A method for fabricating a shape-controllable flexible micro-nano pillar array

A manufacturing method, micro-nano technology, applied in the direction of nanostructure manufacturing, nanotechnology, nanotechnology, etc., can solve the problems of high manufacturing cost, geometric deformation of nanostructure, low output, etc., to avoid easy breakage, simple operability, and reliability Controlled and precise effects

Active Publication Date: 2017-03-29
XI AN JIAOTONG UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At this stage, the manufacturing process of high aspect ratio polymer micro-nano column arrays has the following problems: the micro-nano column or fiber prepared by electrospinning method has low strength, and it is difficult to obtain nanofiber filaments or short fibers separated from each other, and the yield is very low ; The mechanical pressure introduced by the nanoimprint method will cause problems such as geometric deformation of the nanostructure and uneven filling of the variable-size structure; the electric induction molding method and the mold replica method rely on the template, which is generally obtained by dry etching, and its manufacturing cost In addition, the problem of micro-column breakage is prone to occur during the demoulding process of the mold replica method.
In addition, the existing technology is difficult to realize the fabrication of inclined or complex polymer micro-nano column arrays
These issues severely restrict the functional reliability of devices containing polymeric micro-nanopillar arrays

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for fabricating a shape-controllable flexible micro-nano pillar array
  • A method for fabricating a shape-controllable flexible micro-nano pillar array
  • A method for fabricating a shape-controllable flexible micro-nano pillar array

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for manufacturing a shape-controllable flexible micro-nano pillar array, comprising the following steps:

[0029] 1) Refer to figure 1 and figure 2 , first coat the surface of the substrate 1 with a hydrosol adhesion layer 2, then obtain a micro-nano patterned photoresist on the hydrosol adhesion layer 2 through a photolithography process; then obtain the particle size on the surface of the photoresist by scraping D1 = patterning of micro-nanoparticles 3 of 5 μm, and then removing the photoresist to obtain a patterned template of micro-nanoparticles 3, wherein the micro-nanoparticles 3 are spherical polystyrene;

[0030] 2) Refer to figure 2 , coating the polymer 4 on the surface of the substrate 5, and then preheating the substrate 5, the preheating parameters: the temperature is 60°C, the time is 10 minutes, the polymer 4 is PDMS (polydimethylsiloxane) ;

[0031] 3) Refer to figure 2 , contacting and embedding the micronanoparticles 3 on the surface o...

Embodiment 2

[0036] A method for manufacturing a shape-controllable flexible micro-nano pillar array, comprising the following steps:

[0037] 1) Coating a hydrosol adhesion layer 2 on the surface of the substrate 1 first, and then obtaining a micro-nano patterned photoresist on the hydrosol adhesion layer 2 through a photolithography process; Patterning of micro-nanoparticles 3 with a diameter D2=10 μm, and then removing the photoresist to obtain a patterned template of micro-nanoparticles 3, where the micro-nanoparticles 3 are cubic indium trioxide;

[0038] 2) Coating the polymer 4 on the surface of the substrate 5, and then preheating the substrate 5, the preheating parameters: the temperature is 75°C, the time is 6 minutes, and the polymer 4 is PS (polystyrene);

[0039] 3) Refer to Figure 6 (a), contacting and embedding the micronanoparticles 3 on the surface of the patterned template into the polymer 4, the embedding depth T2=5 μm;

[0040] 4) Refer to Figure 6 (b), pull the pa...

Embodiment 3

[0044] A method for manufacturing a shape-controllable flexible micro-nano pillar array, comprising the following steps:

[0045] 1) Refer to Figure 7 (a), first coat the hydrosol adhesive layer 2 on the surface of the substrate 1, then obtain the micro-nano patterned photoresist on the hydrosol adhesive layer 2 by a photolithography process; then pass the scraping method on the photoresist surface Obtain the patterning of micro-nano particles with a 3-shaped pattern of particle diameter D3=200 μm; remove the photoresist to obtain a patterned template of 3-shaped micro-nano particles, and the micro-nano particles 3 are columnar sodium chloride;

[0046] 2) Coating the polymer 4 on the surface of the substrate 5, and then preheating the substrate 5, the preheating parameters: the temperature is 90°C, the time is 2 minutes, and the polymer 4 is PTT (polyurethane);

[0047] 3) Refer to Figure 7 (b), contacting and embedding the micro-nano particles 3 on the surface of the pat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

A method for manufacturing a form-controllable flexible micro-nano pillar array. Firstly, a hydrosol adhesive layer is coated on the surface of the substrate, and then a micro-nano patterned photoresist is obtained on the hydrosol adhesive layer through a photolithography process. The surface of the resist is patterned with micro-nano particles by scraping, and the photoresist is removed to obtain a patterned template of micro-nano particles; the polymer is coated on the surface of the substrate, and then the substrate is preheated; the patterned template The micro-nano particles on the surface contact and embed the polymer; then pull the patterned template to make the polymer stretched into a micro-nano column array, and then heat the substrate to solidify the micro-nano column array; then heat the patterned template to make the micro-nano column array The nanoparticles are detached from the hydrosol adhesion layer to obtain a micro-nano column array with micro-nano particles on the top; finally, the micro-nano particles on the top of the micro-nano column array are removed to obtain a polymer micro-nano column array. The present invention has the advantages of simple operation, low cost Advantages of low cost and short cycle time.

Description

technical field [0001] The invention belongs to the technical field of micro-nano manufacturing, and in particular relates to a method for manufacturing a shape-controllable flexible micro-nano column array. Background technique [0002] High-aspect-ratio polymer micro-nanopillar arrays have large specific surface area and good electromagnetic wave modulation ability, and are widely used in the enhanced absorption of electrons in solar cells, cell inspection and particle separation in the biological field, functional coatings (superhydrophobic and superoleophobic) ), microfluidic chips and other fields. At present, the preparation methods of high-aspect-ratio polymer micro-nano-column arrays mainly include: electrospinning, nanoimprinting, electrical induction molding, and mold replicating. Among them, the electrospinning method refers to the process in which a polymer solution (or melt) forms fibers under the action of a high-voltage electric field. Its core is to make the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B82B3/00B82Y40/00B81C1/00
CPCB81C1/00B82B3/00B82B3/0004B82Y40/00
Inventor 蒋维涛刘红忠雷彪陈邦道史永胜尹磊
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap