A kind of nickel hydroxide/graphene nanocomposite material and preparation method thereof, supercapacitor electrode and supercapacitor

A nano-composite material, nickel hydroxide technology, applied in hybrid capacitor electrodes, hybrid/electric double-layer capacitor manufacturing, nanotechnology, etc., can solve the problems of limited application, poor conductivity of transition metal hydroxides, etc., and achieve higher ratio Effects of surface area utilization, overall performance improvement, and utilization improvement

Active Publication Date: 2018-08-31
嘉兴企远网信息科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Transition metal hydroxides are used as electrode materials in supercapacitors. They have the advantages of high specific capacitance, low price, and environmental protection. Applications on supercapacitors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nickel hydroxide/graphene nanocomposite material and preparation method thereof, supercapacitor electrode and supercapacitor
  • A kind of nickel hydroxide/graphene nanocomposite material and preparation method thereof, supercapacitor electrode and supercapacitor
  • A kind of nickel hydroxide/graphene nanocomposite material and preparation method thereof, supercapacitor electrode and supercapacitor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Preparation of graphite oxide: weigh 5.0g graphite and 3.75g NaNO respectively 3 Put it into a 1L beaker, stir vigorously, slowly add 150mL of concentrated sulfuric acid, stir for 0.5 hours, then slowly add 20g of KMnO 4, Added in 0.5 hours, and continued to stir for 20 hours, the viscosity of the reactant increased, and the stirring was stopped to obtain a paste-like purple-red substance. After standing for 5 days, slowly add 500mL deionized water and 30mLH 2 o 2 At this time, the color of the solution becomes more obvious bright yellow. After the solution is fully reacted, it is centrifuged and washed to obtain graphite oxide.

[0042] Take 5.0 mg of graphite oxide, disperse it in 100 mL of deionized water, and sonicate for 1 hour to obtain solution A. Control the water temperature at 5-40°C, and the water temperature in this embodiment is 25°C. Weigh 0.6g of nickel chloride hexahydrate and dissolve it in 20mL of deionized water, stir evenly, add to solution A, and...

Embodiment 2

[0045] The preparation method of graphite oxide is with embodiment 1. Take 10.0 mg of graphite oxide, disperse it in 100 mL of deionized water, and sonicate for 1 hour to obtain solution A. Control the water temperature at 5-40° C., which is 30° C. in this embodiment. Weigh 1.2g of nickel chloride hexahydrate and dissolve it in 20mL of deionized water, stir well, add to solution A, and ultrasonicate for 30 minutes to obtain solution B. Take 1.0g of vitamin C and dissolve it in 15mL of deionized water, stir it evenly, add it to solution B, and sonicate for 30 minutes to obtain solution C. Dissolve 0.6g of urea in 15mL of deionized water, stir evenly, add to solution C, and sonicate the solution for 20 minutes to obtain solution D. Pour the solution D into a 200mL polytetrafluoroethylene reactor and react at 120°C for 24 hours.

[0046] The product was washed three times with deionized water and ethanol, respectively, and dried at 60°C for 10 hours to obtain a nickel hydroxide...

Embodiment 3

[0048] The preparation method of graphite oxide is with embodiment 1. Take 20.0 mg of graphite oxide, disperse it in 100 mL of deionized water, and sonicate for 1 hour to obtain solution A. Control the water temperature at 5-40° C., which is 30° C. in this embodiment. Weigh 1.6g of nickel chloride hexahydrate and dissolve it in 20mL of deionized water, stir well, add to solution A, and ultrasonicate for 30 minutes to obtain solution B. Take 1.0g of vitamin C and dissolve it in 15mL of deionized water, stir it evenly, add it to solution B, and sonicate for 30 minutes to obtain solution C. Dissolve 0.8g of urea in 15mL of deionized water, stir evenly, add to solution C, and sonicate the solution for 20 minutes to obtain solution D. Pour the solution D into a 200mL polytetrafluoroethylene reactor and react at 140°C for 12 hours.

[0049] The product was washed three times with deionized water and ethanol, and dried at 80°C for 6 hours to obtain nickel hydroxide / graphene nanocom...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a nickel hydroxide / graphene nano composite, a preparation method thereof, a supercapacitor electrode and a supercapacitor. The composite is formed by base material graphene and a nickel hydroxide nanosheet growing on the surface of the graphene in situ, and the composite integrally has a three-dimensional porous structure. A graphene-based composite is prepared by loading a transition metal hydroxide on the surface of the graphene with high specific surface area and excellent conductivity in a composition manner. Due to synergistic effect of all componenta of the composite, all components can mutually enhance advantages and avoid disadvantages; and meanwhile, long circle life, high power density and high stability of an electric double-layer capacitor and high specific capacitance characteristic of a pseudocapacitor are combined, thereby improving the comprehensive performances of the supercapacitor.

Description

technical field [0001] The invention belongs to the technical field of nanomaterial preparation, and in particular relates to a nickel hydroxide / graphene nanocomposite material and a preparation method thereof, a supercapacitor electrode and a supercapacitor. Nickel nanosheets, and sheet-like nickel hydroxide / graphene self-assemble into a three-dimensional porous structure. Background technique [0002] Supercapacitors are also called electrochemical capacitors, and have the characteristics of short charging time, long service life, good temperature characteristics, high safety, energy saving and environmental protection. Supercapacitors have attracted considerable attention over the past few decades due to their higher power density and longer cycle life than secondary batteries, traditional electrostatic and electrolytic capacitors. Electrode materials are the key to improving the performance of supercapacitors, and they are also factors that determine the cost of superca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01G11/30H01G11/36H01G11/86B82Y30/00B82Y40/00
CPCY02E60/13
Inventor 黄家锐李雪雪谷翠萍刘畅
Owner 嘉兴企远网信息科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com