Environment-friendly and energy-saving medium-temperature bronze glaze and method for making environment-friendly and energy-saving medium-temperature bronze-glazed ceramic products

An environment-friendly, energy-saving, ceramic product technology, applied in the field of ceramics, can solve the problems of PbO human injury and easy breakage, and achieve the effect of low dissolution rate, reducing firing cost and labor cost

Active Publication Date: 2019-02-05
FUJIAN DEHUA HUATAI CERAMICS CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, heavy metals such as PbO are used in the raw materials, and the product is prone to damage in actual use, resulting in the leakage of PbO and causing harm to the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly and energy-saving medium-temperature bronze glaze and method for making environment-friendly and energy-saving medium-temperature bronze-glazed ceramic products
  • Environment-friendly and energy-saving medium-temperature bronze glaze and method for making environment-friendly and energy-saving medium-temperature bronze-glazed ceramic products

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Environmentally friendly and energy-saving medium-temperature bronze glaze, including the following raw materials in terms of parts by mass: 49 parts of Sanming potassium feldspar, 14 parts of barium carbide, 4 parts of Longyan kaolin, 14 parts of calcium carbide, 6 parts of quartz, and 1 part of copper tailings copper tailings 9 parts, 9 parts of 2# frit, wherein, described 2# frit comprises the following raw material according to mass parts: 9 parts of potassium oxide, 14 parts of sodium oxide, 2 parts of calcium oxide, 21 parts of zinc tailings, magnesium oxide 4 parts.

[0027] The method for making ceramic products with the described environment-friendly and energy-saving medium-temperature bronze glaze comprises the following steps:

[0028] Step 1, ingredients ball milling and sieving:

[0029] 1) Proportioning the raw materials according to the parts by mass to obtain a proportioning material, putting the proportioning material in a ball mill according to the p...

Embodiment 2

[0036] Environmental protection and energy saving medium temperature bronze glaze, including the following raw materials in terms of mass fraction: 53 parts of Sanming potassium feldspar, 16 parts of barium carbide, 6 parts of Longyan kaolin, 5 parts of calcium carbide, 8 parts of quartz, 3 parts of copper tailings, 2# 12 parts of frit, wherein, the 2# frit includes the following raw materials in parts by mass: 12 parts of potassium oxide, 16 parts of sodium oxide, 3 parts of calcium oxide, 23 parts of zinc tailings, and 6 parts of magnesium oxide.

[0037] The method for making ceramic products with the described environment-friendly and energy-saving medium-temperature bronze glaze comprises the following steps:

[0038] Step 1, ingredients ball milling and sieving:

[0039] 1) Proportioning the raw materials according to the parts by mass to obtain a proportioning material, putting the proportioning material in a ball mill according to the proportioning material: ball: wate...

Embodiment 3

[0046] Environmentally friendly and energy-saving medium-temperature bronze glaze, including the following raw materials in terms of parts by mass: 56 parts of Sanming potassium feldspar, 17 parts of barium carbide, 7 parts of Longyan kaolin, 17 parts of calcium carbide, 11 parts of quartz, and 4 parts of copper tailings 14 parts, 14 parts of 2# frit, wherein, described 2# clinker comprises the following raw material according to mass parts: 14 parts of potassium oxide, 17 parts of sodium oxide, 4 parts of calcium oxide, 25 parts of zinc tailings, magnesium oxide 8 servings.

[0047] The method for making ceramic products with the described environment-friendly and energy-saving medium-temperature bronze glaze comprises the following steps:

[0048] Step 1, ingredients ball milling and sieving:

[0049]1) Proportioning the raw materials according to the mass parts to obtain a proportioning material, putting the proportioning material in a ball mill according to the proportion...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses eco-friendly energy-saving middle-temperature bronze glaze and a method for preparing an eco-friendly energy-saving middle-temperature bronze glazed ceramic through the eco-friendly energy-saving middle-temperature bronze glaze and belongs to the technical field of ceramics. The eco-friendly energy-saving middle-temperature bronze glaze is prepared from 49-56 parts by mass of Sanming potassium feldspar, 14-17 parts by mass of barium carbide, 4-7 parts by mass of Longyan kaolin, 14-17 parts by mass of calcium carbide, 6-11 parts by mass of quartz, 1-4 parts by mass of copper mine tailings and 9-14 parts by mass of frits 2#. The frits 2# are prepared from 9-14 parts by mass of potassium oxide, 14-17 parts by mass of sodium oxide, 2-4 parts by mass of calcium oxide, 21-25 parts by mass of zinc mine tailings and 4-8 parts by mass of magnesium oxide. The method for preparing an eco-friendly energy-saving middle-temperature bronze glazed ceramic comprises material blending, ball milling, sieving, immersion in glaze and sintering. The eco-friendly energy-saving middle-temperature bronze glazed ceramic saves energy, is environmentally friendly, has high wear resistance, has low cadmium and lead content and has no toxic or side effect on the human body.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to an environment-friendly and energy-saving medium-temperature bronze glaze and a method for making environment-friendly and energy-saving medium-temperature bronze-glazed ceramic products using the same. Background technique [0002] Glaze is a glassy thin layer covering the surface of ceramics, enamel and other bodies. Generally, the raw materials used in glaze are mineral raw materials such as quartz, feldspar, Longyan kaolin, etc. mixed with chemical additives according to a certain ratio. After grinding, glazing, Burning and other steps derived. The surface of the glaze is smooth and shiny, and has the performance of being impermeable and not easy to stain, which can not only improve the physical properties of the ceramic body, but also enhance and beautify the appearance of the ceramic product. Among them, bronze glaze is also called black glaze and black gold g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/04C04B41/86
CPCC03C8/04C04B41/5022C04B41/86
Inventor 庄锦贵
Owner FUJIAN DEHUA HUATAI CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com