High-strength repairing material for concrete cracks and construction method of high-strength repairing material

A technology for repairing materials and concrete, applied in the field of building construction, can solve the problems of sand, the ground floor is not compacted, the surface layer falls off, etc., and achieves the effect of improving its own strength, increasing connection strength, and ensuring cleanliness.

Inactive Publication Date: 2017-01-11
QINGDAO XINHUAYOU CONSTR GROUP
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] During the ground construction process, the ground is prone to cracks due to factors such as construction schedule, construction procedures, and seasonal construction. Finished, without doing a second wipe
After the ground is cracked, it is easy to have various quality problems such as sanding and surface layer falling off, which will eventually affect the normal use of the ground. According to the conventional repair method: during the construction period, it takes a long time to seal the repaired ground, and the area to be chiseled during maintenance is relatively small. Large, the ground after maintenance is easy to crack, and the rework rate after maintenance is generally high. These problems hinder the development of the construction industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A high-strength repair material for concrete cracks, comprising the following raw materials in parts by mass: 40 parts of crushed powder aggregate from waste concrete; 6 parts of fine sand; 20 parts of polyvinyl chloride ethyl ester; 8 parts of gypsum powder; 10 parts of resin curing agent 15 parts of water, the resin curing agent is an epoxy resin curing agent, and the powder aggregate crushed by waste concrete is a particle with a diameter of 3 mm.

[0030] A construction method of a high-strength repair material for concrete cracks, comprising the following construction steps:

[0031] (1) Making repairing materials: Mix the crushed powdered aggregates of waste concrete, fine sand, polyvinyl chloride, gypsum powder, add water, and stir for 5 minutes, then add epoxy resin curing agent for secondary stirring, two The mixing time for each time is 4 minutes, and the use time of the repairing material after stirring shall not exceed 20 minutes;

[0032] (2) Clean up the ...

Embodiment 2

[0037] A high-strength repair material for concrete cracks, comprising the following raw materials in parts by mass: 45 parts of crushed powder aggregate from waste concrete; 7 parts of fine sand; 23 parts of polyvinyl chloride ethyl ester; 9 parts of gypsum powder; 13 parts of resin curing agent parts; 17 parts of water. The resin curing agent is an epoxy resin curing agent, and the crushed powder aggregate of waste concrete is a particle with a diameter of 5 mm.

[0038] A construction method of a high-strength repair material for concrete cracks, comprising the following construction steps:

[0039] (1) Making repairing materials: Mix the crushed powdered aggregates of waste concrete, fine sand, polyvinyl chloride, gypsum powder, add water and stir for 8 minutes, then add epoxy resin curing agent for secondary stirring, two The mixing time for each time is 6 minutes, and the use time of the repairing material after stirring shall not exceed 20 minutes;

[0040] (2) Clean ...

Embodiment 3

[0046] A high-strength repair material for concrete cracks, comprising the following raw materials in parts by mass: 50 parts of crushed powder aggregate from waste concrete; 8 parts of fine sand; 25 parts of polyvinyl chloride ethyl ester; 10 parts of gypsum powder; 15 parts of resin curing agent parts; 20 parts of water. The resin curing agent is an epoxy resin curing agent, and the crushed powder aggregate of waste concrete is a particle with a diameter of 3 mm.

[0047] A construction method of a high-strength repair material for concrete cracks, comprising the following construction steps:

[0048] (1) Making repairing materials: Mix the crushed powdered aggregates of waste concrete, fine sand, polyvinyl chloride, gypsum powder, add water and stir for 10 minutes, then add epoxy resin curing agent for secondary stirring, two The mixing time for each time is 8 minutes, and the use time of the repairing material after stirring shall not exceed 20 minutes;

[0049] (2) Clea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength repairing material for concrete cracks. The high-strength repairing material comprises the following raw materials in parts by weight: 40-50 parts of ground waste concrete powder aggregate, 6-8 parts of fine sand, 20-25 parts of polyvinyl chloride ethyl ester, 8-10 parts of gypsum powder, 10-15 parts of a resin curing agent and 15-20 parts of water. A construction method of the high-strength repairing material for the concrete cracks comprises the following construction steps: (1) preparing the repairing material; (2) cleaning the cracks; (3) preprocessing the cracks; (4) filling the cracks; and (5) carrying out maintenance. The high-strength repairing material has the advantages that the raw material source is wide, the economic cost is low, the connection strength is high, the cracking is avoided, and the construction is simple and convenient.

Description

technical field [0001] The invention relates to the technical field of building construction, in particular to a high-strength repair material for concrete cracks and a construction method thereof. Background technique [0002] During the ground construction process, the ground is prone to cracks due to factors such as construction schedule, construction procedures, and seasonal construction. Finished, without doing a second wipe. After the ground is cracked, it is easy to have various quality problems such as sanding and surface layer falling off, which will eventually affect the normal use of the ground. According to the conventional repair method: during the construction period, it takes a long time to seal the repaired ground, and the area to be chiseled during maintenance is relatively small. Large, the ground after maintenance is easy to crack, and the rework rate after maintenance is generally high. These problems hinder the development of the construction industry. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B111/34
CPCC04B28/14C04B2111/00672C04B2111/343C04B18/16C04B14/06C04B24/2682C04B24/281C04B22/002
Inventor 石国强王恩鹏于忠福
Owner QINGDAO XINHUAYOU CONSTR GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap