylene oxide so that the pressure in the reactor is not higher than 0.6MPa, slowly raise the temperature under constant stirring, control the temperature below 70°C for 15 hours, the reaction is completed, and slowly lower the temperature to 50°C Control the degree of vacuum below 600 mm Hg (preferably below 500 mmHg) to slowly remove unnecessary water (for example, reaching a water content lower than 20 wt%), then release the vacuum, and rel...

Embodiment A-2

[0180] Add 1.4 tons of ammonium carbamate, 0.7 tons of ethylene glycol, and 0.9 tons of water into a stainless steel reactor with a cooling jacket, start stirring, so that the ammonium carbamate is slowly dissolved (not necessarily completely dissolved), and the reaction After the system is treated and protected with nitrogen, it is heated up, the temperature is controlled at 45-70°C, and the pressure is controlled not to exceed 0.6MPa. Then, a total of 1.3 tons of ethylene oxide (molecular weight 44.05) is slowly added in batches, and the control is performed after the addition is completed. The temperature is 45-70°C, the pressure is below 0.6MPa and the reaction is stirred for 5 hours, then the temperature is lowered to 50°C, and unnecessary water is removed under reduced pressure at 600mHg (for example, to achieve a water content lower than 30wt%), and the temperature is lowered to below 40°C After the product is released, compound A-2 is obtained. The viscosity is about 2...

Embodiment A-3

[0181] Embodiment A-3 (the present invention is preferred)

[0182] The ammonium carbamate of 1kg, the water of 1kg are joined in the reactor, dissolve under agitation (allow the ammonium carbamate that does not dissolve), then add the propylene oxide of 2kg in the transparent quartz glass reactor, start stirring, Slowly raise the temperature under constant stirring, control the temperature between 50-60°C, and carry out the reaction under the condition that the pressure is not higher than 0.6MPa. When the reaction lasts for about 2 hours, a wonderful phenomenon suddenly appears: the turbid, opaque mixture instantly Turn into a transparent or clear solution, continue to react for 8 hours, then lower the temperature to 50°C, remove unnecessary water under a vacuum of 600 mm Hg, and release the product after cooling down to below 40°C. The reaction time ensures that the reaction is complete according to the molar ratio. Compound A-3 was obtained. The viscosity is 200 centipois...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Decomposition temperatureaaaaaaaaaa
Viscosityaaaaaaaaaa
Decomposition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses an orthoformic acid organic amine salt compound A<n->[B<m+>]p with the following general formula (I). In the formula (I), A<n-> is an orthoformic radical, B<m+> is or includes an ammonium ion and / or an organic amine B positive ion, m is 1-10, p is larger than 0 and smaller than or equal to n / m. The compound with the general formula (I) has at least one hydroxyalkyl group connected with an N atom, that is, the compound has alcohol amine residue. The compound can be used as a polyurethane foaming agent or a polystyrene foaming agent or a polyvinyl chloride foaming agent.

Description

technical field [0001] The present invention relates to having as CO 2 Anionic organoammonium compounds of the donor and their use as blowing agents, more specifically, providing not only 2 The anion of the donor and has a hydroxyalkyl or hydroxyalkylalkoxy group as a solubilizing group or a C2-C14 hydrocarbon group (such as 2-chloroethyl, 3-chloropropyl or phenethyl) as a solubilizing group A new type of organic ammonium salt compound, and its application in foam materials such as polyurethane foam or PVC foam or polystyrene foam. [0002] technical background [0003] As a new polymer material, polyurethane rigid foam is light in weight, high in strength and has extremely low thermal conductivity. Automobiles, refrigerators and freezers and other household appliances and other industries. The most important raw material in the production of rigid polyurethane foam is the blowing agent. At present, these blowing agents are chlorofluorocarbons except cyclopentane. Because...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C07C213/08C07C215/08C07C215/12C07C41/60C07C43/32C08G65/28C08G65/06C08G65/24C08G65/08C08G65/26C08J9/08C08L75/04C08L25/06C08L27/06
CPCC07C41/60C07C213/08C08G65/06C08G65/08C08G65/2609C08G65/2624C08J9/08C08J2203/02C08J2203/184C08J2205/052C08J2325/06C08J2327/06C08J2375/04C07C215/08C07C215/12C07C43/32
Inventor 毕戈华毕玉遂陈唐建翟志强
Owner 新泰补天新材料技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com