Environmental-friendly industrial waste special anti-crack dry-mixed mortar and preparation method thereof

A technology of industrial waste and dry-mixed mortar, applied in the field of mortar preparation, can solve the problems of increased production cost, trouble on construction site, poor water retention, adhesion and crack resistance, etc.

Inactive Publication Date: 2017-04-19
绍兴职业技术学院
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing dry-mixed mortar still has the problems of poor water retention, cohesion and crack resistance, which reduces the stability and reliability of the mortar quality; and the composition is complex, which increases the production cost
At the same time, when using dry-mixed mortar, it is necessary to mix the appropriate proportion with water. Sometimes due to geographical location, a large amount of water resources cannot be supplied, which brings trouble to the actual construction site.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The raw material components and the mass percentages of each component in the total amount of raw materials are as follows:

[0036] Quartz sand 55%

[0037] Cement 20%

[0038] Fly Ash 5%

[0039] Water retention thickener 0.5%

[0040] Polycarboxylate high performance water reducer 0.1%

[0041] Wherein the water-retaining thickener comprises cellulose and thixotropic lubricant, and wherein weight percent is:

[0042] Cellulose 30%

[0043] Thixotropic lubricant 60%;

[0044] Cement is 425# Portland cement in the present embodiment 1.

Embodiment 2

[0046] The raw material components and the mass percentages of each component in the total amount of raw materials are as follows:

[0047] Quartz sand 63%

[0048] Cement 23%

[0049] Fly Ash 8%

[0050] Water retention thickener 0.6%

[0051] Polycarboxylate high performance water reducer 0.2%

[0052] The water-retaining thickener includes cellulose and thixotropic lubricant, wherein the weight percentage is:

[0053] Cellulose 35%

[0054] Thixotropic lubricant 65%;

[0055] Cement is 425# Portland cement in the present embodiment 2.

Embodiment 3

[0057] The raw material components and the mass percentages of each component in the total amount of raw materials are as follows:

[0058] Quartz sand 70%

[0059] Cement 25%

[0060] Fly Ash 10%

[0061] Water retention thickener 0.7%

[0062] Polycarboxylate high performance water reducer 0.3%

[0063] The water-retaining thickener includes cellulose and thixotropic lubricant, wherein the weight percentage is:

[0064] Cellulose 40%

[0065] Thixotropic lubricant 60%;

[0066] Cement is 425# Portland cement in the present embodiment 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile bond strengthaaaaaaaaaa
Tensile bond strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to environmental-friendly industrial waste special anti-crack dry-mixed mortar. The environmental-friendly industrial waste special anti-crack dry-mixed mortar comprises the following components in percentage by mass: 55-70% of sand, 20-25% of cement, 5-10% of a mineral admixture, 0.5-0.7% of a water retaining thickener and 0.1-0.3% of a water reducer. The mineral admixture is slag, coal ash or volcanic ash, the water reducer is a polycarboxylate-type high-performance water reducer, and the water retaining thickener is a mixture of 30-40% by weight of cellulose and 60-70% by weight of a thixotropic lubricant. The mortar provided by the invention is simple in component and low in production cost, and the water retaining property and crack resistance of the mortar are greatly improved, the utilization amount of a water resource is reduced, and the application range is improved. Therefore, the mortar is particularly suitable for various building construction sites.

Description

technical field [0001] The invention belongs to the technical field of mortar preparation, and in particular relates to an environment-friendly industrial waste special crack-resistant dry-mixed mortar and a preparation method thereof. Background technique [0002] At present, whether it is masonry mortar, plastering mortar or ground leveling mortar, the quality of the mortar prepared on the construction site is unstable, the strength cannot meet the requirements, and even poor quality leads to a series of problems such as cracking, leakage, hollowing, and falling off. Common quality problems. The dry powder mortar adopts industrial production, which can strictly control the raw materials and mix ratio to ensure the stable and reliable quality of the mortar. It is a semi-finished mortar made of accurate ingredients and uniform mixing in the factory. It can be used only by adding water and stirring at the construction site. There are many types of dry-mixed mortar, and its ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B111/34
CPCC04B28/04C04B2111/00017C04B2111/343C04B2201/50
Inventor 汤薇蒋晓燕
Owner 绍兴职业技术学院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products