Conveyer belt reproduction polymer compounded rubber material

A technology of compounding rubber and polymer, applied in the field of polymer materials, can solve problems such as waste and reuse, and achieve the effect of improving service life, prolonging service life and enhancing wear resistance.

Inactive Publication Date: 2016-12-21
山西佰得拓普工贸有限公司
View PDF9 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, generally speaking, after the conveyor belt is damaged, it is discarded and cannot be rebuilt and reused, resulting in waste
The prior art and inventions all focus on how to enhance the wear resistance and service life of new conveyor belts. So far, they have never involved composite materials suitable for remanufacturing conveyor belts. The present invention focuses on the recycling of conveyor belts and has enhanced Aiming at the wear resistance and service life of remanufactured conveyor belts, a polymer composite material suitable for remanufacturing conveyor belts and its preparation method have been developed and designed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Conveyer belt reproduction polymer compounded rubber material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A polymer composite rubber material for conveyor belt recycling, comprising the following components by weight:

[0028] 2 parts of methyl vinyl silicone rubber, 5 parts of natural rubber, 3 parts of butadiene rubber, 1.5 parts of styrene-butadiene rubber, 3 parts of carbon fiber reinforced material, 2 parts of zinc oxide, 0.5 parts of stearic acid, 5 parts of carbon black, Guma Long 0.2 parts, accelerator 1 part, anti-aging agent 2.5 parts, sulfur 0.8 parts.

[0029] After uniform mixing, it can be vulcanized and formed by conventional vulcanization process.

Embodiment 2

[0031] A polymer composite rubber material for conveyor belt recycling, comprising the following components by weight:

[0032] 4 parts of methyl vinyl silicone rubber, 6 parts of natural rubber, 1 part of butadiene rubber, 2 parts of styrene-butadiene rubber, 1 part of carbon fiber reinforced material, 1 part of zinc oxide, 0.6 parts of stearic acid, 3 parts of carbon black, Guma Long 0.8 parts, accelerator 2 parts, anti-aging agent 3 parts, sulfur 0.1 part.

[0033] After uniform mixing, it can be vulcanized and formed by conventional vulcanization process.

Embodiment 3

[0035] A polymer composite rubber material for conveyor belt recycling, comprising the following components by weight:

[0036] 1 part of methyl vinyl silicone rubber, 1 part of natural rubber, 6 parts of butadiene rubber, 2.5 parts of styrene-butadiene rubber, 1.5 parts of carbon fiber reinforced material, 2 parts of zinc oxide, 1 part of stearic acid, 4 parts of carbon black, Guma 1 part of Long, 1 part of Accelerator, 1.5 parts of Antiaging Agent, 1 part of Sulfur.

[0037] After uniform mixing, it can be vulcanized and formed by conventional vulcanization process.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technique of preparation of a conveyer belt rubber material, particularly to a conveyer belt reproduction polymer compounded rubber material. The conveyer belt reproduction polymer compounded rubber material comprises the following components in parts by weight: 1-10 parts of methyl vinyl silicone rubber, 1-8 parts of natural rubber, 1-6 parts of butadiene rubber, 1-3 parts of butadiene styrene rubber, 1-3 parts of carbon fiber reinforced plastic, 1-2 parts of zinc oxide, 0.1-1 part of stearic acid, 1-5 parts of carbon black, 0.1-1 part of coumarone, 1-2 parts of an accelerant, 1-3 parts of an antiager and 0.1-1 part of sulphur. The conveyer belt reproduction polymer compounded rubber material is used for reproducing a conveyer belt, is synthesized from the methyl vinyl silicone rubber and part of polymer rubbers, has the excellent performance of high abrasion resistance, high strength and shock resistance, and accords with the industry requirement.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a polymer composite rubber material for remanufacturing the upper and lower rubber of a conveyor belt and a preparation method thereof. Background technique [0002] The conveyor belt, also known as the conveyor belt, is used in the belt conveyor belt to carry and transport materials. It is a composite product of rubber and fiber, metal, or a composite product of plastic and fabric. Conveyor belts are widely used in cement, coking, metallurgy, chemical, steel and other industries where the conveying distance is short and the conveying volume is small. [0003] At present, generally speaking, after the conveyor belt is damaged, it is discarded and cannot be rebuilt and reused, resulting in waste. The prior art and inventions all focus on how to enhance the wear resistance and service life of new conveyor belts. So far, they have never involved composite mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L83/07C08L9/00C08L9/06C08K13/04C08K7/06C08K3/22C08K5/09C08K3/04
CPCC08L7/00C08L9/00C08L83/04C08L2201/08C08L2205/02C08L2205/035C08L9/06C08K13/04C08K7/06C08K2003/2296C08K5/09C08K3/04
Inventor 高伟苏会永陶建中
Owner 山西佰得拓普工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More