Autoclaved flyash-lime brick and manufacturing method thereof

A technology for autoclaved fly ash bricks and a manufacturing method, which is applied in the field of building materials, can solve problems such as large amount of dust, and achieve the effects of saving production costs, improving production environment and saving steam costs

Active Publication Date: 2017-01-04
中盐安徽红四方新型建材科技有限公司
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the deficiencies of the prior art, the present invention provides an autoclaved fly ash brick and its manufacturing method, which solves the technical problem of excessive dust in the production process of the autoclaved fly ash brick in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Autoclaved flyash-lime brick and manufacturing method thereof
  • Autoclaved flyash-lime brick and manufacturing method thereof
  • Autoclaved flyash-lime brick and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The autoclaved fly ash brick in this embodiment includes the following raw materials in weight percentage: 5% of coal gasification slag, 15% of fly ash, 50% of aggregate, 20% of carbide slag, and 10% of phosphogypsum.

[0042] According to the percentage by weight of the raw materials of this embodiment, the manufacture method of the autoclaved fly ash brick comprises the following steps:

[0043] S1. Weigh each raw material according to the percentage by weight of the raw material;

[0044] S2. Evenly measure the coal gasification slag, aggregate, calcium carbide slag and phosphogypsum into the feeding hopper through the belt, then add the materials and fly ash in the feeding hopper to the mixer at the same time, mix and stir evenly, and the stirring time is 3 minutes ;

[0045] S3. Send the uniformly stirred material in step S2 into the digestion chamber, store and digest for 2 hours, then send it to the powder mixer, and then send it to the automatic hydraulic brick...

Embodiment 2

[0047] The autoclaved fly ash brick in this embodiment includes the following raw materials in weight percentage: 5% of coal gasification slag, 15% of fly ash, 50% of aggregate, 20% of carbide slag, and 10% of phosphogypsum.

[0048] According to the percentage by weight of the raw materials of this embodiment, the manufacture method of the autoclaved fly ash brick comprises the following steps:

[0049] S1. Weigh each raw material according to the percentage by weight of the raw material;

[0050] S2. Evenly measure the coal gasification slag, aggregate, calcium carbide slag and phosphogypsum into the feeding hopper through the belt, then add the materials and fly ash in the feeding hopper to the mixer at the same time, mix and stir evenly, and the stirring time is 3 minutes ;

[0051] S3. Send the uniformly stirred material in step S2 into the digestion bin, store and digest for 2 hours, then send it to the powder mixer, and then send it to the automatic hydraulic brick mac...

Embodiment 3

[0053] The autoclaved fly ash brick in this embodiment includes the following raw materials in weight percentage: 5% of coal gasification slag, 15% of fly ash, 50% of aggregate, 20% of carbide slag, and 10% of phosphogypsum.

[0054] According to the percentage by weight of the raw materials of this embodiment, the manufacture method of the autoclaved fly ash brick comprises the following steps:

[0055] S1. Weigh each raw material according to the percentage by weight of the raw material;

[0056] S2. Evenly measure the coal gasification slag, aggregate, calcium carbide slag and phosphogypsum into the feeding hopper through the belt, then add the materials and fly ash in the feeding hopper to the mixer at the same time, mix and stir evenly, and the stirring time is 3 minutes ;

[0057]S3. Send the uniformly stirred material in step S2 into the digestion chamber, store and digest for 2 hours, then send it to the powder mixer, and then send it to the automatic hydraulic brick ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an autoclaved flyash-lime brick and a manufacturing method of the autoclaved flyash-lime brick, and refers to the technical field of building materials. The autoclaved flyash-lime brick comprises the following raw materials, coal gasification slag, fly ash, aggregate, acetylene sludge, and ardealite; according to a formula of the invention, content of fly ash is low; meanwhile, a certain amount of coal gasification slag is mixed, thus the production environment of big dust capacity caused by high content of fly ash is improved, utilization of coal gasification slag is increased, production cost is reduced, and performance index of the autoclaved flyash-lime brick product is improved; moreover, the product appearance and color are similar to antique black brick.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to an autoclaved fly ash brick and a manufacturing method thereof. Background technique [0002] Autoclaved fly ash brick is a new wall material, which is widely used in the interior and exterior walls of various civil buildings, public buildings and industrial plants, as well as the foundation of houses. Autoclaved fly ash bricks are an alternative to fired clay bricks. Fired clay bricks use clay as the main raw material, and there are solid and hollow clay bricks. The clay resources required for the production of solid clay bricks are relatively high-quality clay in arable land. The promotion of autoclaved fly ash bricks plays a positive role in reducing environmental pollution, protecting cultivated land, and improving building functions. [0003] In the prior art, autoclaved fly ash bricks are made of fly ash, lime or cement as the main raw material, mixed with appr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B18/06C04B18/08C04B18/04B28B3/02B28B11/24B28B17/02
CPCB28B3/02B28B11/24B28B17/02C04B28/143C04B2201/50C04B18/065C04B18/08C04B14/00C04B18/0481Y02W30/91
Inventor 谢中平韩凯锋杨爱萍吴根水孙梦雅王国防樊荣琦任永霞陈莉陈安跃
Owner 中盐安徽红四方新型建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap