A production process of an automobile turbocharger intake hose

A technology of turbocharger and production process, applied in the direction of tubular articles, applications, household appliances, etc., can solve the problems of high product scrap rate, easy accumulation of air in the valley, etc., to improve product performance and high product strength , the effect of enhancing compatibility

Inactive Publication Date: 2018-04-27
NINGBO FENGMAO FAR EAST RUBBER
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the fluidity of the internal rubber material is too good, the air is easy to accumulate in the trough during molding, resulting in a high scrap rate of the product, so it is necessary to improve the process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A production process of an automobile turbocharger intake hose
  • A production process of an automobile turbocharger intake hose

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A production process for the intake rubber hose of an automobile turbocharger, including raw material preparation, mixing (temperature 80°C, time 2 hours), calendering, pre-vulcanization, cloth cutting (cutting the tape to the designed specifications), reeling (Wrap the rubber cloth on the mold to form a rubber sleeve), sleeve (put the rubber sleeve on the mold), shaping and vulcanization steps.

[0032] The raw material of the automobile turbocharger intake rubber hose is composed of the following components in parts by weight: 100 parts of methyl vinyl silicone rubber, 5 parts of modified carbon nanotubes, vulcanizing agent (bis(2,4-peroxide) Dichlorobenzoyl)) 1 part, 0.5 part by weight of color masterbatch (commercially available), 0.5 part by weight of anti-frost agent (commercially available, silicone rubber anti-frost agent, Ningbo Zhenhai Weiqi Rubber & Plastic Technology Co., Ltd.).

[0033] The preparation method of the modified carbon nanotube is as follows: ...

Embodiment 2

[0038] A production process for the intake rubber hose of an automobile turbocharger, including raw material preparation, mixing (temperature 90°C, time 1 hour), calendering, pre-vulcanization, cloth cutting (cutting the tape to the designed specifications), reeling (Wrap the rubber cloth on the mold to form a rubber sleeve), sleeve (put the rubber sleeve on the mold), shaping and vulcanization steps.

[0039] The raw material of the automobile turbocharger intake rubber hose is composed of the following components in parts by weight: 100 parts of methyl vinyl silicone rubber, 10 parts of modified carbon nanotubes, vulcanizing agent (bis(2,4-peroxide) Dichlorobenzoyl)) 3 parts, color masterbatch (commercially available) 1.5 parts by weight, anti-frost agent (commercially available, silicone rubber anti-frost agent, Ningbo Zhenhai Weiqi Rubber and Plastic Technology Co., Ltd.) 1 part by weight.

[0040] The preparation method of the modified carbon nanotube is as follows:

[0...

Embodiment 3

[0045] A production process for an automobile turbocharger intake hose, including raw material preparation, mixing (temperature 85°C, time 1.5 hours), calendering, pre-vulcanization, cloth cutting (cutting the tape to the designed specifications), reeling (Wrap the rubber cloth on the mold to form a rubber sleeve), sleeve (put the rubber sleeve on the mold), shaping and vulcanization steps.

[0046] The raw material of the automobile turbocharger intake rubber hose is composed of the following components in parts by weight: 100 parts of methyl vinyl silicone rubber, 8 parts of modified carbon nanotubes, vulcanizing agent (bis(2,4-peroxide) Dichlorobenzoyl)) 2 parts, color masterbatch (commercially available) 1 part by weight, anti-frost agent (commercially available, silicone rubber anti-frost agent, Ningbo Zhenhai Weiqi Rubber & Plastic Technology Co., Ltd.) 0.8 part by weight.

[0047] The preparation method of the modified carbon nanotube is as follows:

[0048] (1) Hydrox...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production process of an air inlet rubber tube of an automobile turbocharger. The production process comprises the following steps: raw material preparation; mixing; rolling; fabric cutting; coiling; sleeving; sizing; and vulcanization. A prevulcanization step is additionally arranged between rolling and fabric cutting, wherein the prevulcanization temperature is 190+ / -5 DEG C, and the time is 8-10min. The production process disclosed by the invention improves the percent of pass of production while improving the product performance, thereby reducing the production cost of a product.

Description

technical field [0001] The invention relates to a production method of automobile parts, in particular to a production process of an automobile turbocharger air intake hose. Background technique [0002] A turbocharger is a device that uses the exhaust energy of the engine to drive the turbine and drive the compressor to increase the intake pressure of the engine. It compresses more air into the cylinder to increase the amount of fuel, thereby improving the combustion performance. In order to improve fuel economy and reduce exhaust emissions. [0003] The biggest advantage of the turbocharger is that it can greatly increase the power and torque of the engine without increasing the engine displacement. Generally speaking, the maximum output power and torque of the engine after the turbocharger is installed will increase. More than 40%, so many automobile manufacturing companies use this supercharging technology to improve the output power of the engine, so as to realize the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C69/02B29C35/02C08L83/07C08K9/06C08K5/14C08K7/24B29L23/00
CPCB29C35/02B29C69/02B29L2023/005C08K5/14C08K7/24C08K9/06C08K2201/011C08L83/04
Inventor 蒋春雷张高峰
Owner NINGBO FENGMAO FAR EAST RUBBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com