Low-density high-temperature-resistant tray and preparation method thereof

A low-density, high-temperature-resistant technology, applied in the field of storage, can solve the problems of high temperature resistance, easy wear and tear of pallets, easy damage, etc., and achieve the effects of good adhesion, convenient operation and simple steps.

Inactive Publication Date: 2017-08-15
SUZHOU KESHENG STORAGE & LOGISTICS EQUIP
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Pallets are accessories in great demand in the warehousing and logistics industry. The storage environment is extremely complex and there are many goods. The pallets in the prior art have the disadvantages of easy wear, damage and high temperature resistance, which reduces work efficiency. To improve work efficiency and the safety of the work environment, the present invention proposes a low-density high-temperature-resistant tray and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] This embodiment provides a low-density, high-temperature-resistant tray, including a tray, and a layer of low-density, high-temperature-resistant layer is coated on the outside of the tray. The low-density, high-temperature-resistant layer is composed of A, B, and C. The ratio is compounded, and A, B, C contain the following components in parts by mass:

[0027] Component A includes the following components in parts by mass: propylene carbonate: 5 parts, 3-butanediol: 7 parts, diethylene glycol: 5 parts, polyvinyl chloride resin: 6 parts, brightener: 15 parts, film-forming aid: 9 parts, plasticizer: 9 parts, auxiliary material: 13 parts;

[0028] Component B includes the following components in parts by mass: tetrahydrofuran: 2 parts, diiodomethane: 7 parts, 2-butoxyethanol: 2 parts, dibutyl phthalate: 6 parts, nano-dioxide Silicon: 17 parts, benzyl alcohol: 20 parts, curing agent: 8 parts, defoamer: 11 parts, solvent: 20 parts;

[0029] Component C includes the follo...

Embodiment 2

[0037] This embodiment provides a low-density, high-temperature-resistant tray, including a tray, and a layer of low-density, high-temperature-resistant layer is coated on the outside of the tray. The low-density, high-temperature-resistant layer is composed of A, B, and C. The ratio is compounded, and A, B, C contain the following components in parts by mass:

[0038] Component A includes the following components in parts by mass: propylene carbonate: 8 parts, 3-butanediol: 11 parts, diethylene glycol: 8 parts, polyvinyl chloride resin: 9 parts, brightener: 18 parts, film-forming aid: 15 parts, plasticizer: 11 parts, auxiliary material: 17 parts;

[0039] Component B includes the following components in parts by mass: tetrahydrofuran: 7 parts, diiodomethane: 10 parts, 2-butoxyethanol: 5 parts, dibutyl phthalate: 9 parts, nano-dioxide Silicon: 19 parts, benzyl alcohol: 22 parts, curing agent: 12 parts, defoamer: 14 parts, solvent: 23 parts;

[0040] Component C includes the ...

Embodiment 3

[0048] This embodiment provides a low-density, high-temperature-resistant tray, including a tray, and a layer of low-density, high-temperature-resistant layer is coated on the outside of the tray. The low-density, high-temperature-resistant layer is composed of A, B, and C. The ratio is compounded, and A, B, C contain the following components in parts by mass:

[0049] Component A includes the following components in parts by mass: propylene carbonate: 7 parts, 3-butanediol: 8 parts, diethylene glycol: 7 parts, polyvinyl chloride resin: 7 parts, brightener: 17 parts, film-forming aid: 13 parts, plasticizer: 10 parts, auxiliary material: 15 parts;

[0050] Component B includes the following components in parts by mass: tetrahydrofuran: 5 parts, diiodomethane: 9 parts, 2-butoxyethanol: 3 parts, dibutyl phthalate: 8 parts, nano-dioxide Silicon: 18 parts, benzyl alcohol: 21 parts, curing agent: 11 parts, defoamer: 13 parts, solvent: 21 parts;

[0051] Component C includes the fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low-density high-temperature-resistant tray. A component A comprises the following components in parts by mass: 5-8 parts of propylene carbonate, 7-11 parts of 3-butanediol, 5-8 parts of diethylene glycol, 6-9 parts of a polyvinyl chloride resin, 15-18 parts of a brightener, 9-15 parts of a coalescing agent, 9-11 parts of a plasticizer and 13-17 parts of auxiliary materials; a component B comprises the following components in parts by mass: 2-7 parts of tetrahydrofuran, 7-10 parts of diiodomethane, 2-5 parts of 2-butoxyethanol, 6-9 parts of dibutyl phthalate, 17-19 parts of nano-silica, 20-22 parts of benzyl alcohol, 8-12 parts of a curing agent, 11-14 parts of an antifoaming agent and 20-23 parts of a solvent; and a component C comprises the following components in parts by mass: 22-25 parts of polyphenylene oxide resin powder, 9-12 parts of methylbenzene, 5-8 parts of a plasticizer, 13-16 parts of a coupling agent, 2-7 parts of a flame retardant, 12-16 parts of wood fiber powder, 25-28 parts of carbon fiber powder, 9-11 parts of a cross-linking agent and 15-19 parts of a coalescing agent.

Description

technical field [0001] The invention relates to the storage field, in particular to a low-density, high-temperature-resistant tray and a preparation method thereof. Background technique [0002] Pallets are accessories in great demand in the warehousing and logistics industry. The storage environment is extremely complex and there are many goods. The pallets in the prior art have the disadvantages of easy wear, damage and high temperature resistance, which reduces work efficiency. To improve the work efficiency and the safety of the work environment, the invention proposes a low-density high-temperature resistant tray and a preparation method thereof. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the shortcomings of the prior art and provide a low-density high-temperature-resistant tray, including the tray, which is coated with a low-density high-temperature-resistant layer. Composite according to the ratio o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D171/12C09D197/02C09D127/06C09D7/12
CPCC09D171/12C08K2201/011C08K2201/014C08L2201/08C08L2205/035C09D5/18C09D7/61C09D7/63C09D7/65C08L97/02C08L27/06C08K13/04C08K7/06C08K5/053C08K5/12C08K3/36C08K3/08C08K5/521C08K5/1515C08K5/17
Inventor 王忠义王正勇
Owner SUZHOU KESHENG STORAGE & LOGISTICS EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com