Titanium-silicon-aluminum molecular sieve, preparation method and applications thereof, and a cyclic ketone oxidation method

A molecular sieve and titano-silicate-alumina technology, which is applied in the direction of molecular sieves and alkali exchange compounds, molecular sieve catalysts, oxidative preparation of carboxylic acids, etc., can solve the problems of occupying land resources and storage space, and achieve good catalytic effects

Active Publication Date: 2016-10-19
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this way, valuable land resources and storage space are taken up, and the recovery and utilization technology development of deactivated ammoximation catalysts is urgently needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Titanium-silicon-aluminum molecular sieve, preparation method and applications thereof, and a cyclic ketone oxidation method
  • Titanium-silicon-aluminum molecular sieve, preparation method and applications thereof, and a cyclic ketone oxidation method
  • Titanium-silicon-aluminum molecular sieve, preparation method and applications thereof, and a cyclic ketone oxidation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] Therefore, as previously mentioned, the present invention provides a method for preparing the titano-silicon-aluminum molecular sieve of the present invention, the method comprising:

[0027] (1) Mix the unloading agent with the acid solution for beating, carry out the first heat treatment to the obtained slurry, and separate and obtain the first solid, wherein the unloading agent is the unloading agent of the reaction device using titanium silicon molecular sieve as the catalyst active component. Dispensing;

[0028] (2) The second heat treatment is performed after mixing the first solid, the aluminum source, the titanium source and the alkali source in the presence of an aqueous solvent.

[0029]In the present invention, the unloading agent of the reaction device using titanium-silicon molecular sieve as the catalyst active component can be the unloading agent from various devices that use titanium-silicon molecular sieve as the catalyst active component, for example,...

Embodiment 1

[0108] This example illustrates the methods and products provided by the invention.

[0109] At normal temperature (20°C, the rest of the comparative examples are the same as the examples) and normal pressure (0.1MPa, the rest of the comparative examples are the same as the examples), the deactivated cyclohexanone oximation catalyst SH-2 and 1mol / L hydrochloric acid The aqueous solution was mixed and beaten, and then the mixed slurry was mixed and stirred at 80°C for 12 hours; after solid-liquid separation, the solid, aluminum source aluminum sulfate, titanium source titanium sulfate and sodium hydroxide aqueous solution (pH 12) were mixed and the mixture was put into Stainless steel sealed reaction kettle, treated at 170°C for 12 hours, wherein, the mass composition of the material is deactivated cyclohexanone oximation catalyst: titanium source: aluminum source: acid: alkali: water = 100: 1: 1: 10: 5: 250, deactivated cyclohexanone oximation catalyst with SiO 2 In terms of ...

Embodiment 2

[0114] This example illustrates the methods and products provided by the invention.

[0115] At normal temperature and pressure, first mix the deactivated cyclohexanone oximation catalyst SH-3 with 5mol / L hydrochloric acid solution for beating, then mix and stir the mixed slurry at 60°C for 1 hour; after solid-liquid separation, separate the solid, Aluminum source aluminum sol (content is 20% by weight), titanium source tetrabutyl titanate and tetrapropyl ammonium hydroxide aqueous solution (pH is 10) are mixed, and the mixed solution is put into a stainless steel sealed reaction kettle, and treated at 150°C for 12h , wherein the quality of the material is composed of deactivated cyclohexanone oximation catalyst: titanium source: aluminum source: acid: alkali: water=100:2:0.5:15:15:200, and the deactivated cyclohexanone oximation catalyst is SiO 2 In terms of acid, H + In terms of alkali in OH - count. Then the product was recovered according to the method of Example 1 to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
adsorption capacityaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The present invention relates to the field of molecular sieves, and mainly provides a titano-silicon-alumina molecular sieve and its preparation method and application. The titano-silicon-alumina molecular sieve contains aluminum, titanium, silicon and oxygen, and its pore volume is 0.3 cm 3 /g or more, the total specific surface area is 200m 2 /g or more, the outer area is 30m 2 /g or more, and the ratio of the outer surface area to the total specific surface area is 10-55%; 0 = 0.10 and the adsorption time is 1h, the measured benzene adsorption is at least 65mg/g molecular sieve, N 2 Under the static adsorption test, it has a micropore size distribution in the range of 0.9-2.0nm. The invention also provides a method for oxidizing cyclic ketones. The titano-silicon-alumina molecular sieve with special physical and chemical characteristic structure of the present invention has the advantages of high benzene adsorption capacity and micropore pore size distribution in the range of 0.9-2.0nm, for example, it is used for cyclic molecules, especially cyclic ketone molecules to participate or The generated reaction can achieve better catalytic effect.

Description

technical field [0001] The invention relates to a titano-silicon-aluminum molecular sieve and a preparation method of the titano-silicon-aluminum molecular sieve. The invention also relates to the application of the titano-silicon-aluminum molecular sieve and a method for oxidizing cyclic ketones. Background technique [0002] Titanium-silicon molecular sieve is a molecular sieve whose skeleton is composed of silicon, titanium and oxygen elements, and has broad application prospects in petroleum refining and petrochemical industry. Among them, TS-1 molecular sieve is a new type of titanium-silicon molecular sieve with excellent catalytic selective oxidation performance formed by introducing transition metal element titanium into the molecular sieve framework with ZSM-5 structure. [0003] TS-1 not only has the catalytic oxidation of titanium, but also has the shape-selective effect and excellent stability of ZSM-5 molecular sieve, and has successfully realized industrial app...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B39/00B01J29/89C07C51/31C07C59/01B09B3/00
Inventor 史春风林民朱斌
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap