Method for preparing copper-containing waste water treatment agent through compound modification of fly ash
A wastewater treatment agent and composite modification technology, which is used in water/sewage treatment, adsorbed water/sewage treatment, water/sludge/sewage treatment, etc. It can solve the problems of unsatisfactory treatment effect, secondary pollution and high operating cost , to achieve the effect of remarkable treatment effect, simple operation and cost reduction.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
example 1
[0018] First, according to the solid-liquid ratio of 1:2, take fly ash and water, stir at 150r / min for 30min, then let it stand until no solid particles sink, remove impurities floating on the water surface, filter, collect the filtrate, and filter the filtrate Mix evenly with calcium carbonate at a mass ratio of 3:1, put it into a calciner, calcinate at 600°C for 1 hour, cool down to room temperature with the furnace, put the calcined product into a pulverizer for crushing, and pass through a 100-mesh sieve to obtain pretreatment Fly ash; then the above-mentioned pretreated fly ash and the sulfuric acid solution with a mass fraction of 92% are mixed uniformly at a solid-to-liquid ratio of 1:3, put into a glass reactor, set the temperature at 70 ° C, and keep the temperature for 10 minutes. Add sulfuric acid solution volume 40% in the reaction kettle, the mass fraction is 30% hydrogen peroxide solution, use nitrogen to discharge the air in the reaction kettle, stir and react wi...
example 2
[0021] First, according to the solid-liquid ratio of 1:2, take fly ash and water, stir at 150r / min for 35min, then let it stand until no solid particles sink, remove impurities floating on the water surface, filter, collect the filtrate, and filter the filtrate Mix evenly with calcium carbonate at a mass ratio of 3:1, put it into a calciner, calcinate at 600°C for 1.5h, cool down to room temperature with the furnace, put the calcined product into a pulverizer for crushing, and pass through a 100-mesh sieve to obtain a pre-calcined product. Treat the fly ash; then mix the pretreated fly ash obtained above with the sulfuric acid solution with a mass fraction of 92% at a solid-to-liquid ratio of 1:3, put it into a glass reactor, set the temperature at 75°C, and keep it warm for 13 minutes , add sulfuric acid solution volume 43% mass fraction in the reaction kettle and be 30% hydrogen peroxide solution, use nitrogen to discharge the air in the reaction kettle, stir and react with 1...
example 3
[0024] First, according to the solid-liquid ratio of 1:2, take fly ash and water, stir at 150r / min for 40min, then let it stand until no solid particles sink, remove impurities floating on the water surface, filter, collect the filtrate, and filter the filtrate Mix evenly with calcium carbonate at a mass ratio of 3:1, put it into a calciner, calcinate at 600°C for 2 hours, cool down to room temperature with the furnace, put the calcined product into a pulverizer for crushing, and pass through a 100-mesh sieve to obtain pretreatment Fly ash; then the above-mentioned pretreated fly ash and the sulfuric acid solution with a mass fraction of 92% are mixed uniformly at a solid-to-liquid ratio of 1:3, put into a glass reactor, set the temperature at 80 ° C, and keep the temperature for 15 minutes. Add sulfuric acid solution volume 45% to the reaction kettle with a mass fraction of 30% hydrogen peroxide solution, use nitrogen to discharge the air in the reaction kettle, and stir and r...
PUM
Property | Measurement | Unit |
---|---|---|
quality score | aaaaa | aaaaa |
quality score | aaaaa | aaaaa |
quality score | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com