Low-temperature-resistant low-smoke inflaming-retarding light-diffusing polycarbonate composite material

A low-smoke flame-retardant, polycarbonate technology, applied in the field of polymer composite materials, to achieve good low-temperature impact performance, low smoke density, and low smoke density

Active Publication Date: 2017-05-10
SHANGHAI CHANGWEI JINCI ENG PLASTIC
View PDF1 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no report about a light-diffusing PC composite material with low temperature resistance, good flame retardancy, low smoke and no halogen.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature-resistant low-smoke inflaming-retarding light-diffusing polycarbonate composite material
  • Low-temperature-resistant low-smoke inflaming-retarding light-diffusing polycarbonate composite material
  • Low-temperature-resistant low-smoke inflaming-retarding light-diffusing polycarbonate composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Example 1. Preparation of Low Temperature, Low Smoke, Flame Retardant and Light Diffusion Polycarbonate Composite Material

[0041]The following components in weight percent: 974 parts of branched-chain PC of model 3127, 10 parts of branched polysiloxane flame retardant FCA-107, 4 parts of silicone microbead resin TSR-9002, 2 parts of anti- Oxygen agent 168, 1 part of antioxidant 1076, 4 parts of pentaerythritol stearate, 2 parts of light stabilizer 770, 2 parts of ultraviolet absorber UV234 and 1 part of toner are mixed in a high-speed mixer for 3 minutes, and then mixed at 260-280 Extrude through a twin-screw extruder at ℃, cool and granulate, dry the obtained pellets at 120℃ for 4 hours, and then inject them into standard strips at 260-280℃.

Embodiment 2

[0042] Example 2. Preparation of Low Temperature, Low Smoke, Flame Retardant and Light Diffusion Polycarbonate Composite Material

[0043] The following components in weight percent: 972 parts of branched chain PC of model 3127, 10 parts of branched chain polysiloxane flame retardant FCA-107, 2 parts of sulfonate flame retardant F535, 4 parts of organic silicon Bead-like resin TSR-9002, 2 parts of antioxidant 168, 1 part of antioxidant 1076, 4 parts of pentaerythritol stearate, 2 parts of light stabilized 770, 2 parts of ultraviolet absorber UV234 and 1 part of toner are mixed at high speed Mix in the machine for 3 minutes, then extrude through a twin-screw extruder at 260-280°C, cool, and granulate. The obtained pellets are dried at 120°C for 4 hours and then injection-molded into a standard spline at 260-280°C. have to.

Embodiment 3

[0044] Example 3. Preparation of Low Temperature, Low Smoke, Flame Retardant and Light Diffusion Polycarbonate Composite Material

[0045] The following components will be in weight percentage: 974 parts of linear PC model 3117, 10 parts of branched polysiloxane flame retardant FCA-107, 4 parts of silicone microbead resin TSR-9002, 2 parts of anti Oxygen agent 168, 1 part of antioxidant 1076, 4 parts of pentaerythritol stearate, 2 parts of light stabilizer 770, 2 parts of ultraviolet absorber UV234 and 1 part of toner are mixed in a high-speed mixer for 3 minutes, and then mixed at 260-280 Extrude through a twin-screw extruder, cool, and granulate. The obtained pellets are dried at 120°C for 4 hours and then injection-molded into standard strips at 260-280°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of high molecular composite materials, and particularly discloses a transparent low-temperature-resistant halogen-free low-smoke inflaming-retarding polycarbonate composite material, which is prepared from the following components in percentage by weight: 45 to 90 percent of branch-chain-shaped polycarbonate resin, 5 to 50 percent of siloxane copolymeric PC (Polycarbonate) resin, 0.1 to 1 percent of sulfonate inflaming retarding agent, 0.05 to 1 percent of polysiloxane inflaming retarding agent, 0.1 to 2 percent of light diffusant and 0.5 to 1.5 percent of aid. The transparent low-temperature-resistant halogen-free low-smoke inflaming-retarding polycarbonate composite material has the advantages that the light-diffusing PC composite material provided by the invention also has the characteristics of being resistant to low temperature, low in smoke density, halogen-free and inflaming-retarding besides having the basic optical property of light-diffusing PC; higher inflaming retarding class and lower smoke density can be achieved.

Description

technical field [0001] The invention relates to the field of polymer composite materials, in particular to a low-temperature-resistant, low-smoke, flame-retardant polycarbonate composite material and a preparation method thereof. Background technique [0002] Due to its advantages of environmental protection and energy saving, LED lights gradually replace incandescent and fluorescent lamps, but their luminous intensity per unit area is too high, which is very dazzling when viewed directly, causing glare and visual discomfort. Therefore, a light-transmitting cover is urgently needed, and the light is softened and uniformed through the lamp cover. Polycarbonate (PC) is widely used in the field of LED lampshades because of its excellent weather resistance, high impact resistance, excellent electrical insulation, high light transmittance, and less light energy loss. [0003] Light-diffusing PC is to add a spherical light-diffusing agent to the PC resin and disperse it evenly in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L69/00C08L83/04C08L33/12C08K5/42
CPCC08L69/00C08L2201/02C08L2201/10C08L2201/22C08L2205/025C08L2205/035C08L83/04C08L33/12C08K5/42
Inventor 朱爱华李盛科岳同健赵志刚胡同云
Owner SHANGHAI CHANGWEI JINCI ENG PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More