High-mid-infrared barrier and high-light transmittance PVB film and making method thereof

A technology with high light transmittance and high barrier, which is applied in the field of mid-infrared high barrier and high transmittance PVB film and its preparation, can solve the problems of high cost, low light transmittance and large haze of heat-insulating PVB film, and achieve Improved layering, superior mid-IR blocking and reflective capabilities, and production process optimization

Inactive Publication Date: 2017-08-11
ZHEJIANG DECENT PLASTIC
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In order to solve the problems raised in the prior art, the present invention proposes a PVB adhesive film with high mid-infrared barrier and high light transmittance and its preparation method. By adopting a new process formula, the low light transmittance of the heat-insulating PVB film is solved. , high haze and high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-mid-infrared barrier and high-light transmittance PVB film and making method thereof
  • High-mid-infrared barrier and high-light transmittance PVB film and making method thereof
  • High-mid-infrared barrier and high-light transmittance PVB film and making method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] (1) Preparation of DST nano-dispersion liquid: After mixing 8.5kg of organic solvent triethylene glycol diisocaprylate, 0.8kg of nano-ITO powder and 0.2kg of nano-GATO powder, add 0.5kg of dispersant during slow grinding Silane coupling agent 6598, continue to grind on a ball mill for 24 hours to obtain a nano-DST dispersion.

[0040] (2) 100kgPVB resin powder, 0.5kg antioxidant mixture (from 266.8g tetrakis [β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid] pentaerythritol ester and 133.2g three [2, 4-di-tert-butylphenyl]phosphite), 0.1kg UV absorber mixture (composed of 50g 2-(2'-hydroxy-5'-tert-octyl)-benzotriazole and 50g2-(2'-hydroxy- 5'-methyl)-benzotriazole), added to the powder mixer, and stirred at a high speed of 1000RPM for 20 minutes. Control the temperature of the equipment so that the temperature of the material during the stirring process is between 40°C and 50°C. Finally, 38 kg of plasticizer triethylene glycol diisocaprylate and 1 kg of nano-DST d...

Embodiment 2

[0042] (1) Preparation of DST nano-dispersion liquid: After mixing 8.5kg of organic solvent triethylene glycol diisocaprylate, 0.6kg of nano-ITO powder and 0.4kg of nano-GATO powder, add 0.5kg of dispersant during slow grinding Silane coupling agent 6598, continue to grind on a ball mill for 24 hours to obtain a nano-DST dispersion.

[0043] (2) 100kgPVB resin powder, 0.5kg antioxidant mixture (from 266.8g tetrakis [β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid] pentaerythritol ester and 133.2g three [2, 4-di-tert-butylphenyl]phosphite), 0.1kg UV absorber mixture (composed of 50g 2-(2'-hydroxy-5'-tert-octyl)-benzotriazole and 50g2-(2'-hydroxy- 5'-methyl)-benzotriazole), added to the powder mixer, and stirred at a high speed of 1000RPM for 20 minutes. Control the temperature of the equipment so that the temperature of the material during the stirring process is between 40°C and 50°C. Finally, 38 kg of plasticizer triethylene glycol diisocaprylate and 1 kg of nano-DST d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
transmittivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-mid-infrared barrier and high-light transmittance PVB film and a making method thereof. The method comprises the following steps: completely dispersing a nano-DST novel dispersion nano-material used as functional particles by an organic solvent, a dispersant and a plasticizer to prepare a dispersion, extruding the dispersion through a double screw extruder, and carrying out tape casting to produce the PVB film with high mid-infrared barrier and high light transmittance. The high-mid-infrared barrier and high-light transmittance PVB film produced in the invention has the advantages of excellent mechanical properties, super strong mid-infrared barrier and reflectivity, significant reduction of the cost, and very good market promotion and application prospects.

Description

technical field [0001] The invention relates to a PVB film with high mid-infrared barrier and high transmittance and a preparation method thereof, in particular to a heat-insulating film with a mid-infrared barrier of more than 90% and a light transmittance of more than 90% and a preparation method thereof. Background technique [0002] In 1938, the United States passed the law of using polyvinyl butyral (hereinafter referred to as PVB) film laminated glass on automobiles, which has opened the door to a large number of PVB films. After more than half a century of development, people have put forward more and more requirements for PVB diaphragms. [0003] Energy conservation and environmental protection are the eternal themes of economic development in the world today. Against the background of global warming, the "low-carbon economy" based on low energy consumption, low pollution, and low emissions has become a global hotspot. With the development of science and technology,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L29/14C08K13/06C08K9/06C08K5/134C08K5/526C08K5/3475C08K5/103C08K3/22
CPCC08K13/06C08K3/22C08K5/103C08K5/1345C08K5/3475C08K5/526C08K9/06C08K2201/011C08K2201/014C08L2201/10C08L2203/16C08L29/14
Inventor 蔡海堤谢怀玉陈庚朱立疆许忠明叶新棵叶卫民
Owner ZHEJIANG DECENT PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com