Spinneret or metal sintering net cleaning method

A technology of metal sintered mesh and spinneret, which is applied in the direction of spinneret assemblies, textiles and papermaking, etc. It can solve problems such as non-uniform wire diameters, spinneret attachments that cannot be completely removed, and spinneret clogging, etc., to achieve Simple cleaning effect

Inactive Publication Date: 2017-03-01
上海志骑信息科技有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The problem now is that due to the viscosity of the raw materials in the liquid state, after a long time of use, the holes on the spinneret (head) and the holes on the metal sintering net used together will be bonded to the remaining raw materials in the holes. while clogging
The diameter of the wires flowing through the spinneret (head) and metal sintered mesh is not uniform, which affects the product quality
Traditional cleaning methods or heating or ultrasonic cleaning, all have the defect that the attachments in the spinneret (head) guide holes cannot be completely removed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] Embodiments suitable for the present invention are described in detail below.

[0016] A method for cleaning a spinneret or a sintered metal mesh, which includes an ultrasonic cleaning device, is characterized in that it includes the following steps:

[0017] Step 1, heating the spinneret or metal sintered mesh to be cleaned, so that the overall temperature of the spinneret or metal sintered mesh is higher than the glass transition temperature of the surface attachment;

[0018] Step 2, cooling the spinneret or metal sintered mesh obtained in step 1 to -100 degrees Celsius to -180 degrees Celsius;

[0019] Step 3, placing the spinneret or metal sintered mesh obtained in step 2 in an ultrasonic cleaning device, and starting the ultrasonic cleaning device to perform ultrasonic cleaning on the spinneret or metal sintered mesh.

[0020] The method for cleaning the spinneret or metal sintered net also includes vacuuming equipment, placing the spinneret or metal sintered net...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention specifically relates to a spinneret or metal sintering net negative pressure cleaning method characterized by comprising the following steps: 1, heating up a to-be-cleaned spinneret; 2, placing the spinneret of the step 1 into liquid nitrogen for cooling; 3, carrying out ultrasonic cleaning for the spinneret; 4, placing the spinneret into a negative pressure environment so as to separate and precipitate attachments on the spinneret surface and feed hole inner wall surfaces from the spinneret, thus realizing thoroughly cleaning effect. The whole spinneret or metal sintering net cleaning method is very concise in process, can completely and fully clean the surface and each ultra-small hole of the spinneret, and secondary pollution is prevented.

Description

technical field [0001] The invention relates to the field of fiber yarn manufacturing equipment, specifically to a cleaning equipment for spinnerets or metal sintered nets and a negative pressure cleaning method thereof. Background technique [0002] Spinneret is widely used in the field of fiber manufacturing, such as glass fiber, aramid fiber, carbon fiber, PE fiber and other fibers in the manufacturing process, must flow through a plate with many very small holes and then be cooled and formed. This spinneret is also called spinneret. The quality of the spinneret (head) is an important condition to ensure the quality of the finished raw silk and a good spinning process. Its function is to extrude the precisely metered spinning solution through numerous micropores on the spinneret (head) to extrude fiber bundles with a certain thickness and fine texture. [0003] The problem now is that due to the viscosity of the raw materials in the liquid state, after a long time of us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01D4/04
Inventor 冯华英侯志辉陈文新李炜
Owner 上海志骑信息科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products