Preparation method of composite modified asphalt convenient for post cleaning

A technology of composite modified asphalt and modified asphalt, which is applied in the direction of building components, building insulation materials, buildings, etc., can solve the problem of high temperature, low temperature, elastic recovery of modified asphalt that cannot meet the technical requirements of ultra-thin wear layer and road performance Poor, poor sealing effect and other problems, to achieve the effect of prolonging the service time of the road surface, improving the strength of the sealing layer, and excellent road performance

Inactive Publication Date: 2016-10-12
TIANJIN KANGYUAN ENG MACHINERY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, ordinary emulsified modified asphalt is often difficult to meet the actual traffic and climate conditions, and its road performance is poor.
When ordinary emulsified modified asphalt is used as ultra-thin wear layer sticky layer oil or stone chip seal layer bonding material, often due to its small viscosity, it will flow when spraying a large amount, so that the emulsified modified asphalt cannot be sprayed or a very small amount Into the hot mix mixture, resulting in poor sealing effect, serious water seepage on the road surface, and road surface diseases such as shifting, peeling, pits, cracks, etc. will appear shortly after opening to traffic
Even if the viscosity of some emulsified modified asphalt meets the requirements of use, the high temperature, low temperature, elastic recovery and other indicators of the modified asphalt after demulsification cannot meet the technical requirements of ultra-thin wear layer, and the above-mentioned pavement diseases will still appear in the end

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of composite modified asphalt convenient for post cleaning
  • Preparation method of composite modified asphalt convenient for post cleaning

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The technical solutions of the present invention will be further described below through specific examples.

[0014] A method for preparing composite modified asphalt that is convenient for post-cleaning is carried out according to the following steps:

[0015] Step 1, first heating asphalt and mineral oil to 60-100°C, adding 20-40 parts by weight of a surfactant into the asphalt, and stirring for 10-30 minutes to obtain modified asphalt;

[0016] Step 2, heating the water to 40-60°C, then sequentially adding modifier, blending agent and emulsifier into the water, stirring for 5-10 minutes to obtain mixed soap;

[0017] Step 3: Mix the modified asphalt prepared in step 1 and the mixed soap liquid prepared in step 2 and mechanically stir for 30-40 minutes at a stirring temperature of 80-100°C. After stirring evenly, cool down to 20-25°C to obtain a cationic composite modified asphalt. Sexual asphalt.

[0018] Material addition is shown in the table below in each embodi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of composite modified asphalt convenient for post cleaning. The preparation method comprises the steps that asphalt and mineral oil are heated to 60 DEG C-100 DEG C, 20-40 parts by weight of a surfactant is added into the asphalt, and stirring is conducted for 10-30 min to obtain modified asphalt; water is heated to 40 DEG C-60 DEG C, then a modifier, a blender and an emulsifier are sequentially added into the water, and after stirring is conducted for 5-10 min, mixed soap liquid is obtained; the modified asphalt and the mixed soap liquid are mixed and mechanically stirred for 30-40 min at the temperature of 80 DEG C-100 DEG C, after the materials are stirred to be uniform, the temperature is lowered to 20 DEG C-25 DEG C, and then the cationic composite modified asphalt is obtained. A micro-cracked ground crack is sealed more closely, the surface adsorption capacity of the micro-cracked ground crack is higher, an impermeable isolation layer can be formed on the surface of the ground crack to prevent surface rain and the like from permeating to the stratum, and therefore the service life of a road surface is prolonged; through addition of the surfactant, the asphalt can easily fall off from an adhesion material during post cleaning to avoid the condition that the surfactant component is added in a cleanser again, therefore, the cleaning cost is reduced, and the environment is protected.

Description

technical field [0001] The invention relates to the technical field of road surface repair materials, and more specifically relates to a preparation method of composite modified asphalt which is convenient for later cleaning. Background technique [0002] At present, the emulsified asphalt commonly used as ultra-thin wear layer sticky layer oil and stone chip seal layer in highway construction is mostly fast-cracking ordinary emulsified modified asphalt. The viscous layer oil for ultra-thin wear layer requires emulsified asphalt not only to bond the surface layer and the underlying layer, but more importantly, it can partially enter the upper asphalt mixture to play the role of sealing layer. However, ordinary emulsified modified asphalt is often difficult to meet the actual traffic and climate conditions, and its road performance is poor. When ordinary emulsified modified asphalt is used as ultra-thin wear layer sticky layer oil or stone chip seal layer bonding material, o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L75/04C08L91/00C08L91/06C08L33/08C08L63/00C08L31/04C08L23/22
CPCC08L95/00C08L2205/035C08L63/00C08L91/06C08L75/04C08L91/00C08L33/08C08L31/04C08L23/22
Inventor 刘谦
Owner TIANJIN KANGYUAN ENG MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products