A fluorescent, glove technology, used in gloves, other household appliances, household components, etc., can solve the problem of not well protecting the operator's personal safety, and achieve the effect of saving the length of the production line, reducing injuries, and reducing temperature and time.

Inactive Publication Date: 2017-05-10
山东蓝帆新材料有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the more and more widespread use of PVC gloves, customers have higher and higher requirements for gloves safety and functional diversity. PVC gloves have been applied to various fields, providing people with good protection, but in special working environments For example, under dim light conditions, PVC gloves cannot protect the operator's personal safety very well.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The PVC fluorescent gloves include the following raw materials in parts by weight:

[0033] PVC powder 100 parts

[0034] Dioctyl terephthalate 75 parts

[0035] Fluorescent agent 10 parts

[0036] Changshu Calcium Zinc Stabilizer SBA-203 0.8 parts

[0037] 35 parts of dearomatized solvent oil of D70 grade

[0038] 0.6 parts of water-based PU glue.

[0039] The preparation method of described PVC fluorescent gloves, comprises the following steps:

[0040] (1) Preparation of primary ingredients: first add 75 parts of dioctyl terephthalate into the mixing tank, then add 100 parts of PVC powder, 0.8 parts of Changshu calcium-producing zinc stabilizer SBA-203, and 6 parts of D70 Aromatic solvent oil is stirred to obtain a batching;

[0041] (2) Static defoaming: the obtained primary ingredients are statically defoamed;

[0042] (3) Preparation of secondary ingredients: Add 29 parts of D70 grade dearomatized solvent oil to the primary ingredients after static defoamin...

Embodiment 2

[0054] The PVC fluorescent gloves include the following raw materials in parts by weight:

[0055] PVC powder 100 parts

[0056] Dioctyl terephthalate 75 parts

[0057] Fluorescent agent 20 parts

[0058] Original plastic F990 2 copies

[0059] 35 parts of dearomatized solvent oil of D70 grade

[0060] 0.6 parts of water-based PU glue.

[0061] The preparation method of described PVC fluorescent gloves, comprises the following steps:

[0062] (1) Preparation of primary ingredients: first add 75 parts of dioctyl terephthalate into the mixing tank, then add 100 parts of PVC powder, 2 parts of original plastic F990, and 10 parts of dearomatized solvent oil of D70 grade for stirring. get ingredients once;

[0063] (2) Static defoaming: the obtained primary ingredients are statically defoamed;

[0064] (3) Preparation of secondary ingredients: add 25 parts of dearomatized hydrocarbon solvent oil of D70 grade to the primary ingredients after static defoaming, and stir evenly ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of the plastic glove production, and particularly relates to a PVC fluorescence glove and a preparation method thereof. The PVC fluorescence glove comprises the following raw materials by weight: 100 parts of PVC powder, 25-75 parts of dioctyl terephthalate, 5-20 parts of a fluorescer, 0.5-2 parts of a calcium-zinc stabilizer, 15-35 parts of a viscosity reducer, and 0.5-0.7 parts of water-based PU glue. The PVC fluorescence glove has the characteristics of high absorbancy and long fluorescent time, and can be applied to the fields, such as the cleaning protection and the entertainment venues. The production process is simple and is easily operated.

Description

technical field [0001] The invention belongs to the technical field of plastic glove production, and in particular relates to a PVC fluorescent glove and a preparation method thereof. Background technique [0002] In recent years, PVC gloves have the characteristics of relatively simple production process, low material cost, convenient wearing, good air permeability, comfortable hand feeling, acid and alkali resistance, good isolation effect, no skin allergies, and low price, making PVC gloves The rapid development, widely used in medical, electronics, food processing, scientific research, fast food and other fields. [0003] With the more and more widespread use of PVC gloves, customers have higher and higher requirements for gloves safety and functional diversity. PVC gloves have been applied to various fields, providing people with good protection, but in special working environments For example, under dim light conditions, PVC gloves cannot protect the operator's person...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08K5/12C08J7/04A41D19/00A41D19/015B29C41/14B29L31/48
CPCC08K5/12A41D19/0006A41D19/0055B29C41/14B29L2031/4864C08J7/042C08J2327/06C08J2427/06C08J2475/04
Inventor 刘文静孙传志相刚王德玉周东升
Owner 山东蓝帆新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap