Environment-friendly high-flame-retardant foaming material for agricultural water ladle and preparation method thereof
A foaming material and high flame-retardant technology, which is applied in the field of environmentally friendly high-flame-retardant foaming materials for agricultural water spoons and its preparation, can solve problems such as large environmental impacts and human hazards, reduced safety, and non-environmental protection, so as to ensure fire prevention Safety, light weight, reasonable matching effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0018] An environmentally friendly and highly flame-retardant foaming material for agricultural water spoons, which is composed of the following mass ratio components, isocyanate: composite material = 1:0.65, the said isocyanate is Yantai Wanhua M100, and the composition of the composite material is as follows: Count, the specific mass parts are as follows:
[0019] Polyester 330 35-45 parts
[0020] Polyester 3350 25-35 parts
[0021] Polyester 400 9-12 parts
[0022] Silicone oil 158 2.5-3.5 parts
[0023] Catalyst HPF1 1.2-1.8 parts
[0024] Catalyst S20 1.0-1.5 parts
[0025] 3-3.8 parts of water
[0026] Flame retardant TCPP 33-39 parts.
Embodiment 2
[0028] A preparation method of the above-mentioned environmentally friendly and highly flame-retardant foaming material for agricultural water spoons, comprising the following preparation steps: firstly, a composite material is prepared: 35 parts of polyester 330, 25 parts of polyester 3350, 9 parts of polyester 400, 2.5 parts 158 parts of silicone oil, 1.2 parts of catalyst HPF1, 1.0 parts of catalyst S20, 33 parts of flame retardant TCPP and 3 parts of water are added to the reactor for mixing reaction, the stirring speed is 80r / min, and the stirring time is 6h to obtain the combination material, and then mix the isocyanate and the combined material uniformly at a mass ratio of 1:0.65 to obtain the foaming material.
Embodiment 3
[0030] A preparation method of the above-mentioned environmentally friendly and highly flame-retardant foaming material for agricultural water spoons, comprising the following preparation steps: firstly, a composite material is prepared: 40 parts of polyester 330, 30 parts of polyester 3350, 11 parts of polyester 400, 3 158 parts of silicone oil, 1.6 parts of catalyst HPF1, 1.2 parts of catalyst S20, 35 parts of flame retardant TCPP and 3.4 parts of water are added to the reactor for mixing reaction, the stirring speed is 100r / min, and the stirring time is 7h to obtain the combination material, and then mix the isocyanate and the combined material uniformly at a mass ratio of 1:0.65 to obtain the foaming material.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com