A kind of frit with high transparency and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology with high transparency and frit, applied in the field of ceramics, can solve the problems of simple and insufficient color and texture, differences in physical and chemical properties, high manufacturing cost, etc., and achieve the effect of wide firing range, stable quality and good gloss
Active Publication Date: 2018-09-07
HEYUAN DONGYUAN EAGLE CERAMICS CO LTD
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] At present, the surface of glass-ceramic composite plates on the market adopts translucent or opaque opaque microcrystalline layer, and its surface decoration effect is completely dependent on different colored glass-ceramic frits and their crystallization textures, and the manufacturing cost is high. , the transparency is not good, the color and texture are relatively simple and not rich enough
In order to achieve a certain decorative effect, some enterprises even directly use the glass phase as a method to achieve three-dimensional color, but its physical and chemical properties are very different from those of glass-ceramics, the texture is not clear, and the three-dimensional effect is not strong
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0017] A high-transparency frit whose main chemical composition is as follows in parts by mass: Al 2 o 3 16.68 parts, SiO 2 51.21 parts, Fe 2 o 3 0.094 parts, CaO 13.88 parts, MgO 5.92 parts, K 2 O 2.17 parts, Na 2 O 1.24 parts, TiO 2 0.01 part, SrO2 O 0.50 parts, PbO2 o 3 4.78 parts, P 2 o 5 0.31 parts, F 2.88 parts, and the remaining impurities.
Embodiment 2
[0019] A high-transparency frit whose main chemical composition is as follows in parts by mass: Al 2 o 3 20 parts, SiO 2 45 parts, Fe 2 o 3 0.05 parts, CaO 10 parts, MgO 8 parts, K 2 O 3 parts, Na 2 O 3 parts, TiO 2 0.01 part, SrO2 O 0.30 parts, PbO2 o 3 6 copies, P 2 o 5 0.5 parts, 4 parts of F, and the remaining impurities.
Embodiment 3
[0021] A high-transparency frit whose main chemical composition is as follows in parts by mass: Al 2 o 3 15 parts, SiO 2 55 parts, Fe 2 o 3 0.10 parts, CaO 15 parts, MgO 4 parts, K 2 O 3 parts, Na 2 O 1 part, TiO 2 0.03 part, SrO2 O 0.60 parts, PbO2 o 3 5 copies, P 2 o 5 0.1 part, F 1 part, and the remainder of impurities.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses high-transparency frit and a preparation method thereof. The high-transparency frit is mainly composed of 10-20 parts of Al2O3, 45-55 parts of SiO2, 0.05-0.10 part of Fe2O3, 10-15 parts of CaO, 4-8 parts of MgO, 1-3 parts of K2O, 1-3 parts of Na2O, 0.01-0.03 part of TiO2, less than 0.01 part of SrO, 0.30-0.60 part of LiO2, less than 0.01 part of PbO, less than 0.01 part of ZnO, 3-6 parts of B2O3, 0.1-0.5 part of P2O5 and 1-4 parts of F chemically, and loss on ignition is 3-5%. Frit particles can be closely combined with a ceramic substrate and are free of breakaway and layering; the frit and a blank are matched in expansion coefficient, so that a fired product has a flat surface; the surface of the fired product is free of air bubbles and pinholes, and the fired product is high in glossiness and transparency; raw materials which are extremely low in lead-cadmium content are adopted for formulation, so that the frit is environment-friendly.
Description
technical field [0001] The invention belongs to the field of ceramics, and in particular relates to a high-transparency frit and a preparation method thereof. Background technique [0002] At present, the surface of glass-ceramic composite plates on the market adopts translucent or opaque opaque microcrystalline layer, and its surface decoration effect is completely dependent on different colored glass-ceramic frits and their crystallization textures, and the manufacturing cost is high. , the transparency is not good, and the color and texture are relatively simple and not rich enough. In order to achieve a certain decorative effect, some enterprises even directly use the glass phase as a method to achieve three-dimensional color, but its physical and chemical properties are very different from those of glass-ceramics, the texture is not clear, and the three-dimensional effect is not strong. Contents of the invention [0003] In order to overcome the deficiencies in the p...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.