Durable bone china and preparation method thereof

A bone china, alumina technology, applied in clay products, other household appliances, household appliances, etc., can solve the problem of limited thermal shock resistance and achieve the effect of simple composition

Inactive Publication Date: 2014-01-29
NANJING UNIV OF TECH
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the improvement in thermal shock resistance is very limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The reinforced bone china described in embodiment 1 is prepared from the following raw materials in weight percent (wt%):

[0023] Calcined animal ashes 38.0%, potassium feldspar 11.0%, quartz sand 4.0%, Longyan soil 11.0%, Suzhou soil 6.0%, GF88 clay 5.0%, K18 clay 6.0%, Yixian soil 5.0%, α-alumina powder 2.0 %, limestone 7.0%, waste porcelain powder 5.0%.

[0024] According to a series of production processes such as the above-mentioned formula ingredients, ball milling, sieving, iron removal, aging, mud pressing, degumming, molding, drying, billet trimming, and sintering, the firing temperature is 1230-1290 ° C, and the bone is obtained after cooling. Porcelain biscuit.

[0025] The preparation method of the bone china biscuit is as follows:

[0026] Ball mill the mixture, add it to the ball mill according to the ratio of material: ball: water = 1:2.5:1, ball mill for 16.0 hours, pass through a 100-mesh sieve, use a 18,000-gauss iron remover to remove iron, stale f...

Embodiment 2

[0028] The reinforced bone china described in embodiment 2 is formulated from the following raw materials in weight percent (wt%):

[0029] Calcined animal ashes 40.0%, potassium feldspar 10.5%, quartz sand 6.0%, Longyan soil 11.5%, Suzhou soil 5.5%, GF88 clay 4.5%, K18 clay 6.5%, Yixian soil 4.5%, α-alumina powder 1.0 %, limestone 6.0%, waste porcelain powder 4.0%.

[0030] According to a series of production processes such as the above-mentioned formula ingredients, ball milling, sieving, iron removal, aging, mud pressing, degumming, molding, drying, billet trimming, and sintering, the firing temperature is 1230-1290 ° C, and the bone is obtained after cooling. Porcelain biscuit.

[0031] The preparation method of the bone china biscuit is as follows:

[0032] The mixture is ball milled, put into the ball mill according to the ratio of material: ball: water = 1:2.5:1, ball mill for 17.0 hours, pass through a 100-mesh sieve, use a 18,000-gauss iron remover to remove iron, s...

Embodiment 3

[0034] The reinforced bone china described in embodiment 3 is formulated from the following raw materials in weight percent (wt%):

[0035]Calcined animal ashes 42.0%, potassium feldspar 10.0%, quartz sand 5.0%, Longyan soil 12.0%, Suzhou soil 4.0%, GF88 clay 5.5%, K18 clay 5.0%, Yixian soil 3.0%, α-alumina powder 3.0 %, limestone 7.5%, waste porcelain powder 3.0%.

[0036] According to a series of production processes such as the above-mentioned formula ingredients, ball milling, sieving, iron removal, aging, squeezing mud, degumming, molding, drying, billet trimming, and sintering, the sintering temperature is 1230-1290°C to obtain bone china biscuits .

[0037] The preparation method of the bone china biscuit is as follows:

[0038] Ball mill the mixture, add it to the ball mill according to the ratio of material: ball: water = 1:2.5:1, ball mill for 18.0 hours, pass through a 100-mesh sieve, use a 18,000-gauss iron remover to remove iron, stale for 7 days, squeeze the mu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Flexural strengthaaaaaaaaaa
Flexural strengthaaaaaaaaaa
Flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to daily bone china, and in particular relates to durable bone china and a preparation method of the durable bone china. The green body of the durable bone china is prepared from the following raw materials in percentage by mass: 38.0-44.0% of animal ash, 3.5-7.5% of quartz sand, 7.0-12.0% of potassium feldspar, 4.0-8.0% of Suzhou clay, 8.0-12.0% of Longyan clay, 2.0-6.0% of Yi County clay, 2.0-7.0% of GF88 clay, 3.0-8.0% of K18 clay, 0.5-4.0% of alpha-aluminium oxide, 5.0-9.0% of limestone, and 0.5-8.0% of waste porcelain powder. The preparation method of the durable bone china comprises the following steps of: preparing a mixture from the above raw materials according to percentage by mass, ball-milling the mixture in a ball mill for 14.0-20.0 hours according to the mass ratio of the raw material to balls to water of 1:2.5:1, sieving the slurry using a 100-mesh sieve, removing ion, aging the resulting product for 3-7 days, squeezing the mud, adding certain water and dispersant into a mud cake for dispergation, carrying out slip casting, drying and trimming, firing the resulting product at 1230-1290 DEG C for 1.5-3.0 hours, and cooling the fired product to obtain the biscuit firing billet of the bone china. By adopting the durable bone china provided by the invention, the technical problems of the mutual interaction of the whiteness, the jade sense and the transparency, and the mutual interaction of the thickness, the strength, the hardness, and the thermal stability are solved.

Description

technical field [0001] The invention relates to a daily-use bone china, in particular to a reinforced bone china and a preparation method thereof. technical background [0002] Bone china, formerly known as bone china, is a high-grade porcelain that originated in England in the 18th century. It is mainly made of animal ashes, porcelain stones, clay and other raw materials. Bone china porcelain is fine and smooth, with smooth glaze and soft luster, high transparency and certain mechanical strength [Non-Patent Reference 1]; reputation. As the most high-grade daily-use porcelain recognized in the world, its application is quite extensive, such as tableware, tea sets, vases, etc., and is favored by consumers. [0003] At present, the raw materials used in the production of bone china are generally prepared from well-known animal ashes, clay, silica, feldspar and other raw materials. The products are made by high-temperature bisque firing and low-temperature glaze firing. The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/13C04B33/22
Inventor 张垠杨玉泉
Owner NANJING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com