Electro-spinning nanofiber mask with core-shell structure and preparation method thereof

A nanofiber, core-shell structure technology, applied in the direction of medical preparations containing active ingredients, fiber treatment, skin care preparations, etc., can solve the problem of functional ingredients not being able to penetrate, poor mask compliance, decomposition and dissolution, etc. problems, to achieve good antibacterial activity, stable properties, and guaranteed non-deteriorating effect

Active Publication Date: 2016-06-22
JILIN UNIV
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally, the main functional components of the mask are exposed on the outer layer, which is easily damaged (decomposed and dissolved) by external environmental pollutants, and may also directly contact the skin to cause skin allergies and other problems.
Generally, the conformability of the mask is not good, so the functional ingredients cannot penetrate into the skin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electro-spinning nanofiber mask with core-shell structure and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Made of the following raw materials in parts by weight: 5 parts of bletilla striata, 5 parts of white peony, 5 parts of ginseng, 5 parts of mulberry, 5 parts of mallow, 5 parts of comfrey root, 1 part of nutrients, 0.5 parts of hyaluronic acid, 0.5 parts of collagen ;

[0028] The nutrient is at least one of vitamin E, vitamin C, vitamin A, vitamin B1, vitamin B2, vitamin B3, carotene, and lycopene;

[0029] Include the following steps:

[0030] 1. Take 5 parts of fresh and clean mulberries, dry them in the air until there is no water, squeeze the juice and beat them, and ultrasonically extract them at 10°C and 20W for 20 minutes, filter through 100μm gauze, centrifuge at 1000rpm for 10 minutes, remove the sediment, and take the supernatant , and transferred to the stirrer, put the porous graphene oxide into the stirrer and rotate at 2000rpm for 10 minutes, and the porous graphene oxide 1 times the volume of the supernatant of the mulberry centrifuge, so that the antho...

Embodiment 2

[0037] It is made of the following raw materials by weight: 7.5 parts of bletilla striata, 7.5 parts of white peony, 10 parts of ginseng, 7.5 parts of mulberry, 7.5 parts of mallow, 7.5 parts of comfrey root, 2 parts of nutrients, 1.25 parts of hyaluronic acid, and 1.75 parts of collagen protein;

[0038] The nutrient is at least one of vitamin E, vitamin C, vitamin A, vitamin B1, vitamin B2, vitamin B3, carotene, and lycopene;

[0039] Include the following steps:

[0040] 1. Take 7.5 parts of fresh and clean mulberries, dry them in the air until there is no water, squeeze the juice and make a pulp, and ultrasonically extract at 30°C and 60W for 30 minutes, filter through 200μm gauze, centrifuge at 2500rpm for 15 minutes, remove the sediment, and take the supernatant , and transferred to the stirrer, drop the porous graphene oxide into the stirrer and rotate at 2500rpm for 15 minutes, 1.5 times the volume of the porous graphene oxide is centrifuged in the supernatant of mulb...

Embodiment 3

[0047] It is made of the following raw materials by weight: 10 parts of bletilla striata, 10 parts of white peony, 15 parts of ginseng, 10 parts of mulberry, 10 parts of mallow, 10 parts of comfrey root, 3 parts of nutrients, 2 parts of hyaluronic acid, and 3 parts of collagen protein;

[0048] The nutrient is at least one of vitamin E, vitamin C, vitamin A, vitamin B1, vitamin B2, vitamin B3, carotene, and lycopene;

[0049] Include the following steps:

[0050] 1. Take 10 parts of fresh and clean mulberries, dry them in the air until there is no water, squeeze the juice and make a pulp, and extract them ultrasonically for 40 minutes at 50°C and 100W, filter them through a 300μm gauze, centrifuge at 4000rpm for 20 minutes, remove the sediment, and take the supernatant , and transferred to the stirrer, drop the porous graphene oxide into the stirrer and rotate at 3000rpm for 20 minutes, the supernatant of the mulberry centrifuged with 2 times the volume of the porous graphene...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an electro-spinning nanofiber mask with a core-shell structure and a preparation method thereof and belongs to the field of natural cosmetics. The electro-spinning nanofiber mask is prepared from, by weight, 5-10 parts of bletilla roots, 5-10 parts of radix paeoniae alba, 5-15 parts of ginseng, 5-10 parts of mulberry fruits, 5-10 parts of malva sylvestris, 5-10 parts of alkanna roots, 1-3 parts of nutrients, 0.5-2 parts of hyaluronic acid and 0.5-3 parts of collagen. The electro-spinning nanofiber mask has the advantages that dirt in skin can be completely removed, the mask can be better attached to the skin, the skin absorbs functional matter more rapidly, whitening, freckle removing, inflammation diminishing, sterilizing and anti-aging repairing are comprehensively combined, and the requirements of people for multiple effects of the mask are met.

Description

technical field [0001] The invention belongs to the field of natural cosmetics and relates to an electrospun nanofiber mask with a core-shell structure and a preparation method thereof. Background technique [0002] With the decline of the quality of the surrounding environment, the acceleration of the pace of life and the increase of people's pressure, our skin has suffered serious damage. Spots, acne, lack of water, and aging are the most prominent problems at present, but the cosmetics on the market are somewhat one-sided, and there are still great limitations in solving skin problems in an all-round way. [0003] Nowadays, facial mask products are used more and more widely, but problems also emerge in endlessly. Generally, the main functional components of facial masks are exposed on the outer layer, which are easily damaged (decomposed and dissolved) by external environmental pollutants, and may also directly contact with the skin to cause skin allergies and other prob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/02A61K8/97A61K8/73A61K8/65A61K8/19A61K8/67A61Q19/02A61Q19/08A61Q19/00D04H1/728D01D5/00A61K8/9789A61K8/9794
CPCA61K8/0212A61K8/19A61K8/65A61K8/671A61K8/673A61K8/675A61K8/676A61K8/678A61K8/735A61K8/97A61K2800/413A61K2800/782A61Q19/00A61Q19/02A61Q19/08D01D5/0015D04H1/728
Inventor 金向群陈宇婷苏润萍赵明明李佳芮马方圆
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com