Waste paper/high-density polyethylene luminescent composite and preparation method thereof

A high-density polyethylene and composite material technology, applied in the field of wood-plastic composite materials, can solve the problems of reducing the structural strength of the board, destroying the integrity of the board, increasing the process steps, etc., and achieving the effects of high production efficiency, low cost and abundant resources

Inactive Publication Date: 2016-12-14
SOUTH CHINA AGRI UNIV
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above scheme adopts the hole-opening method to build in the luminescent material, which increases the process steps and complicates the production
Slots or holes destroy the integrity of the board, reduce the structural strength of the board, and affect the performance of the board

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waste paper/high-density polyethylene luminescent composite and preparation method thereof
  • Waste paper/high-density polyethylene luminescent composite and preparation method thereof
  • Waste paper/high-density polyethylene luminescent composite and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The raw materials and mass fractions used in the preparation of a waste paper / high-density polyethylene luminescent composite material are as follows:

[0028]

[0029]

[0030] (1) Put the recovered waste newspapers into a shredder and crush them, the size of the fragments is 5*20mm, and then mix the newspapers with a 1% sodium hydroxide solution, and the mass ratio of the two mixtures is 1:10. Stir at a speed of 20r / min until the newspaper is completely submerged, filter after reacting for 8 minutes, and dry in a drying oven at a drying temperature of 90°C and a drying time of 24 hours. The dried waste paper is pulverized with a cutting grinder to obtain 40-80 mesh paper powder.

[0031] (2) Put paper powder, high-density polyethylene and other raw materials into a high-speed mixer according to the proportion and mix them evenly. The mixing temperature is 120°C and the mixing time is 30 minutes.

[0032] (3) Extrude and granulate the mixed material with a twin-...

Embodiment 2

[0036] The raw materials and mass fractions used in the preparation of a waste paper / high-density polyethylene luminescent composite material are as follows:

[0037]

[0038] (1) Put the recovered milk carton into a pulverizer to crush, the size of the fragments is 5*5mm, and then mix the milk carton with 2.5% sodium hydroxide solution, and the mass ratio of the two mixed is 1:12. Stir at a speed of 30r / min until the milk carton is completely submerged, filter after reacting for 12 minutes, and dry in a drying oven at a drying temperature of 110°C and a drying time of 18 hours. The dried waste paper is pulverized with a cutting grinder to obtain 40-80 mesh paper powder.

[0039] (2) Put paper powder, high-density polyethylene and other raw materials into a high-speed mixer according to the proportion and mix them evenly. The mixing temperature is 140°C and the mixing time is 20 minutes.

[0040] (3) Extrude and granulate the mixed material with a twin-screw extruder. The...

Embodiment 3

[0044] The raw materials and mass fractions used in the preparation of a waste paper / high-density polyethylene luminescent composite material are as follows:

[0045]

[0046] (1) Put the recovered office waste paper into a paper shredder and crush it, the size of the pieces is 5*20mm, and then mix the waste paper with a sodium hydroxide solution with a concentration of 2%, and the mass ratio of the two mixed is 1:8 . Stir at a speed of 20r / min until the waste paper is completely submerged, filter after reacting for 10min, and dry in a drying oven at a drying temperature of 100°C and a drying time of 20h. The dried waste paper is pulverized with a cutting grinder to obtain 40-80 mesh paper powder.

[0047] (2) Put paper powder, high-density polyethylene and other raw materials into a high-speed mixer according to the proportion and mix them evenly. The mixing temperature is 130°C and the mixing time is 25 minutes.

[0048] (3) Extrude and granulate the mixed material with...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
bending strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a composite, and provides a waste paper / high-density polyethylene luminescent composite and a preparation method thereof. A long-persistence luminescent material subjected to organic modification is adopted as luminescent pigment, the long-persistence luminescent material, pretreated waste paper fiber powder, high-density polyethylene, a coupling agent, a processing agent and the like are subjected to blending extrusion, and the luminescent wood-plastic composite is obtained. According to the waste paper / high-density polyethylene luminescent composite and the preparation method thereof, the comprehensive utilization level of waste resources is greatly improved, and environmental pollution caused by treatment of waste resources is greatly reduced; compared with a traditional board and a traditional wood-plastic composite, the luminescent composite is easy to process, low in cost, wide in raw material source, environmentally friendly, free of pollution and the like; besides, by adding the luminescent material, the advantages of practicability, attractiveness, safety and the like of the luminescent composite are improved, and based on an existing wood-plastic board production process, the luminescent composite is a wood-plastic board very suitable for large-scale production.

Description

technical field [0001] The invention belongs to the field of wood-plastic composite materials, and in particular relates to a waste paper / high-density polyethylene luminous composite material and a preparation method thereof. Background technique [0002] Paper is widely used in our life, and paper fiber, as a kind of natural fiber, has been paid more and more attention by people, but the recycling rate of paper products is very low, and most of them are used for recycling to produce lower-grade paper Products, the recycling process is complicated, but the economic benefits are very low, which is not conducive to the rational utilization of resources. Using waste paper instead of wood fibers to make wood-plastic composite materials does not require a deinking process, has low recycling costs, can be filled in large quantities, has a wide range of applications, high economic value, and has a good application prospect. [0003] Wood-plastic composite material is a polymer mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L1/02C08L51/06C08K13/06C08K3/26C08K5/134C08K5/526C08K5/54C08K5/10C08K9/04C08K3/24C08K3/34C08K3/30
CPCC08L23/06C08L1/02C08L2205/03C08L2207/062
Inventor 胡传双涂登云宋杰古今胡芳园周桥芳
Owner SOUTH CHINA AGRI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com