ABS/PBT/PCTG composite material with strong low temperature toughness and solvent resistance and preparation method thereof

A technology of solvent resistance and low temperature toughness, applied in the field of polymer composite materials and their processing, can solve the problems of solvent resistance, low temperature toughness, stress cracking, high rigidity of PC materials, etc. Toughness, overcoming the effect of increased density

Active Publication Date: 2018-01-16
JIANGSU KINGFA SCI & TECH ADVANCED MATERIALS CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the existing binary alloy technology, usually by adding a certain amount of PBT resin to the ABS resin, and adding a certain compatibilizer, an alloy with compatibility is prepared to solve the solvent resistance problem of the ABS resin, but it does not The low-temperature toughness and scratch resistance of the alloy are not considered, and its alloy products still have certain limitations
There are also reports on the low temperature of ABS / PCTG composites prepared from ABS and PCTG (polycondensed from three monomers of terephthalic acid, ethylene glycol and 1,4-cyclohexanedimethanol by transesterification). Compared with PCTG and ABS, the toughness is greatly improved, but the content of PCTG is too high, and there is no improvement in the solvent resistance of the composite material
In addition, there are technical reports using PC (polycarbonate) as the third component polyester to prepare ABS / PBT / PC composites, but the introduction of PC will have a negative impact on the solvent resistance of the ternary composite system, and PC material is more rigid, which will make the internal stress of the alloy higher, and the risk of stress cracking will occur
In summary, the existing composite material technology route cannot achieve excellent comprehensive properties such as good solvent resistance and low temperature toughness at the same time, and can be applied to the preparation of alloy materials for kitchen appliances such as dishwashers, industrial battery casings, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • ABS/PBT/PCTG composite material with strong low temperature toughness and solvent resistance and preparation method thereof
  • ABS/PBT/PCTG composite material with strong low temperature toughness and solvent resistance and preparation method thereof
  • ABS/PBT/PCTG composite material with strong low temperature toughness and solvent resistance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] Below in conjunction with embodiment and comparative example, further set forth advantage of the present invention and notable feature, but be not limitation of the present invention, especially the data in the embodiment do not limit the consumption of each composition in the invention.

[0021] Raw material selection:

[0022] Select the following resins with different characteristics in the following embodiments, and their names and corresponding characteristics are defined as follows:

[0023] PCTG(110): The glass transition temperature of PCTG resin is 110°C;

[0024] PBT (0.6): The intrinsic viscosity of PBT resin is 0.6dl / g;

[0025] PBT (0.8): The intrinsic viscosity of PBT resin is 0.8dl / g;

[0026] PBT (1.1): The intrinsic viscosity of PBT resin is 1.1dl / g;

[0027] ABS(0.3): The average particle size distribution of butadiene rubber used for ABS resin is small, ranging from 0.2-0.5 μm, and the particle size D50≈0.3 μm;

[0028] ABS (1.3): The average part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ABS (acrylonitrile butadiene styrene) / PBT (polybutylene terephthalate) / PCTG (polyethylene terephthalate glycol) composite material high in low-temperature toughness and solvent resistance. The shortcoming that ABS resin is poor in solvent resistance is overcome by introduction of PBT resin from the composite material; low-temperature falling ball impact of the composite material is greatly increased by introduction of PCTG resin, and problems about increasing density, solvent resistance performance degradation and the like due to the fact that existing PC is taken as third-component polyester are solved; a bulking agent is applied to the composite material, compatibility of the composite material can be more effectively improved especially by the adoption of an MGD comb-shaped polymer, and low-temperature falling ball toughness of the material is further improved; the composite material is good in solvent resistance, heat resistance and low-temperature falling ball performance, and strict requirements of kitchen appliances, industrial battery shells and the like can be met.

Description

technical field [0001] The invention relates to an ABS modified composite material and a preparation method thereof, in particular to an ABS / PBT / PCTG composite material with strong low-temperature toughness and solvent resistance and a preparation method thereof, belonging to the technical field of polymer composite materials and processing thereof. Background technique [0002] ABS (acrylonitrile-butadiene-styrene) resin has the advantages of high rigidity of acrylonitrile, good heat resistance, excellent toughness of butadiene and good gloss of styrene, high processing fluidity, and is widely used in electronics, electrical appliances, automobiles , textile equipment, construction and daily necessities, etc. However, the solvent resistance of ABS resin itself is poor, which leads to the problem of solvent cracking when it is used in many products such as kitchen appliances and battery material shells. PBT (polybutylene terephthalate) resin is a kind of crystalline polyest...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08L55/02C08L51/04C08L25/14C08L33/08C08K5/103C08K5/526
CPCC08L67/02C08L2201/08C08L2205/025C08L2205/035C08L2205/06C08L2205/08C08L55/02C08K5/103C08K5/526C08L51/04C08L25/14C08L33/08
Inventor 郭少华黄池光陈日平范聪成刘乐文肖鹏夏建盟
Owner JIANGSU KINGFA SCI & TECH ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com