Energy saving brick used for landscape architecture, and production method thereof

An energy-saving brick and landscape technology, applied in the field of garden equipment, can solve the problems of high production cost and unfavorable promotion, and achieve the effect of beautiful appearance, easy operation and light weight

Inactive Publication Date: 2016-11-09
安徽菲扬新材料有限公司
View PDF8 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the honeycomb energy-saving bricks produced by this technical solution have good thermal insulation and energy-saving effects, the production cost is high, which is not conducive to popularization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An energy-saving brick used in garden landscapes. In parts by mass, the energy-saving brick includes 20 parts of clay, 5 parts of mica powder, 10 parts of lightweight filler, 5 parts of straw-coated particles, 5 parts of attapulgite, clay Mixture 3 parts, kaolin 5 parts, bentonite 5 parts, cement 15 parts, curing agent 0.5 parts.

[0027] Wherein, the straw-coated particles are prepared from the following raw materials in parts by weight: 25-35 parts of diatomite, 20-30 parts of plant straw powder, 15-25 parts of water glass, 1-2 parts of carboxymethyl cellulose, 3-5 parts of clay.

[0028] Wherein, the preparation process of the straw-coated particles is as follows: dry diatomaceous earth and add carboxymethyl cellulose to a high-speed mixer, stir and mix at a speed of 500 rpm at 110°C for 20 minutes, then add water glass and continue to stir for 10 minutes Finally, plant straw powder and clay were added and blended at a speed of 1000 rpm for 5 minutes, dried and sent...

Embodiment 2

[0040] An energy-saving brick used for garden landscapes. In terms of parts by mass, the energy-saving brick includes 30 parts of clay, 10 parts of mica powder, 15 parts of lightweight filler, 10 parts of straw-coated particles, 10 parts of attapulgite, clay Mixture 5 parts, kaolin 10 parts, bentonite 10 parts, cement 20 parts, curing agent 2 parts.

[0041] Wherein, the straw-coated particles are prepared from the following raw materials in parts by weight: 35 parts of diatomite, 30 parts of plant straw powder, 25 parts of water glass, 2 parts of carboxymethyl cellulose, and 5 parts of clay.

[0042] Wherein, the preparation process of the straw-coated particles is as follows: dry diatomaceous earth and add carboxymethyl cellulose to a high-speed mixer, stir and mix at a speed of 800 rpm at 120°C for 30 minutes, then add water glass and continue to stir for 15 minutes Finally, plant straw powder and clay were added and mixed at a speed of 1500rpm for 10 minutes, dried and sen...

Embodiment 3

[0053] Embodiment 3: An energy-saving brick used in garden landscapes. In parts by mass, the energy-saving brick includes 25 parts of clay, 8 parts of mica powder, 12 parts of lightweight filler, 8 parts of straw-coated particles, and attapulgite 8 parts, 4 parts of binder, 7 parts of kaolin, 8 parts of bentonite, 17 parts of cement, and 1 part of curing agent.

[0054] Wherein, the straw-coated particles are prepared from the following raw materials in parts by weight: 30 parts of diatomite, 25 parts of plant straw powder, 20 parts of water glass, 1 part of carboxymethyl cellulose, and 4 parts of clay.

[0055] Wherein, the preparation process of the straw-coated particles is as follows: dry the diatomaceous earth and add carboxymethyl cellulose to a high-speed mixer, stir and mix at 115°C at a speed of 600rpm for 25min, then add water glass and continue to stir for 13min Finally, plant straw powder and clay were added and blended at a speed of 1300rpm for 8 minutes, dried an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an energy saving brick used for landscape architecture, and a production method thereof, and relates to the field of garden equipment. The energy saving brick used for landscape architecture comprises, by mass, 20-30 parts of clay, 5-10 parts of mica powder, 10-15 parts of a lightweight filler, 5-10 parts of straw coated particles, 5-10 parts of attapulgite, 3-5 parts of an adhesive, 5-10 parts of kaolin, 5-10 parts of bentonite, 15-20 parts of cement and 0.5-2 parts of a curing agent. The production method adopting the above technical scheme has the advantages of reasonable production steps, convenience in operation, low production cost, and convenience for promotion, and the produced energy-saving brick has the advantages of light mass, heat insulation, water resistance, earthquake resistance, durability, and beautiful profile.

Description

technical field [0001] The invention relates to the field of garden equipment, in particular to an energy-saving brick for garden landscape and a preparation method thereof. Background technique [0002] After clay bricks are disabled, although there are light-weight aerated cement blocks with better thermal insulation properties as wall materials, the investment is large and it is not easy to popularize, especially the material is loose and the slurry is easy to fall off. Low and poor security, the current porous cement bricks are only made of cement and sand or slag mixed with crushed materials, whether it is sand and gravel bricks, fly ash bricks or metal slag powder bricks and coal gangue bricks, there is no lightweight The blending of insulation materials not only makes the bricks too heavy, but also permeable to water and heat, easy to delamination and damage, not durable, high cost, long construction period, and bricks, as an important part of the garden landscape, di...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B33/13C04B33/02
CPCC04B33/04C04B33/131C04B33/132C04B2235/3427C04B2235/602Y02P40/60
Inventor 岳朝雷
Owner 安徽菲扬新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com