Rare earth plastic shell material and preparation method thereof

A plastic shell and rare earth technology, applied in the field of plastic production, can solve the problems of easy aggregation of carbon nanotubes and large specific surface area of ​​carbon nanotubes, and achieve the effect of increasing interface bonding force, improving the stability and strength of the finished product structure, and improving the dispersion ability

Inactive Publication Date: 2016-10-26
安徽岳塑汽车工业股份有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the large surface energy and specific surface area of ​​carbon nanotubes, carbon nanotubes are easy to agglomerate; at the same time, the surface of carbon nanotubes presents a strong non-polarity, making it insoluble in any solvent and polymer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] A rare earth plastic casing material, which is composed of the following raw materials in parts by weight:

[0021] Cerium oxide 0.1, lanthanum citrate 0.1, carbon nanotube 3, thionyl chloride 40, N,N dimethylformamide 3, ethylenediamine 100, melamine 16, 35% formaldehyde aqueous solution 36, polyvinyl chloride 170, 75wt% sulfuric acid 20, 95wt% nitric acid 30, carboxymethylcellulose sodium 2, anhydrous calcium chloride 4, attapulgite 30, dimethylethanolamine 2, epoxy octyl stearate 10.

[0022] A preparation method of the rare earth plastic casing material, comprising the following steps:

[0023] (1) Mix the above-mentioned 75wt% sulfuric acid and 95wt% nitric acid, stir evenly, add carbon nanotubes, oscillate ultrasonically in a constant temperature water bath at 50°C for 2 hours, add 8 times the weight of the system to dilute with deionized water, and keep it warm , after the solution is layered, the supernatant is discarded, the lower solution is suction-filtered,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a rare earth plastic shell material. The rare earth plastic shell material is prepared from the following raw materials in parts by weight: 0.1 to 0.2 part of cerium oxide, 0.1 to 0.2 part of lanthanum citrate, 3 to 4 parts of carbon nanotubes, 40 to 50 parts of thionyl chloride, 3 to 5 parts of N,N-dimethylformamide, 100 to 120 parts of ethylenediamine, 16 to 20 parts of melamine, 36 to 40 parts of 35 to 37% formaldehyde aqueous solution, 170 to 200 parts of polyvinyl chloride, 20 to 30 parts of 75 to 80 wt% sulfuric acid, 30 to 40 parts of 95 to 98wt% nitric acid, 2 to 3 parts of sodium carboxymethylcellulose, 4 to 7 parts of anhydrous calcium chloride, 30 to 40 parts of attapulgite, 2 to 3 parts of dimethylethanolamine and 10 to 13 parts of octyl epoxy stearate. According to the rare earth plastic shell material, the cerium oxide and the lanthanum citrate are added, so that the surface strength of a finished plastic shell product can be effectively increased, and the weather resistance is increased.

Description

technical field [0001] The invention relates to the field of plastic production, in particular to a rare earth plastic casing material and a preparation method thereof. Background technique [0002] Carbon nanotubes have excellent mechanical properties and self-lubricating properties. As a filling material, if they can be uniformly dispersed in the polyvinyl chloride matrix and can form good interfacial compatibility with the polyvinyl chloride matrix, they can be used effectively. Improve the mechanical properties and friction properties of polyvinyl chloride matrix. However, due to the large surface energy and specific surface area of ​​carbon nanotubes, carbon nanotubes are easy to aggregate; at the same time, the surface of carbon nanotubes presents a strong non-polarity, making it insoluble in any solvent and polymer. Therefore, in order to improve the dispersion of carbon nanotubes in the polymer matrix and enhance the interfacial compatibility between carbon nanotube...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L61/32C08K13/06C08K9/02C08K7/24C08K9/04C08K3/34C08K3/22C08K5/098C08G12/40B29B9/06
CPCB29B9/06C08G12/40C08K2201/011C08L27/06C08L2201/08C08L2205/03C08L61/32C08K13/06C08K9/02C08K7/24C08K9/04C08K3/346C08K2003/2213C08K5/098
Inventor 储诚刚储晓节王焰炉储鹏彭先启王进王鹏
Owner 安徽岳塑汽车工业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com