Rubber tube material and preparation method thereof

A rubber tube and styrene-butadiene rubber technology, used in hoses, pipes, machinery and equipment, etc., can solve the problems of easy wear, inability to withstand high loads, poor fatigue resistance, etc., and achieve good wear resistance and long service life. , the effect of strong carrying capacity

Inactive Publication Date: 2017-01-04
ANHUI JIAMU RUBBLE & PLASTIC IND
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, rubber tubes on the market generally have shortcomings such as poor fatigue resistance and easy wear, so they cannot bear higher loads. It is imperative to develop a rubber tube material that can withstand higher loads and have higher wear resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of rubber tube material, it comprises the raw material of following weight portion: 50 parts of styrene-butadiene rubbers, 70 parts of natural rubbers, 25 parts of nitrile rubbers, 18 parts of polyurethanes, 2.3 parts of vulcanizing agents, 1.3 parts of accelerators, 5 parts of antioxidants, 2.3 parts of dispersant, 7 parts of nano calcium oxide, 8 parts of zinc oxide, 4.5 parts of magnesium oxide, 6 parts of ammonium benzoate, 2.3 parts of decabromodiphenylethane, 4 parts of fatty alcohol polyoxyethylene ether ammonium sulfate, 10 parts of quartz powder Parts, 16 parts of trimethylsiloxane.

[0019] The preparation method of described rubber tube material, comprises the following steps:

[0020] (1) Take each raw material component according to the ratio in parts by weight;

[0021] (2) Add styrene-butadiene rubber, natural rubber, nitrile rubber, vulcanizing agent, accelerator, anti-aging agent, dispersant, nano-calcium oxide, zinc oxide and magnesium oxide in...

Embodiment 2

[0025] A kind of rubber tube material, it comprises the raw material of following weight portion: 40 parts of styrene-butadiene rubbers, 65 parts of natural rubbers, 24 parts of nitrile rubbers, 13 parts of polyurethanes, 3 parts of vulcanizing agents, 2.1 parts of accelerators, 6 parts of antioxidants, 2.5 parts of dispersant, 8 parts of nano calcium oxide, 9 parts of zinc oxide, 4 parts of magnesium oxide, 8 parts of ammonium benzoate, 4 parts of decabromodiphenylethane, 4 parts of fatty alcohol polyoxyethylene ether ammonium sulfate, 10 parts of quartz powder Parts, 14 parts of trimethylsiloxane.

[0026] The preparation method of described rubber tube material, comprises the following steps:

[0027] (1) Take each raw material component according to the ratio in parts by weight;

[0028] (2) Add styrene-butadiene rubber, natural rubber, nitrile rubber, vulcanizing agent, accelerator, anti-aging agent, dispersant, nano-calcium oxide, zinc oxide and magnesium oxide into the...

Embodiment 3

[0032] A kind of rubber tube material, it comprises the raw material of following weight portion: 55 parts of styrene-butadiene rubbers, 50 parts of natural rubbers, 20 parts of nitrile rubbers, 20 parts of polyurethanes, 1.8 parts of vulcanizing agents, 1.7 parts of accelerators, 4.5 parts of antioxidants, 2.6 parts of dispersant, 6 parts of nano calcium oxide, 7 parts of zinc oxide, 5 parts of magnesium oxide, 6 parts of ammonium benzoate, 3 parts of decabromodiphenylethane, 5 parts of fatty alcohol polyoxyethylene ether ammonium sulfate, 12 parts of quartz powder Parts, 18 parts of trimethylsiloxane.

[0033] The preparation method of described rubber tube material, comprises the following steps:

[0034] (1) Take each raw material component according to the ratio in parts by weight;

[0035] (2) Add styrene-butadiene rubber, natural rubber, nitrile rubber, vulcanizing agent, accelerator, anti-aging agent, dispersant, nano-calcium oxide, zinc oxide and magnesium oxide into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rubber tube material that is prepared from the following raw materials in parts by weight: 30-60 parts of butadiene styrene rubber, 45-80 parts of natural rubber, 15-35 parts of nitrile rubber, 10-22 parts of polyurethane, 0.8-3.6 parts of vulcanizing agent, 1-3 parts of accelerant, 3-7 parts of anti-aging agent, 1-4 parts of dispersant, 2-10 parts of nano-calcium oxide, 3-12 parts of zinc oxide, 1-6 parts of magnesium oxide, 2-8 parts of amine benzoate, 1-4 parts of decabromodiphenyl ethane, 1-6 parts of ammonium fatty alcohol polyoxyethylene ether sulfate, 8-16 parts of quartz powder, and 8-20 parts of trimethylsiloxane. The rubber tube material of the invention has favorable abrasive resistance and compressive capacity, and long service life with greatly reduced use cost.

Description

technical field [0001] The invention relates to a packing material, in particular to a rubber tube material and a preparation method thereof. Background technique [0002] With the continuous popularization of rubber products, rubber will be used more in many aspects, especially in the industrial field, because of its low cost, greater impact resistance, better environmental tolerance and other factors, it is used as Widely used in production equipment. Rubber hose is one of the common rubber products, and it is an important component of electrical equipment such as EFI devices, turbochargers, and automobiles. At present, the rubber tubes on the market generally have disadvantages such as poor fatigue resistance and easy wear, so they cannot bear higher loads. It is imperative to develop a rubber tube material that can withstand higher loads and has higher wear resistance. Contents of the invention [0003] The object of the present invention is to provide a rubber tube ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L7/00C08L9/06C08L9/02C08L75/04C08L71/02C08K13/02C08K3/22C08K5/03C08K3/36C08K5/5419F16L11/04
CPCC08L7/00C08L9/06C08L2203/18C08L2205/02C08L2205/035F16L11/04
Inventor 叶春会王泽平
Owner ANHUI JIAMU RUBBLE & PLASTIC IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com