Graphite lubricating oil friction-reducing additive and preparation method thereof
A technology of anti-friction additives and lubricating oils, applied in the petroleum industry, lubricating compositions, etc., can solve problems such as unsatisfactory use effects, no additive control, easy precipitation and stratification, etc., to reduce wear of parts and prolong oil change period, the effect of improving the environment
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] A graphite lubricating oil additive comprises 10 parts by weight of graphite powder, 30 parts by weight of a dispersant, and 60 parts by weight of 60N secondary hydrogenated base oil.
[0023] Weigh the raw materials according to the ratio; add base oil into the low-temperature reaction kettle, the base oil kinematic viscosity at 40°C should not exceed 8CST, and the kinematic viscosity at 100°C should not exceed 2.4CST, then add 3 parts of dispersant, after 10-15 minutes, add particle size 2-3μm graphite powder, continue to stir and disperse, the graphite powder in the reaction kettle is put into the base oil to complete the stirring and dispersing; the stirred graphite mixture enters the colloid mill for dispersing three times, and then enters the high-pressure convection mill for crushing, the pressure Adjust to 26MPa / cm 2 , the convective relative central pressure reaches 35MPa / cm 2 As above, the graphite is pulverized sequentially under high pressure and high speed...
Embodiment 2
[0025] A graphite lubricating oil additive comprises 15 parts by weight of graphite powder, 33 parts by weight of a dispersant, and 52 parts by weight of 60N secondary hydrogenated base oil.
[0026] Weigh the raw materials according to the ratio; add base oil into the low-temperature reaction kettle, the base oil kinematic viscosity at 40°C should not exceed 8CST, and the kinematic viscosity at 100°C should not exceed 2.4CST, then add 3 parts of dispersant, after 10-15 minutes, add particle size 2-3μm graphite powder, continue to stir and disperse, the graphite powder in the reaction kettle is put into the base oil to complete the stirring and dispersing; the stirred graphite mixture enters the colloid mill for dispersing three times, and then enters the high-pressure convection mill for crushing, the pressure Adjust to 29MPa / cm 2 , the convective relative central pressure reaches 32MPa / cm 2 As above, the graphite is pulverized sequentially under high pressure and high speed...
Embodiment 3
[0028] A graphite lubricating oil additive comprises 20 parts by weight of graphite powder, 35 parts by weight of a dispersant, and 45 parts by weight of 60N secondary hydrogenated base oil.
[0029] Weigh the raw materials according to the ratio; add base oil into the low-temperature reaction kettle, the kinematic viscosity of the base oil at 40°C should not exceed 8CST,
[0030] The kinematic viscosity at 100°C is not greater than 2.4CST, then add 3 parts of dispersant, after 10-15 minutes, add graphite powder with a particle size of 2-3μm, continue to stir and disperse, put the graphite powder in the reactor into the base oil, and complete the stirring Dispersion; the stirred graphite mixture enters the colloid mill to disperse three times, and then enters the high-pressure convection mill for crushing, and the pressure is adjusted to 28MPa / cm 2 , the convective relative central pressure reaches 30MPa / cm 2 As above, the graphite is pulverized sequentially under high pressu...
PUM
Property | Measurement | Unit |
---|---|---|
kinematic viscosity | aaaaa | aaaaa |
kinematic viscosity | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com