A kind of ceramic powder and preparation method thereof

A technology of ceramic powder and ceramic raw materials, which is applied in the field of ceramic building materials, can solve the problems of particularly large influence of slurry flow rate, change and reduce the amount of clay, etc., and achieve the effect of improving sustainable development, reducing the amount of clay used, and high strength

Active Publication Date: 2018-11-02
广东清远蒙娜丽莎建陶有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, many additives can improve the strength of the green body very well, but they have a particularly large impact on the flow rate of the slurry, it is difficult to greatly change the amount of clay, and directly use the reinforcing agent to make powder production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] The invention provides a method for preparing ceramic powder, mainly by adjusting the formula of ceramic powder, reducing the clay content in the formula, and mixing additives for improving strength in the powder after powder making to prepare ceramic powder material. In the present invention, "clay" refers to clay materials for ceramics, such as washed ball clay, mixed clay, kaolin, bentonite (mainly composed of montmorillonite), attapulgite (variable composition) and the like.

[0023] Hereinafter, as an example, the preparation method of the ceramic powder of the present invention will be described.

[0024] Formulation of ceramic powder

[0025] The formula of ceramic powder contains clay and other commonly used ceramic raw materials, such as ceramic sand. In the present invention, the ceramic powder formula is adjusted to reduce the clay content. The clay content can be 0-10 wt%, preferably 0-8 wt%. From the perspective of saving clay resources, the less the cl...

Embodiment 1

[0041] Table 1: The name, ratio and chemical composition of each raw material are as follows:

[0042] serial number

raw material name

Proportion

IL

SiO 2

Al 2 o 3

Fe 2 o 3

TiO 2

CaO

MgO

K 2 o

Na 2 o

total

1

Sodium feldspar powder

18％

4.94

67.21

17.1

0.2

0.2

0.3

0.14

1.5

8.01

99.6

2

Potassium feldspar powder

20％

3.86

69.76

18.66

0.30

0.25

0.20

0.08

5.66

1.10

99.87

3

high temperature sand

30％

5.88

67.99

21.35

0.99

0.20

0.36

0.37

2.47

0

99.96

4

Medium temperature sand

27％

2.97

68.66

20.20

0.47

0.04

0.10

0.31

3.13

3.20

99.91

5

mud mix

5％

9.46

62.28

24.62

1.37

0.35

0

0

0.98

0.35

99.98

6

polyvinyl alcohol

0.3％

[0043] First, according to the f...

reference example 1

[0050] Table 2: The names, proportions, chemical compositions and manufacturers of each raw material are as follows:

[0051] serial number

raw material name

Proportion

IL

SiO 2

Al 2 o 3

Fe 2 o 3

TiO 2

CaO

MgO

K 2 o

Na 2 o

total

1

Sodium feldspar powder

18％

4.94

67.21

17.1

0.2

0.2

0.3

0.14

1.5

8.01

99.6

2

Potassium feldspar powder

15％

3.86

69.76

18.66

0.30

0.25

0.20

0.08

5.66

1.10

99.87

3

high temperature sand

22％

5.88

67.99

21.35

0.99

0.20

0.36

0.37

2.47

0

99.96

4

Medium temperature sand

23％

2.97

68.66

20.20

0.47

0.04

0.10

0.31

3.13

3.20

99.91

5

mud mix

22％

9.46

62.28

24.62

1.37

0.35

0

0

0.98

0.35

99.98

[0052] First, weigh the above raw materials and water according to the formula, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
strengthaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to ceramic powder and a preparation method thereof. The preparation method comprises the steps that a ceramic raw material containing ceramic sand and clay is prepared into slurry, powder spraying is carried out, and first powder is obtained, wherein the clay content in the ceramic raw material is 0-10 wt%; an additive is evenly mixed with water to form mixed water, wherein the additive can be evenly dispersed in water and can improve the green body strength; the mixed water is atomized and evenly mixed with the first powder, and therefore the ceramic powder is obtained.

Description

technical field [0001] The invention belongs to the field of ceramic building materials, and in particular relates to a ceramic powder and a preparation method thereof. Background technique [0002] Porcelain clay is an essential part of ceramic formula. Its main function is to provide strength, viscosity and toughness for the formula to ensure that the formula will not rot during molding and processing. It is a non-renewable resource. After decades of use, it is good There are fewer and fewer ceramic clays, and the composition, whiteness, strength and other properties are getting worse and worse. The development of high-grade ceramics is more and more restricted, and the cost is getting higher and higher. At present, many additives can improve the strength of the green body very well, but they have a particularly large impact on the flow rate of the slurry. It is difficult to greatly change and reduce the amount of clay, and directly use the reinforcing agent to make powder...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/14
CPCC04B35/14C04B2235/3472C04B2235/349
Inventor 刘一军杨晓峰汪庆刚陈欢李超潘利敏
Owner 广东清远蒙娜丽莎建陶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com