Fiber enhanced type wet paving/pre-paving waterproof coil material and construction method thereof

A waterproof membrane and fiber-reinforced technology, applied in chemical instruments and methods, infrastructure engineering, lamination, etc., can solve engineering leakage, entry into the structure, post-cast concrete and pre-laid polymer film membrane adhesive The failure of layer bonding and sealing performance, etc., achieves the effects of strong weather resistance, preventing wrinkles, and good contact with the ground

Active Publication Date: 2017-03-29
甘肃大禹防水科技发展有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the time for binding steel bars on the adhesive layer of the membrane exceeds its own weather-proof sealing safety (7~28 days), it will cause the adhesive sealing performance of the post-cast concrete and the pre-laid polymer film membrane adhesive layer to fail. , the above-mentioned "open water" under the waterproof layer will pass through the defects or damaged parts of the waterproof layer itself, and a large amount will enter between the waterproof layer and the structural concrete, and the open water will enter the structure at the structural cracks , resulting in engineering leakage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber enhanced type wet paving/pre-paving waterproof coil material and construction method thereof
  • Fiber enhanced type wet paving/pre-paving waterproof coil material and construction method thereof
  • Fiber enhanced type wet paving/pre-paving waterproof coil material and construction method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] Such as figure 1 and figure 2 As shown, the fiber-reinforced wet-laid / pre-laid waterproof membrane consists of a fiber-reinforced layer, an upper adhesive layer, a base layer, a lower adhesive layer and an isolation membrane.

[0056] Among them, the fiber reinforcement layer is made of polyester non-woven fabric, and its specification is 60g / m 2 The base layer is made of PET ester film with a thickness of 0.05mm and a tensile force of 200N / 5cm; the thickness of the upper adhesive layer and the lower adhesive layer are both 0.7mm; the isolation film is made of PE film.

[0057] The thickness of the waterproof membrane is 1.5mm; the length is 20m, and the width is 1.0m.

[0058] The adhesive layer is modified asphalt: the modifier is SBS.

[0059] The production method of the waterproof membrane is mainly divided into the following steps:

[0060] 1. Place the base layer and the isolation film in sequence, add adhesive between the two, and press the "sandwich" struc...

Embodiment 2

[0073] The fiber-reinforced wet-laid / pre-laid waterproof membrane consists of a fiber-reinforced layer, an upper adhesive layer, a base layer, a lower adhesive layer and an isolation membrane.

[0074] Among them, the fiber reinforced layer is made of polypropylene non-woven fabric, and its specification is 100g / m 2 The base layer of the tire is made of TPO film with a thickness of 0.30mm and a tensile force of 500N / 5cm; the thickness of the upper adhesive layer and the lower adhesive layer are both 0.82mm; the isolation film is made of PE film.

[0075] The thickness of the waterproof membrane is 2.0mm; the length is 15m, and the width is 1m.

[0076] The adhesive layer is modified asphalt: the modifier is SBR.

[0077] The production method of the waterproof membrane is mainly divided into the following steps:

[0078] 1. Place the base layer and the isolation film in sequence, add adhesive between the two, and press the "sandwich" structure together with the pair of rolle...

Embodiment 3

[0091] Such as figure 1 and image 3 As shown, the fiber-reinforced wet-laid / pre-laid waterproof membrane consists of a fiber-reinforced layer, an upper adhesive layer, a base layer, a lower adhesive layer and an isolation membrane.

[0092] Among them, the fiber reinforced layer is made of polyester fiber non-woven fabric, and its specification is 70g / m 2 The tire base layer is made of PE film with a thickness of 0.10mm and a tensile force of 200N / 5cm; the thickness of the upper adhesive layer and the lower adhesive layer are both 0.68mm; the isolation film is made of PP film.

[0093] The thickness of the waterproof membrane is 1.5mm; the length is 20m, and the width is 1m.

[0094] The adhesive layer is modified asphalt: the modifier is APP.

[0095] The production method of the waterproof membrane is mainly divided into the following steps:

[0096] 1. Place the base layer and the isolation film in sequence, add adhesive between the two, and press the "sandwich" struct...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a fiber enhanced type wet paving / pre-paving waterproof coil material and a special construction method of the fiber enhanced type wet paving / pre-paving waterproof coil material for water prevention of an underground engineering bottom plate. The waterproof coil material comprises a fiber enhancing layer, an upper adhesive layer, a tread layer, a lower adhesive layer and an isolating membrane. The construction method comprises the following steps: (1) constructing a concrete cushion layer of the underground engineering bottom plate; (2) wetly paving a fiber enhanced type wet paving / pre-paving waterproof coil material; and (3) bundling bottom plate structure steel bars on the fiber enhancing layer and pouring bottom plate structure concrete. According to the fiber enhanced type wet paving / pre-paving waterproof coil material and the construction method, wet paving and pre-paving construction manners in a waterproof coil material construction process are combined together; a waterproof structure is simple, and waterproof and safe dual guarantees are realized; and the probability of water leakage is effectively reduced.

Description

technical field [0001] The invention relates to the field of underground engineering waterproofing, in particular to a fiber-reinforced wet-laying / pre-laying waterproof coiled material and a construction method thereof. Background technique [0002] In the field of underground engineering waterproofing, the construction method of waterproofing membranes is constantly developing with the development of waterproofing membranes. The waterproofing membranes have developed from ordinary membranes that cannot be bonded and sealed with structural concrete to post-cast concrete with structures. The corresponding construction method of the pre-laid waterproof membrane that forms a bonded interface that is sealed and does not "channel water" has also been continuously improved. [0003] The first is the ordinary membrane that cannot form a bonded seal with structural concrete and its construction method, such as the construction method of SBS modified asphalt waterproof membrane, whic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B11/04B32B11/10B32B27/02B32B27/36B32B27/32B32B27/34B32B37/10E02D31/02
CPCB32B11/046B32B11/10B32B27/32B32B27/36B32B37/10B32B2262/0253B32B2262/0261B32B2262/0284B32B2307/558B32B2307/7265E02D31/025E02D2450/106
Inventor 郑宪明吴敏慧魏利兰
Owner 甘肃大禹防水科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com