Graphene/flax composite fiber preparation method

A graphene fiber and composite fiber technology, applied in fiber treatment, plant fiber, biochemical fiber treatment and other directions, to achieve the effect of enhancing impurity removal effect, improving dyeing effect, and good removal effect

Inactive Publication Date: 2016-11-16
SUZHOU YUXI NEW MATERIAL TECH
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there are still few reports on the preparation of conductive composite fibers by combining graphene fibers with flax fibers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 1) Preparation of compound enzyme refining agent: compound and mix 50% pectinase, 15% dextranase, 25% cellulase, 5% amylase and 5% chelating agent EDTA;

[0026] 2) Pretreatment of flax fiber: immerse the flax fiber in a chitosan aqueous solution with a concentration of 20g / L at 55°C for 3 hours and then dedry;

[0027] 3) Refining: take 10 g of the flax fiber prepared in step 2) and soak in 100 mL of the compound enzyme refining agent prepared in step 1) for 2 hours, wash, dehydrate and dry to obtain modified flax fiber;

[0028] 4) Take 10g of the modified flax fiber prepared in step 3) and mix with 0.1g of graphene fiber.

Embodiment 2

[0030] 1) Preparation of compound enzyme refining agent: compound and mix 60% of pectinase, 5% of dextranase, 15% of cellulase, 10% of amylase and 10% of chelating agent EDTA;

[0031] 2) Pretreatment of flax fiber: immerse the flax fiber in a chitosan aqueous solution with a concentration of 10g / L at 60°C for 1 hour and then dedry;

[0032] 3) Refining: take 10 g of the flax fiber prepared in step 2) and soak in 300 mL of the compound enzyme refining agent prepared in step 1) for 2 hours, wash, dehydrate and dry to obtain modified flax fiber;

[0033] 4) Take 10g of the modified flax fiber prepared in step 3) and mix with 0.5g of graphene fiber.

Embodiment 3

[0035] 1) Preparation of compound enzyme refining agent: compound and mix 55% pectinase, 15% dextranase, 5% cellulase, 15% amylase and 10% chelating agent EDTA;

[0036] 2) Pretreatment of flax fiber: immerse the flax fiber in a chitosan aqueous solution with a concentration of 20g / L at 65°C for 3 hours and then dedry;

[0037] 3) Refining: take 10 g of the flax fiber prepared in step 2) and soak in 500 mL of the compound enzyme refining agent prepared in step 1) for 1 hour, wash, dehydrate and dry to obtain modified flax fiber;

[0038] 4) Take 10 g of the modified flax fiber prepared in step 3) and mix with 1 g of graphene fiber.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
electrical resistivityaaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a graphene / flax composite fiber preparation method, which comprises: 1) preparing a compound enzyme refining agent; 2) pre-treating flax fiber; 3) refining, wherein the prepared flax fiber is immersed into the compound enzyme refining agent and soaked, and washing and dewatering drying are performed to prepare the modified flax fiber; and 4) uniformly mixing the modified flax fiber and graphene fiber. According to the present invention, the flax fiber is mixed with the graphene fiber, such that the strength and the toughness of the blended yarn of the flax fiber can be improved, and the resistivity of the mixed fiber achieves 10-103 [omega].m while the resistivity of the conventional fiber is about 10-14 [omega].m, wherein the resistivity is improved by more than 10 magnitude orders; the flax fiber is subjected to the modification treatment with the biological enzyme so as to improve the dyeing effect of the yarn; and the impurity pectin removing effect and the impurity lignin removing effect are good with the selected compound enzyme refining agent, and the chelating agent is increased so as to further enhance the impurity removing effect of the compound enzyme.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a preparation method of graphene / flax composite fiber. Background technique [0002] Conductive fibers have always been a research hotspot for functional fibers, generally referring to resistivity less than 10 8 The fiber of Ω·cm has the functions of conduction, electric heating and anti-electromagnetic radiation, and is usually concentrated in the fields of anti-static clothing or anti-electromagnetic radiation clothing used in special occasions. [0003] The main methods for the manufacture of conductive fibers include: one is to coat the surface of conventional fibers with conductive components, and the other is to mix conductive materials with fiber raw materials and make conductive fibers by spinning. The method of coating the conductive layer on the surface of the fiber is to coat the conductive material containing metal, carbon black or metal compound on the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/03D06M16/00D01F9/12D02G3/04D01D1/02D01D5/06D06M101/06
CPCD01D1/02D01D5/06D01F9/12D02G3/04D06M15/03D06M16/003D06M2101/06D10B2101/12D10B2201/04
Inventor 杨阳
Owner SUZHOU YUXI NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com